Separation membrane and methods of preparation thereof
A membrane for fluid species transport includes a porous substrate and a selective-transport layer comprising 2-D-material flakes. The porous substrate defines surface pores with dimensions larger than 2 microns, and the selective-transport layer coats the porous substrate and spans across the surface pores. The porous substrate can be contacted with a liquid or coating to fill or coat the surface pores of the porous substrate. Next, a 2-D-material-flake solution is deposited on the porous substrate. Evaporation of solvent from the deposited 2-D-material-flake solution forms the selective-transport layer.
1. A method for fabricating a membrane, the method comprising:
contacting a porous substrate that defines open surface pores with a liquid solution to fill or wet the open surface pores of the porous substrate, wherein the liquid solution comprises a solvent and a solute dissolved in the solvent; then
removing the solvent from the liquid solution to modify the surface charge of the open surface pores with a solute from the liquid solution so as to produce open surface-modified pores with dimensions of at least about 2 microns; then
depositing a 2-D-material-flake solution comprising 2-D-material flakes on the porous substrate with the open surface-modified pores and without a support layer between the otherwise open surface-modified pores of the porous substrate and the selective-transport layer to form a 2-D-material-flake-solution layer with a thickness of less than 40 microns, wherein the solute promotes aggregation of the 2-D-material flakes to inhibit penetration of the 2-D-material flakes into the otherwise open surface-modified pores; and then
evaporating solvent from the 2-D-material-flake-solution layer to form a selective-transport layer comprising 2-D-material flakes on the porous substrate, wherein the selective-transport layer coats the porous substrate and spans across the otherwise open surface-modified pores.
2. The method of claim 1 , the method further comprising removing the solute from the porous substrate after depositing the selective-transport layer on the porous substrate.
3. The method of claim 1 , wherein the porous substrate comprises a fibrous substrate.
4. The method of claim 1 , wherein the 2-D-material-flake solution comprises a composition selected from graphene, graphene oxide, silicene, 2-D silica, phosphorene, boron nitride, borocarbonitrides, transition-metal chalcogenides, MXenes, and mixtures thereof dissolved in water.
5. The method of claim 1 , wherein the solute that modifies the surface charge of the open surface pores of the porous substrate comprises a composition selected from magnesium chloride, magnesium bromide, magnesium hydroxide, magnesium nitrite, magnesium nitrate, magnesium acetate, magnesium citrate, magnesium formate, magnesium fumarate, magnesium gluconate, magnesium lactate, magnesium propionate, magnesium sulfate, calcium chloride, calcium bromide, calcium hydroxide, calcium nitrite, calcium nitrate, calcium acetate, calcium citrate, calcium formate, calcium fumarate, calcium gluconate, calcium lactate, calcium propionate, calcium sulfate, strontium chloride, strontium bromide, strontium hydroxide, strontium nitrite, strontium nitrate, strontium acetate, strontium citrate, strontium formate, strontium fumarate, strontium gluconate, strontium lactate, strontium propionate, strontium sulfate, and mixtures thereof.
6. The method of claim 1 , wherein the solute that modifies the surface charge of the open surface pores of the porous substrate comprises a composition selected from a salt with a cation selected from cetyltrimethylammonium, myristyltrimethylammonium, octadecyltrimethylammonium, decyltrimethylammonium, lauryltrimethylammonium, didecyldimethylammonium, cetylpyridinium, 1-dodecylpyridinium, benzalkonium, benzethonium, benzylhexadecyldimethylammonium, benzyldimethyldodecylammonium, tetramethylammonium, tetraethylammonium, tetrapropylammonium, and tetrabutylammonium; and a polycationic salt, selected from poly(diallyldimethylammonium chloride), poly(vinylbenzyltrimethylammonium chloride), poly(acryloxyethyltrimethyl ammonium chloride), poly(methacryloxy (2-hydroxy) propyltrimethyl ammonium chloride), poly(N-methylvinylpyridinium chloride), poly(allylamine hydrochloride), polyethyleneimine, and mixtures thereof.