Multilayer effect pigment
A multilayer effect pigment includes a transparent substrate, a layer of high refractive index material on the substrate, and alternating layers of low refractive index and high refractive index materials on the first layer, the total number of layers being an odd number of at least three, all adjacent layers differing in refractive index by at least about 0.2 and at least one of the layers having an optical thickness which is different from all of the other layers. The resulting multilayer effect pigment is not a quarter-wave stack. The present multilayer effect pigment may be used in cosmetics or personal care products.
1. A multilayer effect pigment comprising:
a transparent substrate having a layer of titanium dioxide thereon, said layer having an optical thickness of about 85 to 385 nm,
a layer of a low refractive index material on said titanium dioxide layer and an outermost layer of a high refractive index material placed on said low refractive index material layer,
said high refractive index material comprises titanium dioxide having an optical thickness of from about 45 to 420 nm and the low refractive index material is silicon dioxide having an optical thickness of about 30 to 120 nm, and wherein at least one layer has an optical thickness which is different from all of the other layers, whereby the pigment is not a quarter-wave stack.
2. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 134 to 148±12 nm, said silicon dioxide layer has an optical thickness of 105 to 117±8 nm, and the outermost titanium dioxide layer has an optical thickness of 134 to 143±12 nm, said pigment being white.
3. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 134±12 nm, said silicon dioxide layer has an optical thickness of 496±8 nm, and the outermost titanium dioxide layer has an optical thickness of 148±12 nm, said pigment being white.
4. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 143±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and the outermost titanium dioxide layer has an optical thickness of 155±12 nm, said pigment being white.
5. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 148±12 nm, said silicon dioxide layer has an optical thickness of 117±8 nm, and the outermost titanium dioxide layer has an optical thickness of 208±12 nm, said pigment being yellow.
6. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 203±12 nm, said silicon dioxide has an optical thickness of 105 to 117±8 nm and the outermost titanium dioxide layer has an optical thickness of 203 to 210±12 nm, said pigment being yellow.
7. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 203±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm or 96±8 nm, and said outermost layer titanium dioxide layer has an optical thickness of 215 to 227±12 nm, said pigment being yellow.
8. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 243±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and said outermost titanium dioxide layer has an optical thickness of 243±12 nm, said pigment being orange.
9. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 243±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm or 117±8 nm, and said outermost titanium dioxide layer has a thickness of 267 or 248±12 nm, respectively, said pigment being red.
10. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 148±12 nm, said silicon dioxide layer has an optical thickness of 117±8 nm, and the outermost titanium dioxide layer has a optical thickness of 241±12 nm, said pigment being red.
11. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 143 to 148±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and the outermost titanium dioxide layer has a optical thickness of 45±12 nm or 308±12 nm, said pigment being violet.
12. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 265 to 270±12 nm, said silicon dioxide layer has an optical thickness of 117±8 nm, and said outermost titanium dioxide layer has an optical thickness of 265 to 274±12 nm, said pigment being violet.
13. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 372±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and said outermost titanium dioxide layer has an optical thickness of 267±12 nm, said pigment being violet.
14. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 83±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and said outermost titanium dioxide layer has an optical thickness of 72±12 nm, said pigment being violet.
15. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 107±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and said outermost titanium dioxide layer has an optical thickness of 64±12 nm, said pigment being violet.
16. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 143 to 148±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and the outermost titanium dioxide layer has a optical thickness of 72±12 nm or 343±12 nm, said pigment being blue.
17. The multilayer effect pigment of claim 1 wherein said titanium dioxide layer has an optical thickness of 119±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and said outermost titanium dioxide layer has an optical thickness of 86±12 nm, said pigment being blue.
18. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 148±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and the outermost titanium dioxide layer has an optical thickness of 410±12 nm, said pigment being green.
19. The multilayer effect pigment of claim 1 wherein said inner titanium dioxide layer has an optical thickness of 374±12 nm, said silicon dioxide layer has an optical thickness of 117±8 nm, and the outermost titanium dioxide layer has a optical thickness of 374±12 nm, said pigment being green.
20. The multilayer effect pigment of claim 1 wherein said titanium dioxide layer has an optical thickness of 372±12 nm, said silicon dioxide layer has an optical thickness of 58±8 nm, and the outermost titanium dioxide layer has a optical thickness of 417±12 nm, said pigment being green.
21. The multilayer effect pigment of claim 1 wherein said transparent substrate is glass flake.
22. A multilayer effect pigment comprising:
a transparent substrate having a layer of titanium dioxide thereon, said layer having a optical thickness of 489±12 nm;
a layer of silicon dioxide on said titanium dioxide layer, said silicon dioxide layer having an optical thickness of 117±8 nm; and
an outermost titanium dioxide layer placed on said silicon dioxide layer and having an optical thickness of 489±12 nm, said pigment being red.
23. A cosmetic comprising liquid or powder and said multilayer effect pigment of claim 1 .
24. The multilayer effect pigment of claim 1 , wherein the pigment has a chromaticity of at least 40.0.