Bioink for 3D printing, the preparation method and usage
View Patent ↗The present invention relates to a bioink for 3D printing, the preparation method, and the usage. Such bioink is a gel made of α-zein, porogen by 0-10% of the weight of zein, ethanol and water. The preparation method consists of: 10-50% zein is dissolved into an aqueous solution containing 40-90% (v/v) of ethanol, then, the porogen by 0-10% of the weight of zein is added, and then, this solution is allowed to stand at 5-95° C. for 1-10 days, or stirred for 30 min-24 hours, and thus, the bioink for 3D printing can be obtained. The conditions applied to prepare such bioink are mild and the method adopted is easy to operate, in addition, the said bioink for 3D printing has good mechanical properties and biocompatibility, which can be applied in the field of biomedicine for preparing tissue engineered substitutes and hemostatic materials by 3D printing at room temperature.
1 . A bioink for 3D printing, wherein the bioink is a shear-thinning gel consisting of α-zein, ethanol, water, and porogen.
2 . The bioink for 3D printing according to claim 1 , wherein
the gel contains α-zein in an amount of 10-50% by weight, and porogen in an amount of 0-10% of the weight of zein, and a remainder of the gel is made of the ethanol and the water;
a volume ratio of ethanol to water is 40-90:10-60; and
the porogen is a water-soluble salt selected from the group consisting of: mannitol, ammonium bicarbonate, sodium chloride, sodium tartrate, sodium citrate, etc., sugar particles, paraffin particles and ice particles.
3 . The bioink for 3D printing according to claim 2 , wherein the gel includes the α-zein in an amount of 30-50% by weight.
4 . The bioink for 3D printing according to claim 2 , wherein the volume ratio of ethanol to water is 60-85:15-40.
5 . The bioink for 3D printing according to claim 1 , wherein the bioink can be printed at room temperature.
6 . The bioink for 3D printing according to claim 1 , wherein a zero-shear viscosity of the bioink is 30-5000 Pa·s.
7 . A preparation method of the bioink for 3D printing according to claim 1 , the method comprising:
dissolving 10-50% α-zein into a mixed solution of ethanol and water;
allowing the mixed solution of ethanol and water with the 10-50% α-zein dissolved therein to stand at 5-95° C. for 1-10 days, or stirring the mixed solution of ethanol and water with the zein 10-50% α-zein dissolved therein for 30 min-24 hours to form the gel; and
adding porogen in an amount of 0-10% of the weight of α-zein to the gel,
wherein, a volume ratio of ethanol to water is 40-90:10-60.
8 . The preparation method of the bioink for 3D printing according to claim 7 , wherein the mixed solution of ethanol and water with the 10-50% α-zein dissolved therein is allowed to stand at 10° C.-50° C. for 1 to 3 days.
9 . The bioink for 3D printing according to claim 1 , wherein the bioink is used to prepare biomedical materials.
10 . The bioink for 3D printing according to claim 9 , wherein the biomedical materials are tissue engineered substitutes or hemostatic materials with tubular, membraniform, or 3D scaffold structures.
11 . The bioink for 3D printing according to claim 10 , wherein the tissue engineered substitutes consist of nerve conduit, artificial windpipe, artificial urethra, artificial blood vessel, artificial skin, hemostatic membrane materials, artificial bone, artificial cartilage and artificial ear.
12 . The bioink for 3D printing according to claim 9 , wherein the biomedical materials are materials used to stop bleeding resulting from a deep penetrating wound with irregular wound directly by means of injection or smearing, or to stop bleeding.
13 . The preparation method of the bioink for 3D printing according to claim 7 , wherein
dissolving the 0-50% zein into the mixed solution of ethanol and water includes dissolving α-zein in an amount of 10-50% by weight, and porogen in an amount of 0-10% of the weight of zein, with a remainder made of the ethanol and the water measured; and
the porogen is a water-soluble salt selected from the group consisting of: mannitol, ammonium bicarbonate, sodium chloride, sodium tartrate, sodium citrate, etc., sugar particles, paraffin particles and ice particles.
14 . The bioink for 3D printing according to claim 1 , wherein the bioink is prepared by a method comprising:
(a) dissolving 10-50% α-zein into a mixed solution of ethanol and water with a volume ratio of 40-90:10-60;
(b) allowing the mixed solution to stand at 5-95° C. for 1-10 days, or stirring the mixed solution for 30 min-24 hours to form the gel; and
(c) adding porogen in an amount of 0-10% of the weight of α-zein.
15 . The bioink for 3D printing according to claim 14 , wherein the mixed solution of ethanol and water with the 10-50% α-zein dissolved therein is allowed to stand at 10° C.-50° C. for 1 to 3 days.
16 . The bioink for 3D printing according to claim 1 , wherein the bioink is configured for use in preparing biomedical materials selected from: tissue engineered substitutes, hemostatic materials, nerve conduits, artificial blood vessels, and artificial skin.
17 . A method of treating a wound, comprising applying the bioink of claim 1 to a deep penetrating wound with irregular shape by injection or smearing.