Composition and process for improved zincating magnesium and magnesium alloy substrates
View Patent ↗Improved compositions and processes for zincating magnesium and magnesium alloy substrates. An aqueous zincating composition having a pH of from about 8 to about 11 and including zinc ions, a complexing agent, fluoride ions and a reducing agent. A non-electrolytic process for zincating a magnesium or magnesium alloy substrate, including immersing the substrate in the non-electrolytic aqueous zincating composition for a time sufficient to deposit a zincate on the substrate. A non-electrolytic process for zincating a magnesium or magnesium alloy substrate, including preparing a aqueous non-electrolytic composition comprising zinc ions, a complexing agent, fluoride ions and a pH in the range from about 8 to about 11; adding to the composition an amount of a reducing agent sufficient to improve deposition of zincate on the magnesium or magnesium alloy substrate; and immersing the substrate in a composition for a time sufficient to deposit the zincate on the substrate.
1. An aqueous zincating composition having a pH of from about 8 to about 11 and comprising zinc ions, a complexing agent, fluoride ions and a reducing agent, wherein the reducing agent is one or more selected from the group consisting of a hypophosphite, a borane compound, a borohydride, a hydrazine, an alkyl- and/or an aryl-substituted hydrazine, a phosphite, ascorbic acid, isoascorbic acid, hypophosphoric acid, and phosphorous acid.
2. The composition of claim 1 wherein the complexing agent is provided as a pyrophosphate salt, a tripolyphosphate salt, a phosphate salt or a mixture of two or more thereof.
3. The composition of claim 2 wherein the salt comprises potassium, sodium or ammonium cations or a mixture thereof.
4. The composition of claim 1 wherein the zinc ions are provided as one or more of zinc sulfate, zinc acetate, zinc oxide, zinc chloride, zinc fluoride, zinc citrate or zinc sulfonate.
5. The composition of claim 1 wherein the fluoride ions are provided as one or more of potassium fluoride, sodium fluoride, zinc fluoride, ammonium fluoride or ammonium bifluoride.
6. The composition of claim 1 wherein the composition comprises:
from about 0.005 M to about 1.5 M of the zinc ions,
from about 0.01 M to about 2 M of the complexing agent,
from about 0.0025 M to about 1.5 M of the fluoride ions and
from about 0.005 M to about 1.5 M of the reducing agent.
7. A non-electrolytic process for zincating a magnesium or magnesium alloy substrate, comprising:
immersing the substrate in a non-electrolytic aqueous zincating composition for a time sufficient to deposit a zincate on the substrate,
wherein the composition comprises zinc ions, a complexing agent, fluoride ions and a reducing agent and has a pH in the range from about 8 to about 11, wherein the reducing agent is one or more selected from the group consisting of a hypophosphite, a borane compound, a borohydride, a hydrazine, an alkyl- and/or an aryl-substituted hydrazine, a phosphite, ascorbic acid, isoascorbic acid, hypophosphoric acid, and phosphorous acid.
8. The process of claim 7 wherein the complexing agent is provided as comprises a pyrophosphate salt, a tripolyphosphate salt, a phosphate salt or a mixture of two or more thereof.
9. The process of claim 8 wherein the salt comprises potassium, sodium or ammonium cations or a mixture thereof.
10. The process of claim 7 wherein the zinc ions are provided as one or more of zinc sulfate, zinc acetate, zinc hydroxide, zinc oxide, zinc chloride, zinc fluoride, zinc citrate or zinc sulfonate.
11. The process of claim 7 wherein the fluoride ions are provided as one or more of potassium fluoride, sodium fluoride, zinc fluoride, ammonium fluoride or ammonium bifluoride.
12. The process of claim 7 wherein the composition comprises:
from about 0.005 M to about 1.5 M of the zinc ions,
from about 0.01 M to about 2 M of the complexing agent,
from about 0.0025 M to about 1.5 M of the fluoride ions and
from about 0.005 M to about 1.5 M of the reducing agent.
13. The process of claim 7 wherein the deposition and/or at least one property of the zincate is improved compared to the same process in the absence of the reducing agent.
14. The process of claim 7 wherein the amount of reducing agent is sufficient to improve at least one property of the zincate deposited on the substrate, wherein the at least one property comprises one or more of brightness, color, shininess, adhesion to the substrate and thickness uniformity.
15. A non-electrolytic process for zincating a magnesium or magnesium alloy substrate, comprising:
preparing an aqueous non-electrolytic composition comprising zinc ions, a complexing agent, fluoride ions and a pH in the range from about 8 to about 11;
adding to the composition an amount of a reducing agent sufficient to improve deposition of zincate on the magnesium or magnesium alloy substrate; and
immersing the substrate in the composition for a time sufficient to deposit the zincate on the substrate, wherein the reducing agent is one or more selected from the group consisting of a hypophosphite, a borane compound, a borohydride, a hydrazine, an alkyl- and/or an aryl-substituted hydrazine, a phosphite, ascorbic acid, isoascorbic acid, hypophosphoric acid, and phosphorous acid.
16. The process of claim 15 wherein the amount of reducing agent is sufficient to improve at least one property of the zincate deposited on the substrate, wherein the at least one property comprises one or more of brightness, color, shininess, adhesion to the substrate and thickness uniformity.