Method for electroless plating
The present invention discloses a method for electroless plating of a metal or metal alloy onto a metal or a metal alloy structure comprising a metal such as molybdenum or titanium and alloys containing such metals. The method comprises the steps of activation, treatment in an aqueous solution comprising at least one nitrogen-containing compound or a hydroxy carboxylic acid and electroless plating of a metal or metal alloy.
1. A method for electroless plating comprising in this order the steps of
(i) providing a non-conductive substrate having on at least one side attached thereto a metal or metal alloy structure selected from the group consisting of molybdenum, titanium, zirconium, aluminium, chromium, tungsten, niobium, tantalum and alloys thereof,
(ii) contacting said substrate with an activator comprising palladium ions,
(iii) contacting said substrate with an aqueous solution containing at least one nitrogen-containing substance selected from the group consisting of quaternary ammonium polymers, polyamido amines, tetra-ammonium hydroxy compounds having alkyl groups with 2 to 6 carbon atoms, alkanol amines, quaternary ammonium salts based on fatty amines and quaternised aliphatic amine ethoxylates and mixtures thereof, and
(iv) depositing a metal or metal alloy onto said activated surface by means of electroless plating.
2. A method according to claim 1 wherein the metal or metal alloy structure in step (i) is selected from the group consisting of molybdenum, titanium and alloys thereof.
3. A method according to claim 1 wherein the aqueous solution in step (iii) further comprises a hydroxy carboxylic acid.
4. A method according to claim 1 wherein the metal or metal alloy deposited in step (iv) is selected from the group consisting of copper, copper alloys, nickel and nickel alloys.
5. A method according to claim 3 wherein the hydroxy carboxylic acid in step (iii) comprises tartaric acid, citric acid, gluconic acid, 5-sulfosalicylic acid or mixtures of two or more thereof.
6. A method according to claim 1 wherein in step (ii) the palladium ions are deposited on the metal or metal alloy structure by an immersion-type reaction.
7. A method according to claim 1 wherein the at least one nitrogen-containing substance in step (iii) is selected from the group consisting of quaternary ammonium polymers and polyamido amines.