Method of forming tungsten film

1. A method of forming a tungsten film on a surface of an object to be processed in a vessel capable of being vacuumized, the method comprising:

forming a tungsten film by alternately repeating a reduction gas supplying process for supplying a reduction gas to the vessel and a tungsten gas supplying process for supplying a tungsten-containing gas to the vessel with an intervening purge process therebetween for supplying an inert gas to the vessel while exhausting the vessel,

wherein the tungsten film is formed by alternately repeating the reduction gas supplying process for supplying the reduction gas to the vessel and the tungsten gas supplying process for supplying the tungsten-containing gas to the vessel while controlling the total pressure of the gases to be constant in the vessel throughout the step of forming the tungsten film, and

wherein a reduction gas-supplying period of an initial reduction gas supplying process among the repeated reduction gas supplying processes for supplying a reduction gas to the vessel is set to be longer than that of the remaining reduction gas supplying processes for supplying a reduction gas to the vessel.

2. The method of claim 1 , wherein a parameter, which is obtained by multiplying a partial pressure of the reduction gas by the supplying period thereof in the initial reduction gas supplying process among the repeated reduction gas supplying processes, is set to be greater than that in the remaining reduction gas supplying processes.

3. The method of claim 1 , wherein the tungsten-containing gas is WF 6 gas or an orgarnc tungsten source gas.

4. The method of claim 1 , wherein the reduction gas is selected from the group consisting of H 2 gas, silane (SiH 4 ), disilane (Si 2 H 6 ), dichlororosilane (SiH 2 Cl 2 ), diborane (B 2 H 6 ) and phospine (PH 3 ).

5. A method of forming a tungsten film on a surface of an object to be processed in a vacuum vessel, the method comprising the steps of:

forming an initial tungsten film by alternately repeating a reduction gas supplying process for supplying a reduction gas to the vessel and a tungsten gas supplying process for supplying a tungsten-containing gas to the vessel with an intervening purge process therebetween for supplying an inert gas to the vessel while exhausting the vessel; and,

forming a main tungsten film on the initial tungsten film by simultaneously supplying the tungsten-containing gas and the reduction gas to the vessel after the initial tungsten film is formed,

wherein during the step of forming the initial tungsten film, the initial tungsten film is formed by alternately repeating the reduction gas supplying process for supplying the reduction gas to the vessel and the tungsten gas supplying process for supplying the tungsten-containing gas to the vessel while controlling the total pressure of the gases to be constant throughout the step of forming the initial tungsten film, and

wherein during the step of forming the initial tungsten film, a reduction gas supplying period of an initial reduction gas supplying process among the repeated reduction gas supplying processes for supplying a reduction gas to the vessel is set to be longer than that of the remaining reduction gas supplying processes for supplying a reduction gas to the vessel.

6. The method of claim 5 , wherein during the step of forming the initial tungsten film, a parameter, which is obtained by multiplying a partial pressure of the reduction gas by the supplying period thereof in an initial reduction gas supplying process among the repeated reduction gas supplying processes is set to be greater than that in the remaining reduction gas supplying processes.

7. The method of claim 5 , wherein the tungsten-containing gas is WF 6 gas or an organic tungsten source gas.

8. The method of claim 5 , wherein the reduction gas is selected from the group consisting of H 2 gas, silane (SiH 4 ), disilane (Si 2 H 6 ), dichlororosilane (SiH 2 Cl 2 ), diborane (B 2 H 6 ) and phospine (PH 3 ).

9. A method of forming a tungsten film on a surface of an object to be processed in a vacuum vessel, the method comprising the steps of:

forming an initial tungsten film by alternately repeating a reduction gas supplying process for supplying a reduction gas to the vessel and a tungsten gas supplying process for supplying a tungsten-containing gas to the vessel with an intervening purge process therebetween for supplying an inert gas to the vessel while exhausting the vessel;

forming a passivation tungsten film on the initial tungsten film by supplying the tungsten-containing gas and the reduction gas to the vessel; and

forming a main tungsten film on the passivation tungsten film by simultaneously supplying the tungsten-containing gas and the reduction gas to the vessel,

wherein the passivation tungsten film is formed by simultaneously supplying the tungsten-containing gas and the reduction gas to the vessel while controlling a flow ratio of the tungsten-containing gas to be smaller than that in the main tungsten film forming step, and wherein during the step of forming the initial tungsten film, the initial tungsten film is formed by alternately repeating the reduction gas supplying process for supplying the reduction gas to the vessel and the tungsten gas supplying process for supplying the tungsten-containing gas to the vessel while controlling the total pressure of the gases to be constant throughout the step of forming the initial tungsten film, and

wherein during the step of forming the initial tungsten film, a reduction gas supplying period of an initial reduction gas supplying process among the repeated reduction gas supplying processes for supplying a reduction gas to the vessel is set to be longer than that of the remaining reduction gas supplying processes for supplying a reduction gas to the vessel.

10. The method of claim 9 , wherein during the step of forming the initial tungsten film, a parameter, which is obtained by multiplying a partial pressure of the reduction gas by the supplying period thereof, in the initial reduction gas supplying process among the repeated reduction gas supplying processes is set to be greater than that in the remaining reduction gas supplying processes.

11. The method of claim 9 , wherein the initial tungsten film forming step and the passivation tungsten film forming step have at least either a process pressure or a process temperature substantially equal.

12. The method of claim 9 , wherein the main tungsten film forming step has at least either a process pressure or a process temperature substantially higher than the passivation tungsten film forming step.

13. The method of claim 9 , wherein the tungsten-containing gas is WF 6 gas or an organic tungsten source gas.

14. The method of claim 9 , wherein the reduction gas is selected from the group consisting of H 2 gas, silane (SiH 4 ), disilane (Si 2 H 6 ), dichlororosilane (SiH 2 Cl 2 ), diborane (B 2 H 6 ) and phospine (PH 3 ).

15. The method of claim 9 , wherein, in the initial tungsten film forming step, the tungsten-containing gas is WF 6 gas, and the reduction gas includes SiH 4 gas, and

wherein, in the passivation tungsten film forming step, the tungsten-containing gas is WF 6 gas and the reduction gas includes H 2 gas.

16. A method of forming a tungsten film on a surface of an object to be processed in a vacuum vessel, the method comprising the steps of:

forming a tungsten film by alternately repeating a reduction gas supplying process for supplying a reduction gas to the vessel and a tungsten gas supplying process for supplying a tungsten-containing gas to the vessel with an intervening purge process therebetween for supplying an inert gas to the vessel while exhausting the vessel; and

wherein forming the tungsten film is completed by performing the reduction gas supplying process, and

wherein during the step of forming the tungsten film, the tungsten film is formed by alternately repeating the reduction gas supplying process for supplying a reduction gas to the vessel and the tungsten gas supplying process for supplying a tungsten containing gas to the vessel while controlling the total pressure of the gases to be constant throughout the step of forming the tungsten film, and

wherein during the step of forming the tungsten film, a reduction gas supplying period of a reduction gas supplying process among the repeated reduction gas supplying processes for supplying a reduction gas to the vessel is set to be longer than that of the remaining reduction gas supplying processes for supplying a reduction gas to the vessel.

17. The method of claim 16 , wherein during the step of forming the tungsten film, a parameter, which is obtained by multiplying a partial pressure of the reduction gas by the supplying period thereof in a reduction gas supplying process among the repeated reduction gas supplying processes is set to be greater than that in the remaining reduction gas supplying processes.

18. The method of claim 16 , wherein the tungsten-containing gas is WF 6 gas or an organic tungsten source gas.

19. The method of claim 16 , wherein the reduction gas is selected from the group consisting of H 2 gas, silane (SiH 4 ), disilane (Si 2 H 6 ), dichlororosilane (SiH 2 Cl 2 ), diborane (B 2 H 6 ) and phospine (PH 3 ).

20. The method of claim 1 , wherein a TiN film is formed on the surface of the object, and

wherein the tungsten film is formed on the TiN film.

21. The method of claim 5 , wherein a TiN film is formed on the surface of the object, and

wherein the initial tungsten film is formed on the TiN film.

22. The method of claim 9 , wherein a TiN film is formed on the surface of the object, and

wherein the initial tungsten film is formed on the TiN film.

23. The method of claim 2 , wherein the parameter is about 10 to 300 Torr·sec.

24. The method of claim 6 , wherein the parameter is about 10 to 300 Torr·sec.

25. The method of claim 10 , wherein the parameter is about 10 to 300 Torr·sec.

26. The method of claim 1 , wherein the method is performed in a temperature ranging from about 200 to 500° C.

27. The method of claim 5 , wherein the method is performed in a temperature ranging from about 200 to 500° C.

28. The method of claim 9 , wherein the method is performed in a temperature ranging from about 200 to 500° C.

29. The method of claim 5 , wherein the initial tungsten film is formed by supplying WF 6 gas as the tungsten-containing gas and SiH 4 gas as the reduction gas, and

wherein the main tungsten film is formed on the initial tungsten film by supplying WF 6 gas as the tungsten-containing gas and H 2 gas as the reduction gas.

30. The method of claim 1 , wherein, in the tungsten film forming step, the tungsten-containing gas is WF 6 gas and the reduction gas includes SiH 4 gas.

31. The method of claim 16 , wherein, in the tungsten film forming step, the tungsten-containing gas is WF 6 gas and the reduction gas includes SiH 4 gas.

32. The method of claim 16 , wherein a TiN film is formed on the surface of the object, and

wherein the tungsten film is formed on the TiN film.