Piston ring
To provide a piston ring having superior wear resistance and causing less wear damage of a cylinder. A piston ring 1 is used in a reciprocating compressor that compresses gas. The piston ring 1 is formed of a resin composition containing polyetheretherketone resin as a main component. The melt viscosity of the polyetheretherketone resin at the shear rate of 1,000/s and the temperature of 400° C. is 200-550 Pa·s based on a measuring method defined in ISO 11443. The resin composition contains 5-25 vol % of carbon fiber and 5-25 vol % of a solid lubricant, relative to the whole of the resin composition. The solid lubricant includes at least one of PTFE resin and graphite.
1 . A piston ring used in a hydrogen gas reciprocating compressor that compresses hydrogen gas, wherein:
the piston ring is formed of a resin composition containing polyetheretherketone resin as a main component;
where melt viscosity of the polyetheretherketone resin measured at a shear rate of 1,000/s and a temperature of 400° C. is 270-550 Pa·s based on a measuring method defined in ISO 11443,
the piston ring is a heat-treated body of an injection-molded body of the resin composition,
the piston ring has an endothermic peak in a range of 150-330° C., in addition to the endothermic peak due to a point at which the polyetheretherketone resin melts in a differential scanning calorimetry,
having a sulfur content of 250 ppm or less,
the resin composition does not contain polyphenylene sulfide resin, and contains 5-25 vol % of carbon fiber and 5-25 vol % of a solid lubricant, relative to the volume of the resin composition,
the solid lubricant comprises at least one component selected from polytetrafluoroethylene resin and graphite, and
the carbon fiber has an average fiber length of 20-200 μ.
2 . The piston ring as defined in claim 1 , wherein:
said heat treated body of an injection molded body of the resin composition has a content of sulfur element that is smaller than the content of the sulfur element in the injection-molded body.