Process for cleaning aluminum and aluminum alloy surfaces with nitric acid and chromic acid-free compositions
View Patent ↗A process for cleaning (e.g., desmutting) an aluminum surface, using compositions free of nitric acid and chromic acid and comprising, in one embodiment, an oxidant and at least one mineral acid salt. In another embodiment, the process uses a composition free of nitric acid and chromic acid and comprising an oxidant, at least one mineral acid salt, and a complexing agent which is a salt of an organic acid. Due at least in part to the absence of nitric and chromic acids, and in particular, strong mineral acids, the cleaning processes of the present invention remove smut residues from aluminum surfaces without significant etching of the aluminum.
1. A process for pretreating an aluminum or aluminum alloy surface which comprises:
cleaning the surface;
etching the surface; and
applying to the etched surface a composition free of nitric and chromic acid which comprises:
an oxidant;
at least one mineral acid; and
at least one complexing agent which is a salt of an organic acid;
wherein the composition has a pH in the range from about 2 to about 3.
2. The process of claim 1 wherein the applying comprises desmutting the surface.
3. The process of claim 1 wherein the etching results in formation of a smut on the surface.
4. The process of claim 1 further comprising zincating the surface subsequent to the applying.
5. The process of claim 1 wherein the applying substantially does not etch the surface.
6. The process of claim 1 wherein the oxidant is a monopersulfate, persulfate, permanganate, peroxide, perborate, percarbonate, chlorate, bromate, iodate, perchlorate, perbromate, periodate, or a mixture of two or more of said oxidants.
7. The process of claim 1 wherein the mineral acid salt is a sodium, potassium, or ammonium sulfate or bisulfate.
8. The process of claim 1 wherein the composition is an aqueous composition containing from about 1 to about 400 g/l of the oxidant and from about 0.5 to about 100 g/l of one or more mineral acid salts.
9. The process of claim 1 wherein the complexing agent is an alkali metal or ammonium salt of acetic acid, citric acid, tartaric acid, gluconic acid, lactic acid, propionic acid, or mixtures thereof.
10. A process for pretreating an aluminum or aluminum alloy surface which comprises:
cleaning the surface;
etching the surface, wherein the etching results in formation of a smut on the surface;
desmutting the etched surface by applying thereto a composition free of nitric and chromic acid which comprises:
an oxidant;
at least one mineral acid salt; and
at least one complexing agent which is a salt of an organic acid, wherein the composition has a pH in the range from about 2 to about 3; and zincating the surface subsequent to the applying.
11. The process of claim 10 wherein the applying substantially does not etch the surface.
12. The process of claim 10 wherein the oxidant is a monopersulfate, persulfate, permanganate, peroxide, perborate, percarbonate, chlorate, bromate, iodate, perchlorate, perbromate, periodate, or a mixture of two or more of said oxidants.
13. The process of claim 10 wherein the mineral acid salt is a sodium, potassium, or ammonium sulfate or bisulfate.
14. The process of claim 10 wherein the composition is an aqueous composition containing from about 1 to about 400 g/l of the oxidant, from about 0.5 to about 100 g/l of one or more mineral acid salts, and from about 0.1 to about 50 g/l of the complexing agent.
15. The process of claim 10 wherein the complexing agent is an alkali metal or ammonium salt of acetic acid, citric acid, tartaric acid, gluconic acid, lactic acid, propionic acid, or mixtures thereof.