Composition and method for removal of organic paint coatings from substrates
View Patent ↗The invention relates to a non-aqueous stripping composition for removing cured organic paint from substrates comprising i. a source of hydroxide ions; ii. a high-boiling alcohol having a boiling point of at least 100° C.; and iii. at least one surfactant represented by the following formula R—O—(CH 2 CH 2 O) n H and wherein R is an alkyl chain, linear or branched having a 2 to 24 carbon atom chain length.
1. Non-aqueous stripping composition for removing cured organic paint from substrates comprising
i. a source of hydroxide ions;
ii. a high-boiling alcohol having a boiling point of at least 150° C.; and
iii. at least one surfactant represented by the following formula
R—O—(CH 2 CH 2 O) n H and
wherein R is an alkyl chain, linear or branched having a 2 to 30 carbon atom chain length, and n ranges between 2 and 100,
wherein the composition is essentially free of added water and
wherein the high-boiling alcohol is at a concentration in the range from 70 to 99 wt % of the composition.
2. Composition according to claim 1 wherein the substrate is aluminium, steel, galvanized steel, magnesium, zinc and engineering plastic.
3. Composition according to claim 1 wherein R ranges between 8 and 14.
4. Composition according to claim 1 wherein R is selected from 2-propylheptly, n-octadecyl, n-nonadecyl, n-decadecyl, n-dodecyl, —CH 2 —CH(C 3 H 9 )—(CH 2 ) 4 —CH 3 , —CH(CH 3 )—(CH 2 ) 9 —CH 3 , —CH(CH 3 )—(CH 2 ) 10 —CH 3 , —CH(CH 3 )—(CH 2 ) 11 —CH 3 and n-C 12 -n-C 15 .
5. Composition according to claim 1 wherein n ranges between 6 and 25.
6. Composition according to claim 1 wherein the source of hydroxide is an alkali metal hydroxide having a concentration of 1 to 10 wt. %.
7. Composition according to claim 1 wherein the alkali metal hydroxide is sodium or potassium hydroxide.
8. Composition according to claim 1 wherein the high boiling alcohol is a polyethylene glycol.
9. Composition according to claim 8 wherein the polyethylene glycol is a triethylene glycol or tetraethylene glycol.
10. Composition according to claim 1 wherein the composition is essentially free of alkoxylated alkylphenol surfactants.
11. Composition according to claim 1 wherein the composition is essentially free of amines.
12. Composition according to claim 1 wherein the water content in the composition is less than 2 wt. %.
13. Composition according to claim 1 wherein the water content in the composition is less than 0.5 wt. %.
14. Composition according to claim 1 wherein the alcohol content ranges between 90 wt. % to 99 wt. %.
15. A method for stripping cured organic paint from the aluminium, steel, galvanized steel, magnesium, or plastic based substrates comprising the steps of
i. providing a stripping composition according to claim 1 in a tank device;
ii. bringing into contact the aluminium, steel, galvanized steel, magnesium, or plastic based substrates with the stripping composition in the tank device;
iii. heating said stripping composition to a temperature of between 50 and 250° C. for a period of between 30 and 300 minutes and thereby removing or loosening the cured organic paint from the aluminium, steel, galvanized steel, magnesium, zinc or plastic based substrates
iv. completely removing the organic paint from the substrate by applying a high pressure water spray to the substrate surface.
16. Method according to claim 15 wherein the water spray applied in step iv. has a pressure of between 50 and 250 bar.
17. Method according to claim 15 wherein the temperature ranges between 100 and 150° C. and the treatment time between 45 to 100 minutes.
18. Method according to claim 15 wherein the cured organic paint is a polyester powder coating, a 2-part epoxy coating, a epoxy-polyester hybrid powder coating or a polyester-TGIC powder coating.