Chromium-free pickle for plastic surfaces
View Patent ↗A pickling solution for the surface pre-treatment of plastic surfaces in preparation for metallization, the solution comprising a source of Mn(VII) ions; and an inorganic acid; wherein the pickling solution is substantially free of chromium (VI) ions, alkali ions, and alkaline-earth ions.
1. A pickling solution for the surface pre-treatment of plastic surfaces in preparation for metallization, the solution comprising:
Mn(VII) ions; and
an inorganic acid, wherein the inorganic acid is at least one acid from the group consisting of phosphoric acid, peroxomonophosphoric acid, peroxodiphosphoric acid, sulfuric acid, peroxomonosulfuric acid and peroxodisulfuric acid, and the inorganic acid has a concentration between 1 and 18.5 mol/l;
wherein the pickling solution is substantially free of chromium (VI) ions, alkali ions, and alkaline-earth ions, wherein the Mn(VII) ions are present at a concentration of between 0.001 and 0.5 mol/l and the Mn(VII) ions are obtained by means of an oxidation cell from a Mn-ion of an oxidation state lower than (VII); and
wherein the pickling solution maintains a pickling effect at an operating temperature of between about 55° C. and about 80° C. for greater than 24 hours.
2. The pickling solution according to claim 1 further comprising ions of one or more elements selected from the group consisting of Ag, Bi, V, Mo, Cu, and combinations thereof.
3. The pickling solution according to claim 1 comprising between 0.001 and 2.0 mol/l ions of one or more elements selected from the group consisting of Ag, Bi, V, Mo, Cu, and combinations thereof.
4. The pickling solution of claim 1 further comprising a wetting agent.
5. The pickling solution of claim 1 further comprising a defoamer.
6. The pickling solution according to claim 1 , wherein the solution for the oxidative production of Mn(VII) ions is an acidic solution.
7. The pickling solution according to claim 1 wherein the solution for the oxidative production of Mn(VII) ions includes as a source of Mn ions of an oxidation stage lower than (VII) at least one manganese compound selected from the group consisting of MnCO 3 , MnSO 4 , MnO, MnCl 2 , Mn(CH 3 COO) 2 , Mn(NO 3 ) 2 , Mn 2 O 3 , MnPO 4 , MnO(OH), Mn(CH 3 COO) 3 , MnF 3 , MnO 2 , and combinations thereof.
8. The pickling solution according to claim 7 wherein the solution for the oxidative production of Mn(VII) ions includes at least one acid selected from the group consisting of phosphoric acid, peroxomonophosphoric acid, peroxodiphosphoric acid, sulfuric acid, peroxomonosulfuric acid, peroxodisulfuric acid, and combinations thereof.
9. The pickling solution of claim 1 wherein:
the inorganic acid is at least one acid from the group consisting of phosphoric acid, peroxomonophosphoric acid, peroxodiphosphoric acid, sulfuric acid, peroxomonosulfuric acid and peroxodisulfuric acid;
the inorganic acid has a concentration between 1 and 18.5 mol/l;
the pickling solution further comprises between 0.001 and 2.0 mol/l ions of one or more elements from the group consisting of Ag, Bi, V, Mo, and Cu; and
the pickling solution further comprises a wetting agent.
10. A process for pickling ABS plastic surfaces comprising contacting the plastic surface to be pickled with an acidic treatment solution which comprises Mn(VII) ions and is free of alkali and alkaline earth ions, wherein:
the treatment solution comprises at least one inorganic acid from the group consisting of phosphoric acid, peroxomonophosphoric acid, peroxodiphosphoric acid, sulfuric acid, peroxomonosulfuric acid and peroxodisulfuric acid, and the inorganic acid has a concentration between 1 and 18.5 mol/l;
Mn(VII) ions are present in the treatment solution at a concentration of between 0.001 and 0.5 mol/l and the Mn(VII) ions are obtained by means of an oxidation cell from a Mn-ion of an oxidation stage lower than (VII) and
wherein the pickling solution maintains a pickling effect at an operating temperature of between about 55° C. and about 80° C. for greater than 24 hours.
11. A pickling solution for the surface pre-treatment of plastic surfaces in preparation for metallization, the solution comprising:
a source of Mn(VII) ions; and
an inorganic acid, wherein the inorganic acid is at least one acid from the group consisting of phosphoric acid, peroxomonophosphoric acid, peroxodiphosphoric acid, sulfuric acid, peroxomonosulfuric acid and peroxodisulfuric acid, and the inorganic acid has a concentration between 1 and 18.5 mol/l;
wherein the pickling solution is substantially free of chromium (VI) ions, alkali ions, and alkaline-earth ions;
wherein the pickling solution further comprises between 0.001 and 2.0 mol/l ions of one or more elements from the group consisting of Ag, Bi, V, Mo, and Cu; and
wherein the pickling solution maintains a pickling effect at an operating temperature of between about 55° C. and about 80° C. for greater than 24 hours.
12. The pickling solution according claim 11 wherein the source of Mn(VII) ions provides Mn(VII) ions at a concentration between 0.001 and 0.5 mol/l.