Thermally disproportionated anode active material including turbostratic carbon coating
An electrode material for a lithium ion secondary battery and method of forming the same, the electrode material including composite particles, each composite particle including a primary particle including thermally disproportionated silicon oxide, and an envelope disposed on the surface of the primary particle. The envelope includes turbostratic carbon having a Raman spectrum having: a D band having a peak intensity (I D ) at wave number between 1330 cm −1 and 1360 cm −1 ; a G band having a peak intensity (I G ) at wave number between 1530 cm −1 and 1600 cm −1 ; and a 2D band having a peak intensity (I 2D ) at wave number between 2650 cm −1 and 2750 cm −1 , wherein a ratio of I D /I G ranges from greater than zero to about 1.0, and a ratio of I 2D /I G ranges from about 0.4 to about 2.
1 . A method of forming an anode material, the method comprising:
thermally disproportionating SiO x particles, wherein x ranges from about 0.9 to about 1.1, to form primary particles comprising crystalline Si domains disposed in a matrix comprising SiO 2 ;
forming a mixture comprising the primary particles and carbon; and
processing the mixture to form composite particles, each composite particle comprising:
one of the primary particles; and
an envelope disposed on the primary particle and comprising at least 90 wt % turbostratic graphene having a Raman spectrum having:
a D band having a peak intensity (I D ) at wave number between 1330 cm −1 and 1360 cm −1 ;
a G band having a peak intensity (I G ); and
a 2D band having a peak intensity (I 2D ) at wave number between 2650 cm −1 and 2750 cm −1 ,
wherein:
a ratio of I D /I G ranges from greater than zero to about 0.9; and
a ratio of I 2D /I G ranges from about 0.5 to about 2.
2 . The method of claim 1 , wherein:
the thermally disproportionating comprises heating the SiO x particles at a temperature ranging from about 1050° C. to about 1150° C., in an inert atmosphere; and
the processing the mixture comprises spray-drying the mixture.
3 . The method of claim 1 , further comprising carbonizing the composite particles.
4 . The method of claim 1 , further comprising adding a metal dopant or dopant precursor to the primary particles, either before or after the thermal disproportionation of the SiO x particles.
5 . A method of forming an anode material, the method comprising:
forming a mixture comprising SiO x particles, wherein x ranges from about 0.7 to about 1.1, and carbon;
processing the mixture form a powder; and
thermally disproportionating the powder to form composite particles, each of the composite particles comprising:
a primary particle comprising crystalline Si domains disposed in a matrix comprising SiO 2 ; and
an envelope disposed on the primary particle and comprising at least 90 wt % turbostratic graphene having a Raman spectrum having:
a D band having a peak intensity (I D ) at wave number between 1330 cm −1 and 1360 cm −1 ;
a G band having a peak intensity (I G ); and
a 2D band having a peak intensity (I 2D ) at wave number between 2650 cm −1 and 2750 cm −1 ,
wherein:
a ratio of I D /I G ranges from greater than zero to about 0.9; and
a ratio of I 2D /I G ranges from about 0.5 to about 2.
6 . The method of claim 5 , further comprising carbonizing the composite particles.
7 . The method of claim 5 , wherein:
the thermally disproportionating comprises heating the composite particles at a temperature ranging from about 1050° C. to about 1150° C., in an inert atmosphere; and
the processing the mixture comprises spray-drying the mixture.
8 . The method of claim 5 , further comprising adding a metal dopant or dopant precursor to the primary particles, either before or after the thermal disproportionation of the composite particles.