Method of cleaning a coated process chamber component
View Patent ↗In a method of cleaning and refurbishing a process chamber component having a metal coating having a surface thereon, the surface of the metal coating is immersed in an acidic solution to remove at least a portion of the process deposits from the surface. Thereafter, the surface of the metal coating is immersed in a basic solution to remove substantially all the metal coating. The component may optionally be bead blasting to roughen a surface of the component, and the metal coating may be re-formed.
1. A method of cleaning a process chamber component, the component comprising a metal coating having a surface comprising process deposits thereon, the method comprising:
(a) immersing the surface of the metal coating in an acidic solution to remove at least a portion of the process deposits from the surface; and
(b) after (a), immersing the surface of the metal coating in a basic solution to remove substantially all the metal coating.
2. A method according to claim 1 wherein (a) comprises immersing the surface in an acidic solution comprising from about 2 to about 8 M HF.
3. A method according to claim 1 wherein (a) comprises immersing the surface in acidic solution comprising from about 5 to about 15 M HNO 3 .
4. A method according to claim 1 wherein (b) comprises immersing the surface in a basic solution comprising from about 1 to about 8 M KOH.
5. A method according to claim 1 wherein the component comprises an underlying ceramic structure having the metal coating thereon, and wherein the method further comprises:
(c) bead blasting the component to provide a surface having a roughness average of less than about 150 microinches.
6. A method according to claim 1 wherein the component comprises an underlying metal structure having the metal coating thereon, and wherein the method further comprises:
(c) bead blasting the component to provide a surface having a roughness average of at least about 160 microinches.
7. A method according to claim 1 wherein the metal coating comprises one or more of aluminum, titanium, copper and chromium.
8. A method according to claim 7 wherein the component comprises an underlying structure comprising aluminum oxide, aluminum nitride, silicon carbide and silicon nitride, titanium, stainless steel, copper or tantalum.
9. A method of cleaning a process chamber component, the component comprising a metal coating having a surface with process deposits thereon, the metal coating being composed of aluminum, titanium, copper or chromium, the method comprising:
(a) immersing the surface of the metal coating in an acidic solution having a composition selected to remove a least a postion of the process deposits from the surface substantially without corroding the surface, the acidic solution comprising at least one of HF and HNO 3 ; and
(b) after (a), immersing the surface of the metal coating in a basic solution having a composition selected to remove substantially all the metal coating, the basic solution comprising KOH.
10. A method according to claim 9 wherein (a) comprises immersing the surface in an acidic solution comprising at least one of (i) HF in a concentration of from about 2 to 8 M, and (ii) HNO 3 in a concentration of from about 5 to 15 M, and wherein (b) comprises immersing the surface in a basic solution comprising KOH in a concentration of from about 1 to 8 M.
11. A method according to claim 9 wherein the metal coating is composed of aluminum.