Nanoparticle compositions and methods for enhancing lead-acid batteries
This disclosure relates to compositions and methods for improving the performance of batteries, such as lead-acid batteries, including reviving or rejuvenating a partially or totally dead battery, by adding an amount of nonionic, ground state metal nanoparticles to the electrolyte of the battery, and optionally recharging the battery by applying a voltage. The metal nanoparticles may be gold and coral-shaped and are added to provide a concentration within the electrolyte of 100 ppb to 2 ppm or more (e.g., up to 5 ppm, 10 ppm, 25 ppm, 50 ppm, or 100 ppm). The metal nanoparticles may be added to battery electrode paste applied to the electrodes to enhance newly manufactured or remanufactured batteries.
1. A method of rejuvenating and/or improving performance of a battery having an electrolyte solution, comprising:
providing a battery having an electrolyte solution;
adding an amount of nonionic, ground state gold nanoparticles to the electrolyte solution so as to bring the concentration of the gold nanoparticles within the electrolyte solution to at least 100 ppb and up to 100 ppm, wherein the gold nanoparticles are formed by laser ablation so as to have a smooth surface with no external bond angles or edges; and
the nonionic, ground state gold nanoparticles rejuvenating or improving the performance of the battery.
2. The method of claim 1 , wherein the addition of the nanoparticles to the electrolyte solution increases a fully charged resting voltage of the battery as compared to a fully charged resting voltage of the battery prior to addition of the nanoparticles.
3. The method of claim 1 , wherein the addition of the nanoparticles to the electrolyte solution increases a cranking amps or cold cranking amps rating of the battery as compared to a cranking amps or cold cranking amps rating of the battery prior to addition of the nanoparticles.
4. The method of claim 1 , wherein the addition of the nanoparticles to the electrolyte solution increases a reserve capacity of the battery as compared to a reserve capacity of the battery prior to addition of the nanoparticles.
5. The method of claim 1 , wherein an average cell voltage of the battery is increased to 2.6 V and/or is increased by 8 to 25%.
6. The method of claim 1 , wherein the nanoparticles comprise coral-shaped nanoparticles having lengths ranging from 15 nm to 100 nm, wherein the coral-shaped nanoparticles have a non-uniform cross section, a smooth surface, and a globular structure formed by multiple, non-linear strands joined together without right angles, with no edges or corners resulting from joining of separate planes.
7. The method of claim 1 , wherein the nanoparticles comprise spherical-shaped nanoparticles having a mean diameter of 3 nm to 20 nm, wherein the spherical-shaped nanoparticles have no surface edges or external bond angles.
8. The method of claim 1 , wherein the nanoparticles have a concentration within the electrolyte solution of at least 100 ppb and up to 50 ppm.
9. The method of claim 1 , wherein the nanoparticles have a concentration within the electrolyte solution of at least 100 ppb and up to 25 ppm.
10. The method of claim 1 , wherein the nanoparticles have a concentration within the electrolyte solution of at least 100 ppb and up to 10 ppm.
11. The method of claim 1 , wherein the nanoparticles have a concentration within the electrolyte solution of at least 100 ppb and up to 5 ppm.
12. The method of claim 1 , further comprising recharging the lead-acid battery by applying a voltage.
13. The method of claim 1 , wherein the gold nanoparticles are added using a composition consisting of the gold nanoparticles and at least one of water or sulfuric acid.
14. A lead-acid battery having improved performance, comprising:
a positive electrode;
a negative electrode;
an electrolyte in electrical contact with the positive and negative electrodes; and
a plurality of nonionic gold nanoparticles dispersed within the electrolyte at a concentration of at least 100 ppb and up to 100 ppm, wherein the gold nanoparticles are formed by laser ablation so as to have a smooth surface with no external bond angles or edges.
15. The lead-acid battery of claim 14 , wherein the nanoparticles have a concentration within the electrolyte of at least 100 ppb and up to 25 ppm.
16. The method of claim 14 , wherein the electrolyte consists of the gold nanoparticles and at least one of water or sulfuric acid, and optionally lead sulfate.
17. A method of manufacturing an enhanced battery electrode paste comprising:
providing a battery electrode paste formed from lead oxide, sulfuric acid, and water to form one or more lead sulfate compounds selected from PbO.PbSO 4 (monobasic lead sulfate), 2PbO.PbSO 4 (dibasic lead sulfate), 3PbO.PbSO 4 (tribasic lead sulfate), and 4PbO.PbSO 4 (tetrabasic lead sulfate); and
adding nonionic, ground state gold nanoparticles to yield the enhanced battery electrode paste, wherein the gold nanoparticles are formed by laser ablation so as to have a smooth surface with no external bond angles or edges.
18. The method of claim 17 , wherein the nonionic, ground state gold nanoparticles are added before, during, or after forming the one or more lead sulfate compounds.