Semiconductor device having merged epitaxial features with Arc-like bottom surface and method of making the same
A semiconductor device and method of forming the same is disclosed. The semiconductor device includes a substrate, two semiconductor fins over the substrate, and a semiconductor feature over the two semiconductor fins. The semiconductor feature comprises two lower portions and one upper portion. The two lower portions are directly over the two semiconductor fins respectively. The upper portion is over the two lower portions. A bottom surface of the upper portion has an arc-like cross-sectional shape.
1. A method, comprising:
providing a device comprising a substrate and two fins extending from the substrate; etching the two fins, thereby forming two trenches;
epitaxially growing first semiconductor features in the two trenches;
epitaxially growing second semiconductor features over the first semiconductor features in a first growth condition, wherein the second semiconductor features laterally merge to form a merged portion; and
after a dimension of the merged portion reaches a target dimension, epitaxially growing the second semiconductor features in a second growth condition, wherein a growth rate ratio between crystal directions [100] and [111] of the second semiconductor features is greater in the second growth condition than in the first growth condition.
2. The method of claim 1 , wherein the second growth condition includes growing the second semiconductor features at a temperature ranging from 650 to 720 degrees Celsius.
3. The method of claim 1 , further comprising:
performing an etching process to reduce a width of the second semiconductor features after the epitaxially growing of the second semiconductor features in the second growth condition.
4. The method of claim 3 , wherein the second semiconductor features comprise silicon, the first growth condition uses a precursor having dichlorosilane (SiH 2 Cl 2 ), and the second growth condition adds a silane to the precursor.
5. The method of claim 4 , wherein the etching process uses an etchant comprising germane (GeH 4 ) and hydrogen chloride (HCl).
6. The method of claim 1 , further comprising:
forming an inter-layer dielectric layer (ILD) over the second semiconductor features;
etching contact holes through the ILD to expose portions of the second semiconductor features; and
forming conductive features over the exposed portions of the second semiconductor features in the contact holes.
7. A method, comprising:
providing a device having a substrate and at least two fins extending from the substrate; etching the at least two fins, thereby forming at least two trenches;
epitaxially growing first semiconductor features in the at least two trenches;
epitaxially growing second semiconductor features over the first semiconductor features in a first growth condition, wherein the second semiconductor features laterally merge, thereby forming a merged portion;
after a thickness of the merged portion reaches a target dimension, epitaxially growing the second semiconductor features in a second growth condition different from the first growth condition, thereby forming an arc-like shape in a bottom surface of the merged portion where the arc-like shape has an apex in a middle portion of the arc-like shape and bends downwards on both sides of the middle portion; and
performing an etching process to reduce a width of the second semiconductor features.
8. The method of claim 7 , wherein the second semiconductor features comprise silicon, the first growth condition uses a precursor having dichlorosilane (SiH 2 Cl 2 ), the second growth condition uses the precursor and silane (SiH 4 ), and the etching process uses an etchant comprising germane (GeH 4 ) and hydrogen chloride (HCl).
9. The method of claim 8 , wherein a ratio of GeH 4 to HCl in the etchant ranges from 0.5 to 1.2.
10. The method of claim 7 , further comprising:
forming a conductive feature partially embedded in the second semiconductor features.
11. A method, comprising:
providing a structure comprising a substrate and two fins over the substrate;
etching the two fins to produce two trenches, each trench having a bottom opening wider than a top opening;
epitaxially growing first semiconductor features in the two trenches;
epitaxially growing second semiconductor features over the first semiconductor features in a first growth condition, wherein the second semiconductor features laterally merge to form a merged portion; and
after a dimension of the merged portion reaches a target dimension, epitaxially growing the second semiconductor features in a second growth condition different from the first growth condition.
12. The method of claim 11 , wherein a growth rate ratio between crystal directions [100] and [111] of the second semiconductor features is greater in the second growth condition than in the first growth condition.
13. The method of claim 11 , further comprising:
performing an etching process to reduce a width of the second semiconductor features after the epitaxially growing of the second semiconductor features in the second growth condition.
14. The method of claim 13 , wherein the etching process uses an etchant comprising germane (GeH 4 ) and hydrogen chloride (HCl).
15. The method of claim 14 , wherein a ratio of GeH 4 to HCl in the etchant ranges from about 0.5 to about 1.2.
16. The method of claim 11 , wherein a lower portion of the second semiconductor features is surrounded by the first semiconductor features.
17. The method of claim 11 , wherein the second semiconductor features comprise silicon, the first growth condition uses a precursor having dichlorosilane (SiH 2 Cl 2 ), and the second growth condition adds a silane to the precursor.
18. The method of claim 7 , wherein a growth rate ratio between crystal directions [100] and [111] of the second semiconductor features is greater in the second growth condition than in the first growth condition.
19. The method of claim 7 , wherein the epitaxially growing of the first semiconductor features includes partially filling the at least two trenches with the first semiconductor features.
20. The method of claim 19 , wherein a lower portion of the second semiconductor features is surrounded by the first semiconductor features.