Steel sheet for hot stamping and hot stamped product
A steel sheet for hot stamping has a predetermined chemical composition, in which, when a Mo content of the steel sheet is measured by line analysis using an electron probe micro-analyzer (EPMA) in a range of 0.05 mm in a sheet thickness direction, in which a ¼ depth position of a sheet thickness of the steel sheet from a surface of the steel sheet is a center, a maximum value of the Mo content, a minimum value of the Mo content, and an average value of the Mo content satisfy ([Mo] MAX −[Mo] MIN )/[Mo] AVE <0.50, and a standard deviation of a Vickers hardness in a region of 0.3 mm in the sheet thickness direction and 0.6 mm in a direction perpendicular to the sheet thickness direction, in which the ¼ depth position of the sheet thickness of the steel sheet from the surface of the steel sheet is a center, is 20 (Hv) or less.
1 . A steel sheet for hot stamping comprising, as a chemical composition, by mass %:
C: more than 0.40% and 0.70% or less;
Si: less than 2.00%;
Mn: 0.01% or more and less than 0.50%;
P: 0.200% or less;
S: 0.0200% or less;
sol. Al: 0.001% to 1.000%;
N: 0.0200% or less;
Mo: 0.01% or more and less than 0.50%;
B: 0.0002% to 0.0200%;
Ti: 0% to 0.200%;
Nb: 0% to 0.200%;
V: 0% to 0.200%;
Zr: 0% to 0.200%;
Cr: 0% to 2.00%;
W: 0% to 2.00%;
Cu: 0% to 2.00%;
Ni: 0% to 2.00%;
Ca: 0% to 0.0100%;
Mg: 0% to 0.0100%;
REM: 0% to 0.1000%;
Bi: 0% to 0.0500%; and
a remainder: Fe and impurities,
wherein, when a Mo content of the steel sheet is measured by line analysis using an electron probe micro-analyzer (EPMA) in a range of 0.05 mm in a sheet thickness direction, in which a ¼ depth position of a sheet thickness of the steel sheet from a surface of the steel sheet is a center, a maximum value of the Mo content, a minimum value of the Mo content, and an average value of the Mo content satisfy Expression (i), and
a standard deviation of a Vickers hardness in a region of 0.3 mm in the sheet thickness direction and 0.6 mm in a direction perpendicular to the sheet thickness direction, in which the ¼ depth position of the sheet thickness of the steel sheet from the surface of the steel sheet is a center, is 20 (Hv) or less,
(
[
Mo
]
MAX
-
[
Mo
]
MIN
)
/
[
Mo
]
AVE
<
0
.
5
0
(
i
)
wherein meaning of each symbol in Expression (i) is as follows,
[Mo] MAX : the maximum value of the Mo content (mass %),
[Mo] MIN : the minimum value of the Mo content (mass %), and
[MO] AVE : the average value of the Mo content (mass %).
2 . The steel sheet for hot stamping according to claim 1 , wherein the chemical composition contains, by mass %, one or more of:
Ti: 0.001% to 0.200%;
Nb: 0.001% to 0.200%;
V: 0.001% to 0.200%; and
Zr: 0.001% to 0.200%.
3 . The steel sheet for hot stamping according to claim 1 , wherein the chemical composition contains, by mass %, one or more of:
Cr: 0.001% to 2.00%;
W: 0.001% to 2.00%;
Cu: 0.001% to 2.00%; and
Ni: 0.001% to 2.00%.
4 . The steel sheet for hot stamping according to claim 1 , wherein the chemical composition contains, by mass %, one or more of
Ca: 0.0001% to 0.0100%;
Mg: 0.0001% to 0.0100%; and
REM: 0.0001% to 0.1000%.
5 . The steel sheet for hot stamping according to claim 1 , wherein the chemical composition contains, by mass %:
Bi: 0.0001% to 0.0500%.
6 . A hot stamped product comprising:
a base steel sheet,
wherein the base steel sheet includes, as a chemical composition, by mass %,
C: more than 0.40% and 0.70% or less,
Si: less than 2.00%,
Mn: 0.01% or more and less than 0.50%,
P: 0.200% or less,
S: 0.0200% or less,
sol. Al: 0.001% to 1.000%,
N: 0.0200% or less,
Mo: 0.01% or more and less than 0.50%,
B: 0.0002% to 0.0200%,
Ti: 0% to 0.200%,
Nb: 0% to 0.200%,
V: 0% to 0.200%,
Zr: 0% to 0.200%,
Cr: 0% to 2.00%,
W: 0% to 2.00%,
Cu: 0% to 2.00%,
Ni: 0% to 2.00%,
Ca: 0% to 0.0100%,
Mg: 0% to 0.0100%,
REM: 0% to 0.1000%,
Bi: 0% to 0.0500%, and
a remainder: Fe and impurities,
when a Mo content of the base steel sheet is measured by line analysis using an EPMA in a range of 0.05 mm in a sheet thickness direction, in which a ¼ depth position of a sheet thickness of the base steel sheet from a surface of the base steel sheet is a center, a maximum value of the Mo content, a minimum value of the Mo content, and an average value of the Mo content satisfy Expression (ii),
a metallographic microstructure of the base steel sheet contains 90.0% or more of martensite,
a standard deviation of a Vickers hardness in a region of 0.3 mm in the sheet thickness direction and 0.6 mm in a direction perpendicular to the sheet thickness direction, in which the ¼ depth position of the sheet thickness of the base steel sheet from the surface of the base steel sheet is a center, is 20 (Hv) or less, and
a tensile strength of the base steel sheet is 2,300 MPa or more,
(
[
Mo
]
mMAX
-
[
Mo
]
mMIN
)
/
[
Mo
]
mAVE
<
0
.
5
0
(
ii
)
wherein meaning of each symbol in Expression (ii) is as follows,
[Mo] mMAX : the maximum value of the Mo content of the base steel sheet (mass %),
[Mo] mMIN : the minimum value of the Mo content of the base steel sheet (mass %), and
[Mo] mAVE : the average value of the Mo content of the base steel sheet (mass %).