Adhesive sheet, construct, and method for producing construct
An adhesive sheet including an adhesive layer composed of an adhesive having active energy ray curability and ultraviolet ray absorbability, wherein when one surface of the adhesive layer is irradiated with ultraviolet rays having a light amount of 2000 mJ/cm 2 to cure the adhesive layer and an infrared absorption spectrum is then measured for the irradiated surface and non-irradiated surface, the maximum absolute value of absorbance is 0.0001 to 0.012 within a wavenumber range of 700 to 1000 cm −1 in a difference spectrum obtained by subtracting the infrared absorption spectrum of the non-irradiated surface from the infrared absorption spectrum of the irradiated surface, and when the adhesive layer is irradiated with ultraviolet rays having a light amount of 2000 mJ/cm 2 to cure the adhesive layer, the difference in a gel fraction of the adhesive constituting the adhesive layer before and after the irradiation is from 5 to 50 points.
1 . An adhesive sheet comprising an adhesive layer composed of an adhesive having active energy ray curability and ultraviolet ray absorbability, wherein
when one surface of the adhesive layer is irradiated with ultraviolet rays having a light amount of 2000 mJ/cm 2 to cure the adhesive layer and an infrared absorption spectrum is then measured by a total reflection measurement method for each of an irradiated surface that is a surface of the cured adhesive layer irradiated with the ultraviolet rays and a non-irradiated surface that is opposite to the irradiated surface, a maximum value of an absolute value of absorbance is 0.0001 or more and 0.012 or less within a wavenumber range of 700 to 1000 cm −1 in a difference spectrum obtained by subtracting the infrared absorption spectrum of the non-irradiated surface from the infrared absorption spectrum of the irradiated surface,
when the adhesive layer is irradiated with ultraviolet rays having a light amount of 2000 mJ/cm 2 to cure the adhesive layer, a difference in a gel fraction of the adhesive constituting the adhesive layer before and after the irradiation is 5 points or more and 50 points or less,
the adhesive is obtained by thermally crosslinking a pressure sensitive adhesive composition that contains a (meth)acrylic ester polymer (A), a crosslinker (B), an active energy ray curable component (C) and an ultraviolet ray absorber (E),
a content of the active energy ray curable component (C) in the pressure sensitive adhesive composition is 8 mass parts or more and 15 mass parts or less with respect to 100 mass parts of the (meth)acrylic ester polymer (A), and
a content of the ultraviolet ray absorber (E) in the pressure sensitive adhesive composition is 0.01 mass parts or more and 2 mass parts or less with respect to 100 mass parts of the active energy ray curable component (C).
2 . The adhesive sheet according to claim 1 , wherein the adhesive layer has a thickness of 20 μm or more and 1000 μm or less.
3 . The adhesive sheet according to claim 1 , wherein when the adhesive layer is irradiated with ultraviolet rays having a light amount of 2000 mJ/cm 2 to cure the adhesive layer, the gel fraction of the adhesive constituting the cured adhesive layer is 40% or more and 95% or less.
4 . The adhesive sheet according to claim 1 , wherein when the adhesive layer is irradiated with ultraviolet rays having a light amount of 2000 mJ/cm 2 to cure the adhesive layer, the cured adhesive layer has a storage elastic modulus of 0.03 MPa or more and 2.00 MPa or less at 23° C.
5 . The adhesive sheet according to claim 1 , wherein the adhesive constituting the adhesive layer contains a photopolymerization initiator.
6 . The adhesive sheet according to claim 1 , comprising:
two release sheets; and
the adhesive layer interposed between the two release sheets so as to be in contact with release surfaces of the two release sheets.
7 . A structural body comprising:
a first structural member;
a second structural member; and
a cured adhesive layer that bonds the first structural member and the second structural member together,
wherein the cured adhesive layer is obtained by curing the adhesive layer of the adhesive sheet according to claim 1 .
8 . The structural body according to claim 7 , wherein at least one of the first structural member and the second structural member has a surface in contact with the cured adhesive layer, and the surface is provided by a resin material.
9 . The structural body according to claim 7 , wherein
the first structural member is a cover material,
the second structural member is a display device, and
the structural body is a display body attached to an exterior of a moving object.
10 . The structural body according to claim 9 , wherein the moving object is a vehicle.
11 . A method of producing the structural body according to claim 7 , comprising:
bonding the first structural member and the second structural member together by the adhesive layer of the adhesive sheet; and
irradiating the adhesive layer after the bonding with active energy rays via at least one of the first structural member and the second structural member to cure the adhesive layer to obtain the cured adhesive layer.
12 . The adhesive sheet according to claim 1 , wherein the active energy ray curable component (C) is at least one of selected from tricyclodecanedimethanol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, polyethylene glycol di(meth)acrylate, neopentyl glycol adipate di(meth)acrylate, hydroxypivalic acid neopentyl glycol di(meth)acrylate, dicyclopentanyl di(meth)acrylate, caprolactone-modified dicyclopentenyl di(meth)acrylate, ethylene oxide-modified phosphoric acid di(meth)acrylate, di(acryloxyethyl) isocyanurate, allylated cyclohexyl di(meth)acrylate, ethoxylated bisphenol A diacrylate, 9,9-bis[4-(2-acryloyloxyethoxy) phenyl] fluorene, trimethylolpropane tri(meth)acrylate, dipentaerythritol tri(meth)acrylate, propionic acid-modified dipentaerythritol tri(meth)acrylate, pentaerythritol tri(meth)acrylate, propylene oxide-modified trimethylolpropane tri(meth)acrylate, tris(acryloxyethyl) isocyanurate, ε-caprolactone-modified tris-(2-(meth)acryloxyethyl) isocyanurate, diglycerin tetra(meth)acrylate, pentaerythritol tetra(meth)acrylate, propionic acid-modified dipentaerythritol penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate and caprolactone-modified dipentaerythritol hexa(meth)acrylate.
13 . The adhesive sheet according to claim 1 , wherein the ultraviolet ray absorber (E) is at least one of selected from benzophenone-based compound, benzotriazole-based compound, benzoate-based compound, benzoxazinone-based compound, triazine-based compound, phenylsalicylate-based compound, cyanoacrylate-based compound, and nickel complex salt-based compound.
14 . The adhesive sheet according to claim 1 , wherein the ultraviolet ray absorber (E) is the benzophenone-based compound, and
the benzophenone-based compound is at least one of selected from 2,2-dihydroxy-4-methoxybenzophenone, 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-methoxybenzophenone-5-sulfonic acid hydrate, and 2-hydroxy-4-n-octyloxybenzophenone.
15 . The adhesive sheet according to claim 1 , wherein the ultraviolet ray absorber (E) is the benzotriazole-based compound, and
the benzotriazole-based compound is at least one of selected from 2-(2-hydroxy-5-t-butylphenyl)-2H-benzotriazole, octyl-3-[3-t-butyl-4-hydroxy-5-(5-chloro-2H-benzotriazole-2-yl]phenyl) propionate, and 2-ethylhexyl-3-[3-t-butyl-4-hydroxy-5-(5-chloro-2H-benzotriazole-2-yl]phenyl) propionate.