Low temperature fireable thick film silver paste
View Patent ↗The present invention is directed to an electroconductive thick film paste composition comprising Ag and a Pb-free bismuth-tellurium oxide both dispersed in an organic medium, wherein the paste is fireable at temperatures below 420° C. The paste is especially useful for forming electrodes on substrates such as glass or films, particularly electrochromic glass or films, that would be damaged by higher firing temperatures. The present invention is further directed to a device comprising an electrode formed from the paste composition and, in particular, to an electrochromic device comprising such an electrode.
1. A thick film paste composition comprising:
(a) 65-85 wt % Ag;
(b) 1-8 wt % Pb-free bismuth-tellurium-oxide consisting of 22-42 wt % Bi 2 O 3 , 58-78 wt % TeO 2 , 0.1-7 wt % Li 2 O and 0.1-4 wt % TiO 2 , wherein the wt % of Bi 2 O 3 , TeO 2 , Li 2 O and TiO 2 are based on the total weight of said bismuth-tellurium oxide; and
(c) an organic medium;
wherein said Ag, and said bismuth-tellurium-oxide are dispersed in said organic medium and wherein said wt % of said Ag and said bismuth-tellurium-oxide are based on the total weight of said paste composition.
2. The paste composition of claim 1 comprising 70-80 wt % Ag and 2-7 wt % bismuth-tellurium oxide, wherein said wt % are based on the total weight of said paste composition.
3. The paste composition of claim 1 , said bismuth-tellurium-oxide consisting of 22-42 wt % Bi 2 O 3 , 58-78 wt % TeO 2 , 0.9-5 wt % Li 2 O and 0.3-2 wt % TiO 2 , based on the total weight of said bismuth-tellurium oxide.
4. A thick film paste composition comprising:
(a) 65-85 wt % Ag;
(b) 1-8 wt % Pb-free bismuth-tellurium-oxide consisting of 22-42 wt % Bi 2 O 3 , 58-78 wt % TeO 2 , 0.1-7 wt % Li 2 O, 0.1-4 wt % TiO 2 , 0.1-8 wt % B 2 O 3 , 0.1-3 wt % ZnO and 0.3-2 wt % P 2 O 5 , wherein the wt % of Bi 2 O 3 , TeO 2 , Li 2 O, TiO 2 , B 2 O 3 , ZnO and P 2 O 5 are based on the total weight of said bismuth-tellurium oxide; and
(c) an organic medium;
wherein said Ag and said bismuth-tellurium-oxide are dispersed in said organic medium and wherein said wt % of said Ag and said bismuth-tellurium-oxide are based on the total weight of said paste composition.
5. The paste composition of claim 4 , said bismuth-tellurium-oxide consisting of 22-42 wt % Bi 2 O 3 , 58-78 wt % TeO 2 , 0.9-5 wt % Li 2 O, 0.3-2 wt % TiO 2 , 09-6 wt % B 2 O 3 , 0.1-2 wt % ZnO and 0.3-1 wt % P 2 O 5 , based on the total weight of said bismuth-tellurium oxide.
6. The paste composition of any of claims 1 , 2 or 3 - 5 wherein said bismuth-tellurium oxide is in the form of a glass frit.
7. A device comprising an electrode formed from the paste composition of claims 1 , 2 or 3 - 5 , wherein said paste composition has been fired at temperatures below 420° C. to remove the organic medium and form said electrode.
8. The device of claim 7 , wherein said device is an electrochromic device.
9. The device of claim 8 , wherein said paste composition has been fired at temperatures not exceeding 405° C. to remove the organic medium and form said electrode.
10. The device of claim 7 , wherein said paste composition has been fired at temperatures not exceeding 405° C. to remove the organic medium and form said electrode.