Method for producing perfluoroelastomer and composition
A method for producing a perfluoroelastomer, which includes carrying out polymerization of a perfluoromonomer in an aqueous medium in the presence of a polymer (1) having a number average molecular weight of 0.3×10 4 or more to provide a perfluoroelastomer, the polymer (1) containing a polymerized unit (1) derived from a monomer represented by the following general formula (1): CX 2 ═CY(—CZ 2 —O—Rf-A) (1) wherein X, Y, Z, Rf and A are as defined herein, with the proviso that at least one of X, Y, and Z contains a fluorine atom.
1. A method for producing a perfluoroelastomer, comprising carrying out polymerization of a perfluoromonomer in an aqueous medium in the presence of a polymer (1) to provide a perfluoroelastomer, the polymer (1) having a number average molecular weight of 0.3×10 4 or more and containing a polymerized unit (1) derived from a monomer represented by the following general formula (1):
CX 2 ═CY(—CZ 2 —O—Rf-A) (1)
wherein X is the same or different and is —H or —F; Y is —H, —F, an alkyl group, or a fluorine-containing alkyl group; Z is the same or different and is —H, —F, an alkyl group, or a fluoroalkyl group; Rf is a fluorine-containing alkylene group having 1 to 40 carbon atoms or a fluorine-containing alkylene group having 2 to 100 carbon atoms and having an ether bond; and A is —COOM, —SO 3 M, —OSO 3 M, or —C(CF 3 ) 2 OM, where M is —H, a metal atom, —NR 7 4 , imidazolium optionally having a substituent, pyridinium optionally having a substituent, or phosphonium optionally having a substituent and R 7 is —H or an organic group, with the proviso that at least one of X, Y, and Z contains a fluorine atom,
wherein a content of the polymerized unit (1) in the polymer (1) is 90 mol % or more based on all polymerized units.
2. The production method according to claim 1 , wherein at least one of X is —H.
3. The production method according to claim 1 , wherein the polymerized unit (1) is a polymerized unit (1A) derived from a monomer represented by the following general formula (1A):
CH 2 ═CF(—CF 2 —O—Rf-A) (1A)
wherein Rf and A are as described above.
4. The production method according to claim 1 , wherein A is —COOM.
5. The production method according to claim 1 , wherein the polymer (1) is added in an amount of 0.01 to 20% by mass based on 100% by mass of the aqueous medium.
6. The production method according to claim 1 , wherein the polymerization of the perfluoromonomer is carried out in the presence of a polymerization initiator and the polymerization initiator is added in an amount of 0.0001 to 10% by mass based on 100% by mass of the perfluoromonomer.
7. A method for producing a crosslinkable composition, comprising obtaining a perfluoroelastomer by the production method according to claim 1 , and thereafter mixing the perfluoroelastomer and at least one selected from the group consisting of an inorganic nitride, an organotin compound, an ammonia-generating compound, and a cross-linking agent, to provide a crosslinkable composition.
8. A method for producing a crosslinked product, comprising obtaining a crosslinkable composition by the production method according to claim 7 , and thereafter crosslinking the crosslinkable composition to provide a crosslinked product.
9. The production method according to claim 1 , wherein the polymerization of the perfluoromonomer is carried out substantially in the absence of a fluorine-containing surfactant except for a compound having a functional group capable of reacting by radical polymerization and a hydrophilic group.