Overhead conductors with high-temperature resistant cured coatings
An overhead conductor includes a bare conductor coated with a cured coating composition formed from a single-part coating dispersion. The cured coating composition includes silicon dioxide or derivatives thereof, one or more metals from Groups IA-IIIA of the periodic table, one or more acrylates, titanium dioxide, and optionally, barium sulfate. A method of making a coated overhead conductor includes preparing the single-part coating dispersion, applying the coating dispersion to a bare conductor, and curing the coating dispersion to form the coated overhead conductor. The single-part coating dispersion includes silicon dioxide, one or more metal silicates, one or more acrylates, titanium dioxide, water, and optionally, barium sulfate.
1 . An overhead conductor comprising a bare conductor coated with a cured coating composition, the cured coating composition consisting essentially of:
about 30% to 65%, by dry weight, of silicon dioxide or a derivative thereof;
about 10% to about 20%, by dry weight, of one or more acrylates;
about 5% to about 45%, by dry weight, of titanium dioxide;
about 1% to about 25%, by dry weight, of at least one metal selected from Groups IA-IIIA of the periodic table of elements; and
optionally, about 1% to about 15%, by dry weight, of a barium sulfate.
2 . The overhead conductor of claim 1 , wherein the silicon dioxide comprises one or more of amorphous silica, colloidal silica, and crystalline silica.
3 . The overhead conductor of claim 1 , wherein the silicon dioxide derivative comprises one or more silicates.
4 . The overhead conductor of claim 1 , wherein the cured coating composition comprises about 40% to about 60%, by dry weight, of a silicon dioxide or a derivative thereof.
5 . The overhead conductor of claim 1 , wherein the at least one metal comprises one or more of aluminum, potassium, sodium, lithium, magnesium, and calcium.
6 . The overhead conductor of claim 1 , wherein the one or more acrylates is selected from hydroxy acrylate; epoxy acrylate; (meth)acrylate homopolymer or (meth)acrylate copolymer; polyacrylic acid or salts thereof.
7 . The overhead conductor of claim 1 , wherein the cured coating composition comprises about 8% to about 40%, by dry weight, of titanium dioxide.
8 . The overhead conductor of claim 1 , wherein the cured coating composition comprises up to about 9%, by dry weight, of barium sulfate.
9 . A method of making a coated overhead conductor, the method comprising:
preparing a single-part coating dispersion, the coating dispersion comprising:
about 1% to about 25%, by weight, of silicon dioxide;
about 0.3% to about 10%, by weight, of one or more metal silicates, wherein the metal of the metal silicate is selected from Groups IA-IIIA of the periodic table of elements;
about 3% to about 10%, by weight, of one or more acrylates;
about 2% to about 25%, by weight, of titanium dioxide; and
about 30% to about 70%, by weight, of water;
applying the coating dispersion to a bare overhead conductor; and
curing the coating dispersion at ambient temperature to form the coated overhead conductor;
wherein the coating dispersion has a pot life of about 24 hours or longer.
10 . The method of claim 9 , wherein the coating dispersion comprises about 5% to about 22%, by weight, of silicon dioxide.
11 . The method of claim 9 , wherein the coating dispersion further comprises about 0.5% to about 9%, by weight, of barium sulfate.
12 . The method of claim 9 , wherein the coating dispersion is curable at ambient temperature in less than one hour.