Insulation products
The invention relates to a method of making an insulation product and a novel insulation product, wherein the insulation product is made by adhering a facing to at least one major surface of a batt of man-made vitreous fibres in a matrix comprising a binder by the use of an adhesive and curing the adhesive. The adhesive is an aqueous composition which is free of phenol and formaldehyde and comprises: a component (i) in form of one or more lignosulfonate lignins having a carboxylic acid group content of 0.03 to 2.0 mmol/g, such as 0.03 to 1.4 mmol/g, such as 0.075 to 2.0 mmol/g, such as 0.075 to 1.4 mmol/g, based on the dry weight of the lignosulfonate lignins, a component (ii) in form of one or more cross-linkers.
1 . A method of making an insulation product, the method comprising:
providing a batt of man-made vitreous fibres (MMVF) in a matrix comprising a binder, wherein the batt of man-made vitreous fibres comprises at least one major surface;
providing a facing;
fixing the facing to at least one major surface of the batt of man-made vitreous fibres by the use of an adhesive; and
curing the adhesive, wherein the adhesive is an aqueous adhesive composition which is free of phenol and formaldehyde and comprises:
a component (i) in form of one or more lignosulfonate lignins having a carboxylic acid group content of 0.03 to 2.0 mmol/g, based on the dry weight of the lignosulfonate lignins,
a component (ii) in form of one or more cross-linkers,
wherein component (i) has an average carboxylic acid group content of less than 1.8 groups per macromolecule considering the M_n wt. average of component (i).
2 . The method according to claim 1 , wherein the facing is selected from woven or non-woven glass fibre veils or fabrics, scrims, rovings, glass fibre silks, glass filament fabrics, spunbonded polyester webs, vapour membranes, vapour barriers, roof underlay foils, aluminium foil and housewraps.
3 . The method according to claim 1 , wherein the facing is a non-woven glass veil having an area weight in the range of 30 to 150 g/m 2 .
4 . The method according to claim 1 , wherein the facing is a mineral coated non-woven glass veil having an area weight in the range of 150 to 350 g/m 2 .
5 . The method according to claim 1 , wherein the facing is a glass fibre silk or glass filament fabric having an area weight in the range of 90 to 180 g/m 2 .
6 . The method according to claim 1 , wherein the facing has at least one major surface and the method comprises applying adhesive to a major surface of the facing and/or the batt, and then applying said major surface of the facing to a major surface of the batt of man-made vitreous fibres.
7 . The method according to claim 1 , comprising applying the adhesive by spraying.
8 . The method according to claim 1 , wherein the step of curing the adhesive is carried out at a temperature of from 100 to 300° C.
9 . The method according to claim 1 , wherein the step of fixing the facing to at least one major surface of the batt is carried out when the binder for the MMVF is uncured, and the step of curing the adhesive also cures the binder in the matrix of MMVF.
10 . The method according to claim 1 , wherein the step of fixing the facing to at least one major surface of the batt is carried out after curing the binder for the MMVF.
11 . The method according to claim 1 , wherein the batt has a density in the range of 20 to 200 kg/m 3 .
12 . The method according to claim 1 , wherein the loss on ignition (LOI) of the batt of man-made vitreous fibres bonded by the binder is within the range of 0.5 to 8 wt %.
13 . The method according to claim 1 , wherein the insulation product has a thickness in the range of 20 to 400 mm.
14 . The method according to claim 1 , wherein the adhesive is applied in an amount of 40 to 400 g/m 2 of a liquid adhesive.
15 . The method according to claim 1 , wherein the method further comprises applying a coating to the facing after fixing the facing to the batt.
16 . The method according to claim 1 , wherein the insulation product is selected from the group consisting of an external façade, a ventilated façade, an interior ceiling insulation product, an interior wall insulation product, a roof insulation product, a ventilation duct or channel acoustic absorption product.
17 . The method according to claim 1 , wherein the binder in the batt of man-made vitreous fibres (MMVF) is a binder composition which prior to curing is an aqueous composition which is free of phenol and formaldehyde and comprises:
a component (i) in form of one or more lignosulfonate lignins having a carboxylic acid group content of 0.03 to 2.0 mmol/g, based on the dry weight of the lignosulfonate lignins,
a component (ii) in form of one or more cross-linkers.
18 . An insulation product obtained by the method according to claim 1 .
19 . A method of making an insulation product, the method comprising:
providing a batt of man-made vitreous fibres (MMVF) in a matrix comprising uncured binder, wherein the batt of man-made vitreous fibres comprises at least one major surface;
providing a facing;
applying the facing to at least one major surface of the batt of man-made vitreous fibres; and curing the binder so as to fix the facing to the major surface, wherein the binder is an aqueous binder composition which is free of phenol and formaldehyde and comprises:
a component (i) in form of one or more lignosulfonate lignins having a carboxylic acid group content of 0.03 to 2.0 mmol/g, based on the dry weight of the lignosulfonate lignins,
a component (ii) in form of one or more cross-linkers,
wherein component (i) has an average carboxylic acid group content of less than 1.8 groups per macromolecule considering the M_n wt. average of component (i).
20 . A method according to claim 19 , wherein the facing is selected from woven or non-woven glass fibre veils or fabrics, scrims, rovings, glass fibre silks, glass filament fabrics, spunbonded polyester webs, vapour membranes, vapour barriers, roof underlay foils, aluminium foil and housewraps.
21 . The method according to claim 19 , wherein the step of curing the binder is carried out at a temperature of from 100 to 300° C.
22 . An insulation product comprising an insulation element which is a batt of man-made vitreous fibres (MMVF) bonded with a binder, wherein the batt of man-made vitreous fibres comprises at least one major surface, and comprising a facing, wherein the facing is fixed to at least one major surface of the insulation element by an adhesive, wherein the adhesive before curing is an aqueous adhesive composition
which is free of phenol and formaldehyde and comprises:
a component (i) in form of one or more lignosulfonate lignins having a carboxylic acid group content of 0.03 to 2.0 mmol/g, based on the dry weight of the lignosulfonate lignins,
a component (ii) in form of one or more cross-linkers,
wherein component (i) has an average carboxylic acid group content of less than 1.8 groups per macromolecule considering the M_n wt. average of component (i).
23 . A product according to claim 22 , the aqueous adhesive/binder composition further comprising a component (iii) in form of one or more plasticizers.
24 . A product according to claim 23 , wherein component (iii) is in form of
one or more plasticizers selected from the group consisting of fatty alcohols and monohydroxy alcohols; and/or
one or more plasticizers selected from the group consisting of alkoxylates; and/or
one or more plasticizers in form of propylene glycols; and/or
one or more plasticizers in form of glycol esters; and/or
one or more plasticizers selected from the group consisting of adipates, acetates, benzoates, cyclobenzoates, citrates, stearates, sorbates, sebacates, azelates, butyrates, valerates; and/or
one or more plasticizers selected from the group consisting of phenol derivatives; and/or
one or more plasticizers selected from the group consisting of silanols, siloxanes; and/or
one or more plasticizers selected from the group consisting of sulfates, sulfonates, and phosphates; and/or
one or more plasticizers in form of hydroxy acids; and/or
one or more plasticizers selected from the group consisting of monomeric amides and fatty acid amides; and/or
one or more plasticizers selected from the group consisting of quaternary ammonium compounds; and/or
one or more plasticizers selected from the group consisting of vegetable oils; and/or
tall oil, and/or
one or more plasticizers selected from the group consisting of hydrogenated oils, acetylated oils; and/or
one or more plasticizers selected from acid methyl esters; and/or
one or more plasticizers selected from the group consisting of alkyl polyglucosides, gluconamides, aminoglucoseamides, sucrose esters, sorbitan esters; and/or
one or more plasticizers selected from the group consisting of polyethylene glycols, polyethylene glycol ethers; and/or
one or more plasticizers in form of polyols; and/or
triethanolamine.
25 . A product according to claim 23 , wherein component (iii) is in form of propylene glycols, phenol derivatives, silanols, siloxanes, hydroxy acids, vegetable oils, polyethylene glycols, polyethylene glycol ethers, triethanolamine, or any mixtures thereof.
26 . A product according to claim 23 , wherein component (iii) comprises one or more plasticizers having a boiling point of 100 to 380° C..
27 . A product according to claim 23 , wherein component (iii) comprises one or more polyethylene glycols having an average molecular weight of 150 to 50000 g/mol.
28 . A product according to claim 23 , wherein component (iii) is present in the binder composition in an amount of 0.5 to 60, based on the dry weight of component (i).
29 . A product according to claim 22 , the adhesive/binder composition comprising a further component (iv) in form of one or more coupling agents.
30 . A product according to claim 22 , wherein component (i) is having a carboxylic acid group content of 0.05 to 0.6 mmol/g, based on the dry weight of lignosulfonate lignins.
31 . A product according to claim 22 , wherein component (i) is in form of one or more lignosulfonate lignins having an average carboxylic acid group content of less than 1.4 groups per macromolecule considering the M_n wt. average of component (i).
32 . A product according to claim 22 , wherein component (i) is having a content of phenolic OH groups of 0.3 to 2.5 mmol/g, based on the dry weight of lignosulfonate lignins.
33 . A product according to claim 22 , wherein component (i) is having a content of aliphatic OH groups of 1.0 to 8.0 mmol/g, based on the dry weight of lignosulfonate lignins.
34 . A product according to claim 22 , wherein the component (i) comprises ammoniumlignosulfonates and/or comprises calciumlignosulfonates, and/or magnesiumlignosulfonates, and any combinations thereof.
35 . A product according to claim 22 , wherein component (i) comprises ammoniumlignosulfonates and calciumlignosulfonates, wherein the molar ratio of NH 4 + to Ca 2+ is in the range of 5:1 to 1:5.
36 . A product according to claim 22 , wherein the aqueous adhesive/binder composition contains added sugar in an amount of 0 to less than 5 wt.-%, based on the weight of lignosulfonate and sugar.
37 . A product according to claim 22 , wherein the aqueous adhesive/binder composition comprises component (i) in an amount of 50 to 98 wt.-%, based on the dry weight of components (i) and (ii).
38 . A product according to claim 22 , wherein the component (ii) is in form of one or more cross-linkers selected from
a. β-hydroxyalkylamide-cross-linkers, and/or
b. oxazoline-cross-linkers, and/or
c. the group consisting of multifunctional organic amines, and/or
d. epoxy compounds having a molecular weight of more than 500, which contains reactive functional groups, and/or
e. one or more cross-linkers selected from the group consisting of fatty amines; and/or
f. one more cross-linkers in form of fatty amides; and/or
g. one or more cross-linkers selected from polyester polyols; and/or
h. one or more cross-linkers selected from the group consisting of starch, modified starch, CMC; and/or
i. One or more cross-linkers in form of multifunctional carbodiimides; and/or
j. one or more cross-linkers selected from melamine based cross-linkers.
39 . A product according to claim 22 , wherein the component (ii) comprises one or more cross-linkers selected from β-hydroxyalkylamide-cross-linkers and/or oxazoline-cross-linkers.
40 . A product according to claim 22 , the adhesive/binder composition comprising component (ii) in an amount of 1 to 50 wt.-%, based on the dry weight of component (i).
41 . A product according to claim 22 , wherein the component (ii) is in form of one or more cross-linkers selected from
a. β-hydroxyalkylamide-cross-linkers, and/or
b. the group consisting of multifunctional organic amines, and/or
c. epoxy compounds having a molecular weight of more than 500, which contains reactive functional groups, and/or
d. one or more cross-linkers in form of multifunctional carbodiimides.
42 . A product according to claim 22 , wherein the component (ii) comprises one or more cross-linkers selected from
a. β-hydroxyalkylamide-cross-linkers.
43 . A product according to claim 22 , the adhesive/binder composition comprising component (ii) in an amount of 2 to 90 wt.-%, based on the dry weight of component (i).
44 . A product according to claim 22 , the adhesive/binder composition further comprising a component (v) in form of one or more components selected from the group of bases.
45 . A product according to claim 22 , the adhesive/binder composition comprising a further component in form of urea in an amount 5 to 40 wt.-%, based on the dry weight of component (i).
46 . A product according to claim 22 , wherein the batt further comprises a further component (vi) in the form of one or more reactive or nonreactive silicones.
47 . A product according to claim 22 , wherein the batt does not contain an ammonia-oxidized lignin (AOL).
48 . A product according to claim 22 with the proviso that the aqueous composition does not comprise a cross-linker selected from carbonyl compounds selected from aldehydes, carbonyl compounds of the formula R—[C(O)R 1 ] x
in which:
a. R represents a saturated or unsaturated and linear, branched or cyclic hydrocarbon radical, a radical including one or more aromatic nuclei which consist of 5 or 6 carbon atoms, a radical including one or more aromatic heterocycles containing 4 or 5 carbon atoms and an oxygen, nitrogen or sulfur atom, it being possible for the R radical to contain other functional groups,
b. R 1 represents a hydrogen atom or a C 1 -C 10 alkyl radical, and
c. x varies from 1 to 10.
49 . A product according to claim 22 with the proviso that the aqueous composition does not comprise a cross-linker selected from polyamines.
50 . A product according to claim 22 with the proviso that the aqueous composition does not comprise a cross-linker selected from:
a. epoxy compounds having a molecular weight Mw of 500 or less.