Sustainable hybrid composite made from biodegradable polymer reinforced with Extracted Powder Compound from Reject Brine (EPC-RB)
There is disclosed a process of developing a sustainable hybrid composite material, comprising the steps of developing the Extracted Powder Compound from Reject Brine (EPC-RB) and producing a Biodegradable Composite from a Biodegradable Polymer (PLA) reinforced with (EPC-RB). The Extracted Powder Compound from Reject Brine (EPC-RB), which is waste product from different industrial processes, serves as a filler or reinforcement within at least one polymer matrix in different ratios to produce a new hybrid composite material with at least one unique property. Further, reinforcing the Extracted Powder Compound from Reject Brine (EPC-RB) in Biodegradable Polymer (PLA) in different ratios enhances the mechanical, thermal, and other properties of the developed sustainable hybrid composite material.
1 . A process of extracting a powder compound from Reject Brine (EPC-RB) by:
mixing a sample of reject brine solution with Ammonium Hydroxide (NH 4 OH) to form a treated brine solution;
reacting the treated brine solution with Carbon Dioxide (CO 2 ) air gas mixture;
filtering the collected mixture from the reacting step;
recovering ammonia (NH 4 Cl) and sulfate (SO 4 2− ) content in the presence of Calcium Oxide (CaO);
recovering the sulfate content as a solid product;
filtering to isolate the sulfate content as gypsum;
drying the gypsum; and
identifying & analysing the gypsum for presence of the extracted powder compound from reject brine (EPC-RB),
wherein recovering ammonia (NH 4 Cl) and sulfate (SO 4 2− ) content in the presence of Calcium Oxide (CaO) is done within a closed electrocoagulation cell.
2 . A process for producing a Biodegradable Composite of polylactic acid polymer reinforced with extracted Powder Compound from Reject Brine (EPC-RB), which comprises extracting a powder compound from Reject Brine (EPC-RB) according to the process of claim 1 , and mixing the extracted powder compound with polylactic acid polymer.
3 . The process for producing a Biodegradable Composite of polylactic acid polymer (PLA) reinforced with extracted Powder Compound from Reject Brine (EPC-RB) as claimed in claim 2 , wherein said Extracted Powder Compound from Reject Brine (EPC-RB) serves as a filler or reinforcement within a polylactic acid polymer matrix in a ratio of from 5% to 30% to produce a new hybrid composite material with at least one unique property.
4 . A process as claimed in claim 2 , which comprises:
mixing the extracted powder compound with polylactic acid polymer by dry-blending the EPC-RB with PLA and melt-compounding the blend at a temperature at or about the PLA melting point to form a homogeneous composite; and
forming a test article from the composite, wherein the forming comprises at least one of (a) pelletization followed by extrusion into a filament and three-dimensional (3D) printing of a part, and (b) injection molding of standardized mechanical test specimens.
5 . The process as claimed in claim 1 , wherein the Extracted Powder Compound is produced from Reject Brine generated as a waste product of an industrial process.
6 . A process as claimed in claim 5 wherein, the industrial process includes desalination, mining, and chemical production.
7 . A process as claimed in claim 1 , wherein gypsum (CaSO 4 ) is the main component of the EPC-RB.
8 . A process as claimed in claim 1 , wherein the sample of reject brine solution comprises a 1000 ml reject brine solution sample which is mixed with NH 4 OH solution at specific molar ratios (3.34 NH3:1 NaCl) to induce the precipitation of magnesium content.
9 . A process as claimed in claim 8 , wherein mixing a sample of reject brine solution with Ammonium Hydroxide (NH 4 OH) induces precipitation of magnesium content, and the resultant reaction yields a composite of NH 4 HCO 3 and magnesium hydroxide.
10 . A process for producing a Biodegradable Composite of polylactic acid polymer reinforced with extracted Powder Compound from Reject Brine (EPC-RB), which comprises mixing a composition obtained as a result of the process claimed in claim 8 with polylactic acid polymer at a ratio of 10% of the composition in the polylactic acid polymer to enhance the tensile strength of the developed sustainable hybrid composite material.
11 . A process for producing a Biodegradable Composite of polylactic acid polymer reinforced with extracted Powder Compound from Reject Brine (EPC-RB), which comprises mixing a composition obtained as a result of the process claimed in claim 8 with polylactic acid polymer at a ratio of 10% of the composition in the polylactic acid polymer to enhance the stiffness (Modulus of Elasticity) of the developed sustainable hybrid composite material.
12 . A process for producing a Biodegradable Composite of polylactic acid polymer reinforced with extracted Powder Compound from Reject Brine (EPC-RB), which comprises mixing a composition obtained as a result of the process claimed in claim 8 with polylactic acid polymer at a ratio of 30% of the composition in the polylactic acid polymer to enhance the compressive strength and Elastic modulus in compression of the developed sustainable hybrid composite material.
13 . A process as claimed in claim 1 , wherein the sample of reject brine contains dissolved salts, minerals, and waste compounds.
14 . The process of claim 13 , wherein the extraction yields an EPC-RB powder comprising calcium sulfate as its principal phase and minor phases comprising aluminum hydroxide and/or hydrocalumite detectable by spectroscopic analysis.
15 . A process as claimed in claim 13 , wherein the extraction yields an EPC-RB powder comprising diverse morphological structures, including needles and shells surrounding rhombic crystals.
16 . A process as claimed in claim 13 , wherein the extraction yields an EPC-RB powder comprising aluminum hydroxide in the form of shells and lamellar structures.
17 . The process of claim 1 , wherein the EPC-RB thus obtained is provided as a particulate powder comprising gypsum that exhibits needle-like morphology and is suitable for direct melt-compounding with a biodegradable polymer to form a biodegradable composite.