Method for producing all-solid-state battery
The present invention is able to provide a method for producing an all-solid-state battery that has a solid electrolyte layer between a positive electrode layer and a negative electrode layer. This method for producing an all-solid-state battery is characterized by comprising: a step wherein a coating liquid is applied to at least one of the positive electrode layer and the negative electrode layer, said coating liquid containing a solid electrolyte solution, which is obtained by dissolving a solid electrolyte in a solvent, and fine particles which are insoluble in the solid electrolyte solution; and a step wherein the solvent is removed from the applied coating liquid, thereby having the solid electrolyte deposit on at least one of the positive electrode layer and the negative electrode layer.
1. A method for producing an all-solid-state battery having a solid electrolyte layer between a positive electrode layer and a negative electrode layer, the method comprising:
preparing a solid electrolyte solution by dissolving a solid electrolyte in an organic solvent, and obtaining a coating solution by suspending fine particles which are insoluble in the solid electrolyte solution;
coating at least one of the positive electrode layer and the negative electrode layer with the coating solution; and
removing the solvent from the coated coating solution to deposit the solid electrolyte on at least one of the positive electrode layer and the negative electrode layer,
wherein the solid electrolyte consists of at least one selected from the group consisting of LiBH 4 , an LiBH 4 -LiI-based material, 3LiBH 4 -LiI, an LiBH 4 -P 2 S 5 -based material, 9LiBH 4 -P 2 S 5 , an LiBH 4 -P 2 I 4 -based material, 9LiBH 4 -P 2 I 4 , 85LiBH 4 -15P 2 I 4 , Li 2 B 12 H 12 , Li 2 B 10 H 10 , LiCB 11 H 12 and LiCB 9 H 10 .
2. The method according to claim 1 , wherein the fine particles comprise at least one selected from the group consisting of silica (SiO 2 ), alumina (Al 2 O 3 ), titania (TiO 2 ), zirconia (ZrO 2 ), magnesia (MgO) and calcia (CaO).
3. The method according to claim 1 , wherein the coating solution comprises the fine particles in an amount of 0.1 to 30% by mass.
4. The method according to claim 1 , wherein the fine particles have an average particle diameter (median diameter d50) of 10 nm to 1 μm.
5. The method according to claim 1 , wherein the solvent comprises at least one selected from the group consisting of H 2 O, an alcohol-based solvent, an ether-based solvent and a nitrile-based solvent.
6. The method according to claim 1 , wherein a series of operations of the step of coating and the step of depositing is repeated a plurality of times.