Environmental barrier coating and method of repairing the same
A method of repairing a coating on an article according to an exemplary embodiment of this disclosure, among other possible things includes defining a work area surrounding a discontinuity in the coating, the coating including undisturbed bond coat and undisturbed top coat; removing coating material within the work area; applying a slurry containing bond coat constituents in a carrier fluid to the work area; curing the slurry to form a repaired bond coat; applying a slurry containing top coat constituents in a carrier fluid to the work area; and curing the slurry to form a repaired top coat. A method of repairing a coating on an article and an article are also disclosed.
1 . A method of repairing a coating on an article, comprising:
defining a work area surrounding a discontinuity in the coating, the coating including undisturbed bond coat and undisturbed top coat;
removing coating material, including both undisturbed coating and undisturbed bond coat and top coat within the work area;
applying a bond slurry containing bond coat constituents in a carrier fluid to the work area;
curing the bond slurry to form a repaired bond coat;
applying a top slurry containing top coat constituents in a carrier fluid to the work area; and
curing the top slurry to form a repaired top coat.
2 . The method of claim 1 , wherein the removing step includes abrading the work area.
3 . The method of claim 1 , wherein the repaired bond coat has the same composition as the undisturbed bond coat.
4 . The method of claim 1 , wherein the repaired bond coat has a different component than the undisturbed bond coat.
5 . The method of claim 1 , wherein the undisturbed bond coat and the repaired bond coat comprise matrix material, gettering particles, and diffusive particles.
6 . The method of claim 5 , wherein the repaired bond coat contains a higher concentration of diffusive particles than the undisturbed bond coat.
7 . The method of claim 1 , wherein the repaired top coat has a different composition than the undisturbed top coat.
8 . The method of claim 1 , further comprising sintering the repaired bond coat and the repaired top coat.
9 . The method of claim 8 , wherein the article is a component of a gas turbine engine, and the sintering occurs during operation of the gas turbine engine.
10 . The method of claim 8 , wherein the sintering occurs at temperatures of at least about 1260 degrees C. (2300 degrees F.).
11 . The method of claim 1 , further comprising masking the article with masking material having an opening corresponding to the work area after the defining step.
12 . The method of claim 11 , wherein the masking material includes pre-cut masking material with a pre-cut opening, and further comprising selecting the pre-cut masking material to accommodate the size of the discontinuity.
13 . The method of claim 1 , wherein the step of applying the bond slurry containing bond coat constituents, the step of applying the top slurry containing top coat constituents, or both, includes pressing the slurry into the article.
14 . The method of claim 1 , further comprising the step of evaluating the coating to determine a thickness of the undisturbed bond coat, the undisturbed top coat, or both prior to the step of applying the slurry containing bond coat constituents.
15 . A method of repairing a coating on an article, comprising:
defining a work area surrounding a discontinuity in the coating, the coating including undisturbed bond coat and undisturbed top coat, and the discontinuity being in the top coat;
removing top coat material including undisturbed top coat material within the work area to reveal undisturbed bond coat;
applying a top slurry containing top coat constituents in a carrier fluid to the work area over the undisturbed bond coat; and
curing the top slurry to form a repaired top coat.
16 . The method of claim 14 , wherein the repaired top coat has a different composition as the undisturbed top coat.
17 . The method of claim 14 , further comprising masking the article with masking material having an opening corresponding to the work area after the defining step.
18 . The method of claim 1 , further comprising sintering the repaired top coat.
19 . The method of claim 1 , further comprising the step of evaluating the coating to determine a thickness of the undisturbed top coat to the step of applying the slurry containing bond coat constituents.