Compound laser beam welding
View Patent ↗Hot cracking in laser welds produced in metal workpieces, especially aluminum or magnesium sheet alloys, is avoided by suitably combining the beams of two different lasers, for example a CO 2 laser and a YAG laser, into a compound beam that is moved along a weld path in the surface of the workpiece. The power level of at least one of the lasers is cyclically varied so that weld nugget segments of different alternating, hot crack free, configurations are produced in a linear weld.
1. A method for forming a weld in an assembly comprising the edge of a first sheet metal flange folded over the edge of a second sheet metal flange, the edge of said second sheet metal flange being enclosed within the folded-over edge portion of said first flange and unfolded sheet portion of said first flange, said method comprising:
combining the beam of a first laser material at a first laser power level with the beam of a second and different laser material at a second laser power level into a compound beam;
directing said compound beam at the surface of the folded-over edge portion of said first flange;
moving said compound beam along said surface in a linear weld path; and
varying at least one of said first laser power level and said second laser power level during said movement of said compound beam so as to produce variation in the width and depth of weld nugget material produced along said weld path.
2. The method of forming a weld as recited in claim 1 in which said first and second sheet metal flanges are made of aluminum alloy and said first laser beam is a carbon dioxide laser and said second laser beam is a YAG laser.
3. The method of forming a weld as recited in claim 2 comprising:
combining the beam of a carbon dioxide laser beam at a carbon dioxide laser power level with the beam of a YAG laser at a YAG laser power level into a compound beam; and
maintaining said carbon dioxide power level at a carbon dioxide power value while varying said YAG laser power level from a first value to a second value where said second value may be zero power, said combination of said carbon dioxide power level with the varied YAG laser power levels producing weld nugget segments along said weld path of alternating different configurations that are free of hot cracks.
4. The method of forming a weld as recited in claim 1 comprising:
moving said compound beam along said surface in a sinusoidal weld path with first alternating peak portions toward the edge of said first sheet metal flange and second alternating peak portions away from said edge; and
varying at least one of said first laser power level and said second laser power level so as to produce alternating larger weld nugget segments at said first alternating peak portions and smaller weld nugget segments at said second alternating peak portions.