Control of strain in device layers by prevention of relaxation
The benefits of strained semiconductors are combined with silicon-on-insulator approaches to substrate and device fabrication. Strain in the strained semiconductors is controlled for improved device performance.
1. A method for forming a structure, the method comprising:
providing a strained semiconductor layer disposed over and contacting a dielectric layer disposed over a semiconductor substrate, the strained semiconductor layer having a first type of strain; and
forming a transistor including a channel disposed in a portion of the strained semiconductor layer by:
performing an implant of an isoelectronic species to introduce a plurality of point defects into a region of the strained semiconductor layer,
thereafter, performing a shallow source and drain implant having an implant depth less than an approximate implant depth of the isoelectronic species, and
performing a deep source and drain implant.
2. The method of claim 1 , wherein the point defects comprise interstitial defects, and performing the implant comprises performing a pre-amorphization implant to introduce at least a critical dose of interstitial defects into the region of the strained semiconductor layer to amorphize the region.
3. The method of claim 2 , wherein a thickness of the amorphous region is less than 50% of a thickness of the strained semiconductor layer.
4. The method of claim 3 , wherein the thickness of the amorphous region is less than 25% of the thickness of the strained semiconductor layer.
5. The method of claim 2 , further comprising:
recrystallizing the amorphized region.
6. The method of claim 5 , wherein the recrystallized region has a second type of strain substantially the same as the first type of strain.
7. The method of claim 6 , wherein the first and second types of strain are tensile strain.
8. The method of claim 6 , wherein the first and second types of strain are compressive strain.
9. The method of claim 2 , wherein the pre-amorphization implant is performed selectively on the region of the strained semiconductor layer.
10. The method of claim 2 , wherein forming the transistor further comprises defining a strain-inducing stressor, and the strain-inducing stressor induces strain of a same type as the first strain.
11. The method of claim 10 , wherein the strain induced by the strain-inducing stressor is tensile strain.
12. The method of claim 10 , wherein the strain induced by the strain-inducing stressor is compressive strain.
13. The method of claim 10 , wherein the point defects comprise lattice vacancies and performing the implant of the isoelectronic species comprises performing a co-implant to create lattice vacancies in the region of the strained semiconductor layer, the region of the strained semiconductor layer remaining crystalline.
14. The method of claim 10 , wherein the strain-inducing stressor comprises a shallow trench isolation disposed proximate at least one of a source and a drain formed during the deep source and drain implant.
15. The method of claim 10 , wherein the strain-inducing stressor comprises a gate electrode formed over a portion of the strained semiconductor layer.
16. The method of claim 10 , wherein the strain-inducing stressor comprises a metal-semiconductor alloy disposed on at least one of a source and a drain formed during the deep source and drain implant.
17. The method of claim 10 , wherein the strain-inducing stressor comprises at least one dielectric spacer disposed proximate a gate electrode formed over a portion of the strained semiconductor layer.
18. The method of claim 10 , wherein the strain-inducing stressor comprises a dielectric overlayer disposed over a gate electrode formed over a portion of the strained semiconductor layer and at least one of a source and a drain formed during the deep source and drain implant.
19. The method of claim 1 , wherein the region of the strained semiconductor layer comprises a drain of the transistor and the implant of the isoelectronic species is performed at an angle of less than 90° with respect to a top surface of the drain.
20. The method of claim 19 , wherein performing the implant of the isoelectronic species amorphizes at least a portion of the drain of the transistor, and substantially all of a source of the transistor remains crystalline.
21. The method of claim 19 , wherein, after forming the transistor, the drain is partially relaxed and a source of the transistor is approximately fully strained.
22. The method of claim 1 , wherein the implant is performed at a temperature above 25° C.
23. The method of claim 1 , wherein the step of performing a deep source and drain implant forms a source region and a drain region, wherein the source region and the drain region are each formed entirely within the strained semiconductor layer.
24. The method of claim 1 , further comprising performing a recrystallization anneal after the step of performing the shallow source and drain implant and prior to the step of performing the deep source and drain implant.
25. A method for forming a structure, the method comprising:
providing a strained semiconductor layer disposed over and contacting a dielectric layer disposed over a semiconductor substrate, the strained semiconductor layer having a first amount of strain; and
forming a first transistor including:
defining a channel disposed in a portion of the strained semiconductor layer;
removing at least a portion of the strained semiconductor layer proximate the channel to define a recess, and
selectively depositing a conductive material into the recess to define at least a portion of a source or a drain of the first transistor,
wherein the conductive material induces additional strain such that the channel has a second amount of strain greater than the first amount of strain.
26. The method of claim 25 , wherein the conductive material comprises at least one of a metal or a doped semiconductor.
27. The method of claim 25 , wherein the first strain and the second strain are compressive.
28. The method of claim 25 , wherein the first strain and the second strain are tensile.
29. The method of claim 25 , further comprising forming a second transistor including:
defining a second channel disposed in a second portion of the strained semiconductor layer,
removing at least a portion of the strained semiconductor layer proximate the second channel to define a second recess, and
selectively depositing a second conductive material into the second recess to define at least a portion of a source or a drain of the second transistor,
wherein the second conductive material induces strain of a type different from the first and second strains such that the second channel has a third amount of strain which is less than the first amount of strain.
30. The method of claim 29 , wherein the conductive material and the second conductive material are different.
31. A method for forming a structure, the method comprising:
providing a strained semiconductor layer disposed over and contacting a dielectric layer disposed over a semiconductor substrate, the strained semiconductor layer having a first amount of strain; and
forming a first transistor including:
defining a channel disposed in a portion of the strained semiconductor layer;
removing at least a portion of the strained semiconductor layer proximate the channel to define a recess, and
selectively depositing a metal into the recess to define at least a portion of a source or a drain of the first transistor,
wherein a second amount of strain in the channel after metal deposition is greater than or equal to the first amount of strain.