Water-absorbing resin and manufacturing method for same
It is an object to provide a water-absorbing resin that while maintaining water-absorbing resin physical properties such as water absorption performance, has a sufficiently reduced odor produced during swelling. The object is attained by causing the water-absorbing resin to be a water-absorbing resin which is a surface-crosslinked water-absorbing resin, the water-absorbing resin having a volatile component concentration of 3.5 ppm or less as measured when the water-absorbing resin is caused to stand still for 15 minutes under a condition that the water-absorbing resin has a swelling capacity of 1.0-fold.
1. A water-absorbing resin which is a surface-crosslinked water-absorbing resin, said water-absorbing resin comprising a volatile component concentration of 3.5 ppm or less as measured when said water-absorbing resin is caused to stand still for 15 minutes under a condition that said water-absorbing resin has a swelling capacity of 1.0-fold,
where the volatile component concentration as measured when said water-absorbing resin is caused to stand still for 15 minutes under the condition that said water-absorbing resin has a swelling capacity of 1.0-fold is a numerical value obtained by adding together concentrations of all substances that are detected by a photoion detector (PID) of a 10.6 eV lamp and that are included in a volatile component which is present in a closed vessel when 10.0 g of a physiological saline at 23.5±0.5° C. is uniformly added, under room temperature and atmospheric pressure, to 10.0 g of said water-absorbing resin contained in a 2-liter closable glass vessel and said water-absorbing resin to which the physiological saline has been added is caused to stand still in a closed state for 15 minutes, the volatile component concentration being a value represented by a detection value in terms of isobutylene, which is a calibration gas.
2. The water-absorbing resin according to claim 1 , wherein a sum of volatile component concentrations as measured when said water-absorbing resin is caused to stand still for 15 minutes under conditions that said water-absorbing resin has respective swelling capacities of 0.0-fold, 0.5-fold, 1.0-fold, 2.5-fold, 5.0-fold, 10.0-fold, and 20.0-fold is 9.5 ppm or less.
3. The water-absorbing resin according to claim 1 , wherein a maximum value of volatile component concentrations measured every five seconds, under a condition that said water-absorbing resin has a swelling capacity of 5.0-fold, until 900 seconds have passed since initiation of swelling of said water-absorbing resin is 0.4 ppm or less.
4. The water-absorbing resin according to claim 1 , wherein a sum of volatile component concentrations measured every five seconds, under a condition that said water-absorbing resin has a swelling capacity of 5.0-fold, until 900 seconds have passed since initiation of swelling of said water-absorbing resin is 50.0 ppm or less.
5. The water-absorbing resin according to claim 1 , wherein said water-absorbing resin has an absorption capacity without load (CRC) of 23 g/g or more and an absorption capacity under load (AAP) of 15 g/g or more.
6. The water-absorbing resin according to claim 1 , wherein said water-absorbing resin has a mass average particle diameter (D50) of 300 μm to 600 μm, a proportion of particles having a particle diameter of less than 150 μm in said water-absorbing resin is 5 mass % or less, and said water-absorbing resin has a logarithmic standard deviation (σζ) of a particle size distribution of 0.20 to 0.50.
7. The water-absorbing resin according to claim 1 , wherein said water-absorbing resin contains a volatile component reducing agent.
8. The water-absorbing resin according to claim 1 , wherein said water-absorbing resin has a specific surface area of 25 m 2 /kg or more.
9. An absorbent article comprising a water-absorbing resin recited in claim 1 .
10. The absorbent article according to claim 9 , wherein said absorbent article includes an absorbent body, which is a composite containing said water-absorbing resin and a hydrophilic fiber, and said water-absorbing resin is contained in an amount of 60 mass % or more relative to a total mass of the absorbent body.
11. A method for producing a water-absorbing resin recited in claim 1 , successively comprising: a polymerization step of polymerizing an acrylic acid (salt)-based monomer-containing monomer composition so as to obtain a crosslinked hydrogel polymer; a drying step of drying the crosslinked hydrogel polymer that has been obtained in the polymerization step; and a surface-crosslinking step, said method further comprising, at or after an end of the polymerization step, the step of adding an amino group-containing reducing agent.
12. The method according to claim 11 , wherein said method includes, at or after an end of the surface-crosslinking step, the step of adding the amino group-containing reducing agent.
13. The method according to claim 11 , wherein said method includes the step of adding the amino group-containing reducing agent as an aqueous solution.
14. The method according to claim 11 , wherein the amino group-containing reducing agent contains a hydrazide group-containing compound.
15. A method for producing a water-absorbing resin, comprising the step of adding a water-based liquid in a droplet state to a surface-crosslinked water-absorbing resin so that the surface-crosslinked water-absorbing resin to which the water-based liquid has been added has a moisture content of 7.5 mass % or more, and then drying the surface-crosslinked water-absorbing resin, to which the water-based liquid has been added, so that the moisture content is reduced by an amount of 7.5 mass % or more within one hour.
16. A method recited in claim 15 , further comprising at least one of the following steps (A) and (B):
(A) adding a water-based liquid in a droplet state to the surface-crosslinked water-absorbing resin that has a specific surface area of 25 m 2 /kg or more; and
(B) successively including a polymerization step, a drying step of drying a hydrogel having been obtained in the polymerization step, and a surface-crosslinking step, and adding a volatile component reducing agent at or after an end of the polymerization step.
17. The method according to claim 16 , wherein said method includes the step (A) of adding a water-based liquid in a droplet state to the surface-crosslinked water-absorbing resin that has a specific surface area of 25 m 2 /kg or more, and in a case where the water-based liquid is added so that the surface-crosslinked water-absorbing resin to which the water-based liquid has been added has a moisture content of 27.5 mass % or more, the surface-crosslinked water-absorbing resin, to which the water-based liquid has been added, is dried so that the surface-crosslinked water-absorbing resin has a moisture content of 20 mass % or less within one hour.
18. The method according to claim 16 , wherein said method includes the step (B) of successively including a polymerization step, a drying step of drying a hydrogel having been obtained in the polymerization step, and a surface-crosslinking step, and adding a volatile component reducing agent at or after an end of the polymerization step.
19. A method for producing a water-absorbing resin, comprising the step of bringing the water-absorbing resin into contact with a supercritical solvent so as to remove a volatile component from the water-absorbing resin,
the water-absorbing resin containing a polyacrylic acid (salt)-based resin as a main component,
the water-absorbing resin being internally crosslinked, and
the water-absorbing resin being surface-crosslinked.