Nickel crucible for melting analytical sample, method of preparing analytical sample and method of analysis
View Patent ↗A nickel crucible used for melting an analytical sample in the pretreatment of the analytical sample, characterized in that the purity of the nickel crucible is 99.9999 wt % or higher. Also provided is a method of analysis, comprising melting a sample by the use of the nickel crucible for melting having a purity of 99.9999 wt % or higher, and analyzing the melt to thereby obtain an analytical result in which the respective lower limits of determination of Mn, Al, Si, Mg, Pb, Fe, Co, Ti, Cu, Cr, Zr, Mo, and W are Mn: 5 wtppm, Al: 10 wtppm, Si: 10 wtppm, Mg: 5 wtppm, Pb: 5 wtppm, Fe: 5 wtppm, Co: 5 wtppm, Ti: 20 wtppm, Cu: 20 wtppm, Cr: 10 wtppm, Zr: 5 wtppm, Mo: 2 wtppm, and W: 10 wtppm. In light of the recent analytical technology demanded of fast and accurate measurement of high purity materials, high purity analysis is attained through inhibition of mixing of impurities from the crucible.
1. A nickel crucible utilized for melting an analytical sample in the pretreatment of the analytical sample, wherein the purity of the nickel crucible is 99.9999 wt % or higher.
2. A method of treating an analytical sample using a high purity nickel crucible, including a step of preliminarily melting the analytical sample in a nickel crucible having a purity of 99.9999 wt % or higher to obtain the analytical sample.
3. The method of treating an analytical sample according to claim 2 , further including steps of weighing and placing the analytical sample in the crucible, and during said preliminary melting step, melting the analytical sample using a basic flux comprising one or more types of alkali chemicals selected from Na 2 CO 3 , K 2 CO 3 , H 3 BO 3 , NaOH, KOH, Na 2 B 2 O 7 , and Li 2 B 2 O 7 , or said basic flux added with one or more types of oxidizing agents selected from Na 2 O, Na 2 O 2 , K 2 O, K 2 O 2 , KNO 3 , and KClO 3 , or one or more types of acid flux selected from Na 2 S 2 O 7 , K 2 S 2 O 7 , and NaHSO 4 .
4. A method according to claim 2 , further comprising the step of analyzing the analytical sample as melted during said preliminary melting step with lower limits of quantification for Mn, Al, Si, Mg, Pb, Fe, Co, Ti, Cu, Cr, Zr, Mo, and W of respectively Mn: 5 wtppm, Al: 10 wtppm, Si: 10 wtppm, Mg: 5 wtppm, Pb: 5 wtppm, Fe: 5 wtppm, Co: 5 wtppm, Ti: 20 wtppm, Cu: 20 wtppm, Cr: 10 wtppm, Zr: 5 wtppm, Mo: 2 wtppm, and W: 10 wtppm.
5. A method of analysis comprising the steps of melting an analytical sample by the use of a nickel crucible having a purity of 99.9999 wt % or higher, and performing analyses with the analytical sample melted during said melting step to obtain analytical results, in which lower limits of quantification for Mn, Al, Si, Mg, Pb, Fe, Co, Ti, Cu, Cr, Zr, Mo, and W are respectively Mn: 5 wtppm, Al: 10 wtppm, Si: 10 wtppm, Mg: 5 wtppm, Pb: 5 wtppm, Fe: 5 wtppm, Co: 5 wtppm, Ti: 20 wtppm, Cu: 20 wtppm, Cr: 10 wtppm, Zr: 5 wtppm, Mo: 2 wtppm, and W: 10 wtppm.