Fibrous sheet that disintegrates in water, process for manufacturing said fibrous sheet, core consisting of strips of said fibrous sheet
A fibrous sheet having a basis weight of between 20 and 1000 g/m 2 that disintegrates in water, has 10% to 70% starch on the basis of the total weight of the dry fibrous sheet. The disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm 2 , is less than 50 seconds. A loss of strength of the sheet measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being wetted with water for a duration of 6 seconds, and/or a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%. The fibrous sheet may be used for the manufacture of a water disintegrable core in a roll of tissue paper.
1. A fibrous sheet having a basis weight of between 100 to 600 g/m 2 that disintegrates in water, comprising:
(1) at least 30% of paper making fibres and (2) 15 to 40% starch on a basis of the total weight of the fibrous sheet when dry;
wherein the disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm 2 , is less than 50 seconds;
wherein a loss of strength measured in accordance with a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85°, after having been wetted with water for a duration of 6 seconds;
wherein the fibrous sheet is being manufactured according to a wet papermaking process;
wherein said starch is substantially uniformly distributed through the thickness of the fibrous sheet;
and wherein the paper making fibres are coated with said starch by: (a) incorporating starch in a pulp at a temperature at which starch is not soluble in water, or (b) applying starch in a dry state on a wet web and subsequently drying the web, during the wet papermaking process.
2. A fibrous sheet having a basis weight of between 100 to 600 g/m 2 that disintegrates in water, comprising:
(1) at least 30% of paper making fibres and (2) 15 to 40% starch on a basis of the total weight of the fibrous sheet when dry;
wherein the disintegration time in water, measured in accordance with standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm 2 , is less than 50 seconds;
wherein a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%;
wherein the fibrous sheet is being manufactured according to a wet papermaking process;
wherein said starch is substantially uniformly distributed through the thickness of the fibrous sheet;
and wherein the paper making fibres are coated with said starch by: (a) incorporating starch in a pulp at a temperature at which starch is not soluble in water, or (b) applying starch in a dry state on a wet web and subsequently drying the web, during the wet papermaking process.
3. A fibrous sheet having a basis weight of between 100 to 600 g/m 2 that disintegrates in water in less than 120 seconds, comprising:
(1) at least 30% of paper making fibres and (2) 15 to 40% starch on a basis of the total weight of the fibrous sheet when dry;
wherein a loss of strength measured according to a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85°, after having been wetted with water for a duration of 6 seconds;
wherein a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test, is less than 1%;
wherein the fibrous sheet is being manufactured according to a wet papermaking process;
wherein said starch is substantially uniformly distributed through the thickness of the fibrous sheet;
and wherein the paper making fibres are coated with said starch by: (a) incorporating starch in a pulp at a temperature at which starch is not soluble in water, or (b) applying starch in a dry state on a wet web and subsequently drying the web, during the wet papermaking process.
4. A fibrous sheet having a basis weight of between 100 to 600 g/m 2 that disintegrates in water, comprising:
(1) at least 30% of paper making fibres and (2) 15 to 40% starch on a basis of the total weight of the fibrous sheet when dry;
wherein the disintegration time in water, measured in accordance with the standard NF Q34-020 applied to a specimen of the sheet of 9×8 cm 2 , is less than 50 seconds;
wherein a loss of strength measured according to a defined table test corresponds to a loss of strength of a specimen of said sheet forming an angle of at least 85° after having being been wetted with water for a duration of 6 seconds;
wherein a residual wet strength of the sheet relative to its dry strength, as measured according to a defined ring crush test is less than 1%;
wherein the fibrous sheet is being manufactured according to a wet papermaking process;
wherein said starch is substantially uniformly distributed through the thickness of the fibrous sheet;
and wherein the paper making fibres are coated with said starch by: (a) incorporating starch in a pulp at a temperature at which starch is not soluble in water, or (b) applying starch in a dry state on a wet web and subsequently drying the web, during the wet papermaking process.
5. A core comprising a helical winding of one or more strips comprising a fibrous sheet according to claim 1 .
6. A toilet paper roll comprising a core according to claim 5 .
7. A tampon applicator comprising a fibrous sheet according to claim 1 .