High purity ZrB
View Patent ↗A high purity ZrB 2 powder having a purity of 99.9 wt % or higher excluding C and gas components, and a manufacturing method of such high purity ZrB 2 powder, including the steps of: subjecting a Zr sponge raw material to electron beam melting and casting to prepare an ingot having a purity of 99.9 wt % or higher; cutting the ingot into a cut powder and hydrogenating the cut powder into ZrH 2 ; pulverizing and dehydrogenating the resultant product into a Zr powder and oxidizing the Zr powder at a high temperature in an oxygen atmosphere into a ZrO 2 fine powder; and mixing the ZrO 2 fine powder with B having a purity of 99.9 wt % or higher so as to reduce ZrO 2 and obtain a ZrB 2 powder having a purity of 99.9 wt % or higher. Purity of the ZrB 2 powder for use in sintering is made to be 99.9 wt % or higher, which is required in the manufacture of a ZrB 2 single crystal substrate with the high frequency induction heating FZ method (Floating Zone Method), and it is thereby possible to obtain a high purity ZrB 2 powder and the manufacturing method thereof enabling the enlargement of a ZrB 2 single crystal substrate and reduction in the manufacturing costs associated therewith.
1. A high purity ZrB 2 powder having an average grain size of 100 μm or less and a purity of 99.9 wt % or higher excluding impurity C and other gas component elements, wherein a content of impurity C is 0.1 wt % or lower and contents of Fe, Cr and Nb as impurities are each 0.05 wt % or lower.
2. A high purity ZrB 2 powder according to claim 1 , wherein contents of Hf and Ti as impurities are each 0.1 wt % or lower.
3. The high purity ZrB 2 powder according to claim 1 , wherein said powder has a purity of 99.95 wt % or higher excluding gas component elements.
4. The high purity ZrB 2 powder according to claim 1 , wherein said powder has a purity of 99.99 wt % excluding gas component elements.
5. The high purity ZrB 2 powder according to claim 1 , wherein said powder is of a quality enabling an ingot of a single crystal of a size of 10 mm to 50 mm to be produced therefrom.
6. A manufacturing method of high purity ZrB 2 powder, including the steps of:
subjecting a Zr sponge raw material to electron beam melting and casting to prepare an ingot;
cutting the ingot into a cut powder and hydrogenating the cut powder into ZrH 2 ;
pulverizing and dehydrogenating the resultant product into a Zr powder and oxidizing the Zr powder at a high temperature in an oxygen atmosphere into a ZrO 2 fine powder; and
mixing the ZrO 2 fine powder with B so as to reduce ZrO 2 and obtain a ZrB 2 powder, wherein said ZrB 2 powder has an average grain size of 100 μm or less and a purity of 99.9 wt % or higher excluding impurity C and other gas component elements, wherein a content of impurity C is 0.1 wt % or lower and contents of Fe, Cr and Nb as impurities are each 0.05 wt % or lower.
7. A method according to claim 6 , wherein a content of each of Hf and Ti as impurities in said ZrB 2 powder is 0.1 wt % or lower.
8. A high purity ZrB 2 powder, comprising:
a high purity ZrB 2 powder having an average grain size of 100 μm or less and a purity of 99.9 wt % or higher excluding impurity C and gas component elements;
said powder having a content of each of Fe, Cr and Nb as an impurity element of 0.05 wt % (500 wtppm) or lower;
said powder having a content of each of Hf and Ti as an impurity element of 0.1 wt % (1000 wtppm) or lower;
said powder having a content of impurity C of 0.1 wt % (1000 wtppm) or lower; and
said powder being of a quality enabling an ingot of a single crystal of a size of 10 mm to 50 mm to be produced.
9. The high purity ZrB 2 powder according to claim 8 , wherein said content of impurity C is within a range of 20 to 950 wtppm.
10. The high purity ZrB 2 powder according to claim 9 , wherein said content of Hf is within a range of 5 to 450 wtppm.
11. The high purity ZrB 2 powder according to claim 10 , wherein said content of Fe is within a range of 2 to 150 wtppm, and said content of Cr is within a range of 1 to 160 wtppm.
12. The high purity ZrB 2 powder according to claim 11 , wherein said content of Nb is within a range of 2 to 30 wtppm.
13. The high purity ZrB 2 powder according to claim 11 , wherein said content of Nb is less than 1 wtppm.
14. The high purity ZrB 2 powder according to claim 10 , wherein said content of Ti is within a range of 40 to 350 wtppm.
15. The high purity ZrB 2 powder according to claim 10 , wherein said content of Ti is less than 1 wtppm.
16. The high purity ZrB 2 powder according to claim 8 , wherein said powder has a purity of 99.95 wt % or higher as determined when excluding gas component elements including impurity C.
17. The high purity ZrB 2 powder according to claim 8 , wherein said powder has a purity of 99.99 wt %, as determined when excluding gas component elements including impurity C.
18. The high purity ZrB 2 powder according to claim 17 , wherein said content of impurity C is 20 wtppm, a combined content of Hf and Ti is less than 6 wtppm, and a combined content of Fe, Cr and Nb is less than 4 wtppm.