Injectable monophase hydrogels
An injectable monophase hydrogel is provided that is made of a reaction mixture of hyaluronic acids having different molecular weights.
1. An injectable composition comprising a hyaluronic acid gel, the hyaluronic acid gel comprising:
about 5% by weight to about 50% by weight of a first hyaluronic acid having a molecular weight of about 3×10 6 Da; and
about 50% by weight to about 95% by weight of a second hyaluronic acid having a molecular weight of about 3×10 5 Da;
wherein the hyaluronic acid gel is crosslinked via covalent bonding between a bifunctional crosslinker and hydroxyl moieties of the first and second hyaluronic acids; and further wherein the hyaluronic acid gel has a Tan δ 1 Hz in the range of about 0.07 to about 0.12.
2. The injectable composition of claim 1 , wherein the hyaluronic acid gel comprises about 5% by weight to about 30% by weight of the first hyaluronic acid.
3. The injectable composition of claim 1 , wherein the hyaluronic acid gel comprises about 70% by weight to about 95% by weight of the second hyaluronic acid.
4. The injectable composition of claim 1 , wherein the bifunctional crosslinker is selected from the group consisting of bifunctional crosslinking agents epichlorohydrin, divinyl sulfone, 1,4-bis(2,3-epoxypropoxy)butane, 1,4-bisglycidoxybutane, 1,4-butanediol diglycidyl ether (BDDE)), 1,2-bis(2,3-epoxypropoxy)ethylene, 1-(2,3-epoxypropyl)-2,3-epoxycyclohexane, formaldehyde, glutaraldehyde, and crotonaldehyde.
5. The injectable composition of claim 4 , wherein the bifunctional crosslinker is (BDDE).
6. The injectable composition of claim 1 having a concentration of hyaluronic acid gel of between 10 and 40 mg/g.
7. The injectable composition of claim 1 having a concentration of hyaluronic acid gel of between 20 and 30 mg/g.
8. The injectable composition of claim 1 having a concentration of hyaluronic acid gel of 26 mg/g.
9. The injectable composition of claim 1 , wherein the first hyaluronic acid has a first intrinsic viscosity and the second hyaluronic acid has a second intrinsic viscosity different from the first intrinsic viscosity.
10. The injectable composition of claim 1 , wherein hyaluronic acid gel comprises the first hyaluronic acid and the second hyaluronic acid in a weight ratio of 10:90, respectively.
11. The injectable composition of claim 1 , wherein the hyaluronic gel is homogenized.
12. The injectable composition of claim 1 , wherein the injectable composition is sterilized.
13. The injectable composition of claim 1 , wherein the injectable composition further comprises an aqueous solution buffered to a pH of between 6.5 and 7.5.
14. The injectable composition of claim 13 , wherein the aqueous solution is a phosphate buffer.
15. The injectable composition of claim 14 , wherein the aqueous solution is buffered to a pH of between 7.1 and 7.3.
16. The injectable composition of claim 1 , wherein the hyaluronic gel is a monophase hyaluronic acid hydrogel.
17. The injectable composition of claim 1 , wherein the injectable composition has an injectability of about 12 to about 17 Newtons as measured in a standard syringe having a needle of 27 G½, at a rate of 12.5 mm/min.
18. The injectable composition of claim 1 , wherein the hyaluronic acid gel has a degree of crosslinking from about 0.5% to about 70%.
19. The injectable composition of claim 18 , wherein the degree of crosslinking is between about 4% and about 50%.