Low-cost, effective phosphate-based lime bucking inhibitor
A dry construction plaster composition made with at least stucco in an amount from about 25 to about 99 wt %; hydrated lime in an amount from about 0.5 to about 75 wt %; a phosphate-based lime bucking inhibitor in an amount from about 0.01 to about 1 wt %; and a setting reaction controlling agent, wherein the setting reaction controlling agent comprises a set accelerator, a set inhibitor, or any combination thereof is provided. Methods for preparing construction plaster slurries and pastes with reduced lime bucking and methods for finishing a substrate are also provided.
1 . A dry construction plaster composition comprising:
stucco in an amount from about 25 to about 99 wt %;
hydrated lime in an amount from about 5 to about 50 wt %;
a phosphate-based lime bucking inhibitor in an amount from about 0.01 to about 1 wt %; and
a setting reaction controlling agent, wherein the setting reaction controlling agent comprises a combination of a set accelerator and a set inhibitor;
wherein the set accelerator comprises calcium sulfate anhydrate, calcium sulfate dihydrate, calcium sulfate dihydrate co-ground with sugar, sodium or any mixture thereof; and
wherein the set inhibitor comprises diethylenetriaminepenta-acetate, pentasodium diethylenetriaminepenta-acetate, potassium bitartrate, citric acid or salt, maleic acid or salt, succinic acid or salt, tartaric acid or salt, or any combination thereof.
2 . The dry construction plaster composition of claim 1 , wherein the dry construction plaster composition comprises the set accelerator in an amount from about 0.001 to about 0.1 wt %.
3 . The dry construction plaster composition of claim 1 , wherein stucco in the mixture contains beta stucco and/or hydrated lime is dolomitic hydrated lime.
4 . The dry construction plaster composition of claim 1 , wherein the phosphate-based lime bucking inhibitor includes at least one orthophosphate and/or at least one polyphosphate.
5 . The dry construction plaster composition of claim 1 , wherein the phosphate-based lime bucking inhibitor includes trisodium phosphate (TSP), sodium tripolyphosphate (STPP), sodium trimetaphosphate (STMP), or any combination thereof.
6 . The dry construction plaster composition of claim 1 , wherein the dry construction plaster composition comprises sodium tripolyphosphate, calcium sulfate dihydrate co-ground with sugar, potassium bitartrate and maleic acid.
7 . The dry construction plaster composition of claim 1 , wherein the dry construction plaster composition further comprises one or more aggregates and/or one or more additives.
8 . The dry construction plaster composition of claim 1 , wherein the dry construction plaster composition comprises one or more of the following: sand, expanded perlite, clay, a defoamer, a thickener, or any combination thereof.
9 . A method for mixing construction plaster slurry or paste, the method comprising mixing the dry construction plaster composition of claim 1 with water.
10 . The method of claim 9 , wherein the method further comprises adding at least one aggregate and/or at least one additive.
11 . The method of claim 9 , wherein the dry construction plaster composition is mixed with water in an amount in the range from about 0.20 to about 0.75 liters of water per one kilogram of the dry construction plaster composition.
12 . A method for finishing a substrate, the method comprising:
a) mixing a construction plaster slurry or paste in accordance with claim 9 ; and
b) applying the slurry or paste to the substrate.
13 . The method of claim 12 , wherein the substrate is wallboard.
14 . The method of claim 12 , wherein step b) is performed by using a hawk, trowel or a spray applicator.