Container made from soda-lime glass with improved chemical resistance for a pharmaceutical or diagnostic substance
The invention relates to a container ( 1 ) comprising a wall ( 2 ) made of glass delimiting a cavity ( 3 ) to accommodate a substance, particularly for a pharmaceutical or diagnostic substance, the glass wall ( 2 ) having an internal face ( 4 ) situated facing the accommodating cavity ( 3 ), the container ( 1 ) being characterized in that the wall ( 2 ) is made of soda-lime glass, the internal face ( 4 ) forming a bare glass surface intended to come into direct contact with the substance, the glass wall ( 2 ) having an atomic fraction of sodium, measured by X-ray-induced photoelectron spectrometry, which is less than or equal to 4 at. % down to a depth of at least 200 nm from the surface of the inner face ( 4 ).
1 . A container ( 1 ) comprising a glass wall ( 2 ) delimiting an accommodation cavity ( 3 ) for a substance, said glass wall ( 2 ) having an inner face ( 4 ) located facing said accommodation cavity ( 3 ), said container ( 1 ) being characterized in that said wall ( 2 ) is made of soda-lime glass, said inner face ( 4 ) forming a bare glass surface intended to come into direct contact with said substance, said glass wall ( 2 ) having anatomic fraction of sodium, as measured by X-ray induced photoelectron spectrometry, that is lower than 4 at. % up to a depth of at least 200 nm from the surface of the inner face ( 4 ).
2 . The container ( 1 ) according to claim 1 , characterized in that said atomic fraction of sodium is lower than or equal to 3.5 at. % up to a depth of at least 200 nm from the surface of the inner face ( 4 ).
3 . The container ( 1 ) according to claim 1 , characterized in that said atomic fraction of sodium is lower than or equal to 3.5 at. % up to a depth of at least 100 nm from the surface of the inner face ( 4 ).
4 . The container ( 1 ) according to claim 1 , characterized in that said atomic fraction of sodium is lower than or equal to 2.4 at. % up to a depth of 30 nm from the surface of the inner face ( 4 ).
5 . The container ( 1 ) according to claim 1 , characterized in that said atomic fraction of sodium is lower than or equal to 2.0 at. % up to a depth of 15 nm from the surface of the inner face ( 4 ).
6 . The container ( 1 ) according to claim 1 , characterized in that said atomic fraction of sodium is lower than or equal to 1.5 at. % at a depth of 0 nm from the surface of the inner face ( 4 ).
7 . The container ( 1 ) according to claim 1 , characterized in that said atomic fraction of sodium is lower than or equal to 2.5 at. % up to a depth of at least 200 nm from the surface of the inner face ( 4 ), lower than or equal to 2.0 at. % up to a depth of at least 30 nm from the surface of the inner face ( 4 ), while being lower than or equal to 1.0 at. % at a depth of 0 nm from the surface of the inner face ( 4 ).
8 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of sodium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.130 up to a depth of at least 200 nm from the surface of the inner face ( 4 ).
9 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of sodium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.130 up to a depth of at least 100 nm from the surface of the inner face ( 4 ).
10 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of sodium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.080 up to a depth of at least 30 nm from the surface of the inner face ( 4 ).
11 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of sodium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.080 up to a depth of at least 15 nm from the surface of the inner face ( 4 ).
12 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of sodium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.050 at a depth of 0 nm from the surface of the inner face ( 4 ).
13 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of calcium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.240 up to a depth of at least 200 nm from the surface of the inner face ( 4 ).
14 . The container ( 1 ) according to claim 1 , characterized in that said glass wall has a ratio of an atomic fraction of calcium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.230 up to a depth of at least 100 nm from the surface of the inner face ( 4 ).
15 . The container ( 1 ) according to claim 1 , characterized in that said glass wall has a ratio of an atomic fraction of calcium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.210 up to a depth of at least 30 nm from the surface of the inner face ( 4 ).
16 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of calcium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.200 up to a depth of at least 15 nm from the surface of the inner face ( 4 ).
17 . The container ( 1 ) according to claim 1 , characterized in that said glass wall has a ratio of an atomic fraction of calcium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.050 at a depth of 0 nm from the surface of the inner face ( 4 ).
18 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of aluminium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.040 up to a depth of at least 200 nm from the surface of the inner face ( 4 ).
19 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of aluminium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.040 up to a depth of at least 100 nm from the surface of the inner face ( 4 ).
20 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of aluminium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.050 up to a depth of at least 30 nm from the surface of the inner face ( 4 ).
21 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of aluminium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.050 up to a depth of at least 15 nm from the surface of the inner face ( 4 ).
22 . The container ( 1 ) according to claim 1 , characterized in that said glass wall ( 2 ) has a ratio of an atomic fraction of aluminium to an atomic fraction of silicon, measured by X-ray induced photoelectron spectrometry, that is lower than or equal to 0.040 at a depth of 0 nm from the surface of the inner face ( 4 ).
23 . The container ( 1 ) according to claim 1 , characterized in that it forms a vial or a bottle.
24 . The container ( 1 ) according to claim 1 , characterized in that it is made of moulded glass.
25 . A raw container intended to form a container ( 1 ) according to claim 1 , said raw container comprising said glass wall delimiting an accommodation cavity, said glass wall of said raw container having said inner face located facing said accommodation cavity, said glass wall being made of soda-lime glass, said inner face forming said glass surface provided with sodium sulphate grains shaped and arranged in a substantially uniform manner on said surface, thus forming a substantially homogeneous translucent white bloom, said raw container being intended to undergo a washing of the surface of the glass wall inner face of said raw container in order to eliminate said bloom.
26 . The raw container according to claim 25 , wherein said sodium sulphate grains have an average size between 50 nm and 1,500 nm.
27 . The raw container according to claim 25 , wherein said sodium sulphate grains are distributed over the glass surface of the inner face with an average surface density from 0.1 grains/μm 2 to 30 grains/μm 2 .