Deposition of conformal films by atomic layer deposition and atomic layer etch
Methods for depositing conformal films using a halogen-containing etchant during atomic layer deposition are provided. Methods involve exposing a substrate to a halogen-containing etchant such as nitrogen trifluoride between exposing the substrate to a first precursor and exposing the substrate to a second plasma-activated reactant. Examples of conformal films that may be deposited include silicon-containing films and metal-containing films. Related apparatuses are also provided.
1. A method of processing substrates in a chamber, the method comprising:
(a) providing a substrate having one or more features, each feature comprising a feature opening;
(b) exposing the substrate to a silicon-containing precursor under conditions allowing the silicon-containing precursor to adsorb onto the surface of the substrate, thereby forming an adsorbed layer of the silicon-containing precursor;
(c) after exposing the substrate to the silicon-containing precursor, exposing the substrate to a halogen-containing etchant; and
(d) exposing the substrate to a nitrogen-containing reactant and igniting a plasma to selectively etch the adsorbed layer of the silicon-containing precursor at or near the feature openings and form a silicon nitride film.
2. The method of claim 1 , wherein the substrate is exposed to the halogen-containing etchant under conditions allowing the halogen-containing etchant to selectively adsorb onto the adsorbed layer of the silicon-containing precursor.
3. The method of claim 1 , wherein the halogen-containing etchant is selected from the group consisting of nitrogen trifluoride, chlorine, fluoroform, carbon tetrafluoride, and combinations thereof.
4. The method of claim 1 , wherein the halogen-containing etchant comprises a compound with a chemical formula of C n F 2n+2 or C n F 2n , where n>1.
5. The method of claim 1 , wherein the chamber is purged after exposing the substrate to the halogen-containing etchant.
6. The method of claim 5 , wherein the chamber is purged by flowing a purge gas selected from the group consisting of argon, helium, nitrogen, and hydrogen.
7. The method of claim 1 , wherein the silicon-containing precursor is selected from the group consisting of silane, disilane, trisilane, tetrasilane, trisilylamine, aminosilanes, and halosilanes.
8. The method of claim 1 , wherein the nitrogen-containing reactant is selected from the group consisting of nitrogen, ammonia, hydrazine, and amines.
9. The method of claim 1 , further comprising repeating (a)-(d).
10. The method of claim 1 , wherein (a)-(d) are performed in the same chamber.
11. A method of processing substrates in a chamber, the method comprising:
depositing a film by performing one or more cycles, a cycle comprising:
(a) providing a substrate having one or more features, each feature comprising a feature opening;
(b) exposing the substrate to a first precursor under conditions allowing the first precursor to adsorb onto the surface of the substrate, thereby forming an adsorbed layer of the first precursor;
(c) after exposing the substrate to the first precursor, exposing the substrate to a halogen-containing etchant; and
(d) exposing the substrate to a second reactant and igniting a plasma to selectively etch the adsorbed layer of the first precursor at or near the feature openings and form a film.
12. The method of claim 11 , wherein the halogen-containing etchant is selected from the group consisting of nitrogen trifluoride, chlorine, fluoroform, carbon tetrafluoride, and combinations thereof.
13. The method of claim 11 , wherein the chamber is purged before (d).
14. The method of claim 11 , wherein the film is a dielectric or metal film.
15. The method of claim 11 , wherein the film is selected from the group consisting of silicon nitride, silicon carbide, and silicon oxide.
16. The method of claim 11 , wherein the second reactant is an oxidant or reductant.
17. The method of claim 11 , wherein (d) is performed every n cycles, where n is an integer equal to or greater than 1.