Selective plasma processing method
A selective plasma processing method, within a processing chamber of a plasma processing apparatus, acts oxygen-containing plasma on a target object having silicon and a silicon nitride layer to selectively oxidize the silicon with respect to the silicon nitride layer and to form a silicon oxide film. Further, the ratio of a thickness of a silicon oxynitride film formed within the silicon nitride layer to a thickness of the silicon oxide film formed by the oxidization is equal to or smaller than 20%.
1. A selective plasma processing method for, within a processing chamber of a plasma processing apparatus, acting oxygen-containing plasma on a target object having a silicon and a silicon nitride layer to selectively oxidize the silicon with respect to the silicon nitride layer and to form a silicon oxide film,
wherein the ratio of a thickness of a silicon oxynitride film formed on the silicon nitride layer to a thickness of the silicon oxide film formed by the oxidization is equal to or smaller than 20%.
2. The selective plasma processing method of claim 1 , wherein the oxygen-containing plasma comprises microwave-excited high density plasma generated by introducing microwaves into the processing chamber through a planar antenna having a plurality of slots.
3. The selective plasma processing method of claim 1 , wherein a processing pressure is 400 Pa or higher.
4. The selective plasma processing method of claim 3 , wherein the processing pressure ranges from 400 Pa to 1333 Pa.
5. A selective plasma processing method for, within a processing chamber of a plasma processing apparatus, acting oxygen-containing plasma on a target object having a silicon exposing surface and a silicon nitride exposing surface to preferentially oxidize silicon on the silicon exposing surface in such a way that the ratio of a thickness of a silicon oxynitride film formed on the silicon nitride exposing surface to a thickness of a silicon oxide film formed on the silicon exposing surface becomes equal to or smaller than 20%.
6. A selective plasma processing method for, within a processing chamber of a plasma processing apparatus, acting nitrogen-containing plasma on a target object having a silicon and a silicon oxide layer thereon to selectively nitriding the silicon with respect to the silicon oxide layer and to form a silicon nitride film,
wherein the ratio of a thickness of a silicon oxynitride film formed on the silicon oxide layer to a thickness of the silicon nitride film formed by the nitriding is equal to or smaller than 25%.
7. The selective plasma processing method of claim 6 , wherein the nitrogen-containing plasma comprises microwave excited high density plasma generated by introducing microwaves into the processing chamber through a planar antenna having a plurality of slots.
8. The selective plasma processing method of claim 6 , wherein a processing pressure is 400 Pa or higher.
9. The selective plasma processing method of claim 8 , wherein the processing pressure ranges from 400 Pa to 1333 Pa.
10. A selective plasma processing method for, within a processing chamber of a plasma processing apparatus, acting nitrogen-containing plasma on a target object having a silicon exposing surface and a silicon oxide exposing surface to preferentially nitride silicon on the silicon exposing surface in such a way that the ratio of a thickness of a silicon oxynitride film formed on the silicon oxide exposing surface to a thickness of a silicon nitride film formed on the silicon exposing surface becomes equal to or smaller than 25%.
11. A plasma processing apparatus comprising:
a vacuum-evacuated processing chamber including a table for supporting a target object; and
a control part adapted to control the plasma processing apparatus to have the apparatus to perform a selective plasma processing method for, within the processing chamber, acting oxygen-containing plasma on the target object having a silicon exposing surface and a silicon nitride exposing surface to preferentially oxidize silicon on the silicon exposing surface in such a way that the ratio of a thickness of a silicon oxynitride film formed on the silicon nitride exposing surface to a thickness of a silicon oxide film formed on the silicon exposing surface becomes equal to or smaller than 20%.
12. A plasma processing apparatus comprising:
a vacuum evacuable processing chamber including a mounting table for mounting a target object; and
a controller adapted to control the plasma processing apparatus to have the apparatus to perform a selective plasma processing method for, within the processing chamber, acting nitrogen-containing plasma on the target object having a silicon exposing surface and a silicon oxide exposing surface to preferentially nitride silicon on the silicon exposing surface in such a way that the ratio of a thickness of a silicon oxynitride film formed on the silicon oxide exposing surface to a thickness of a silicon nitride film formed on the silicon exposing surface becomes equal to or smaller than 25%.