Tunable shape memory capacitor and a method of preparation thereof

Inventors: Faten Ebrahim S. Al-Hazmi (Jeddah, SA); Fahrettin Yakuphanoglu (Elazig, TR); Ahmed A. Al-Ghamdi (Jeddah, SA); Yusuf Al-Turki (Jeddah, SA)
Assignee: King Abdulaziz University
H01G7/04H01G4/206H01G7/021H01G7/028H01L41/193
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 10,181,381
App. No.
15/240,655
Granted
Jan 15, 2019
Kind
B2
Abstract

A variable capacitor device that includes a dielectric layer comprising a shape-memory polymer, a first metal plate and a second metal plate, wherein the dielectric layer is sandwiched between the first and the second metal plates. The shape-memory polymer has a first thickness at a first temperature under a first external compressive load, a second thickness at a second temperature under a second external compressive load, wherein the first thickness is greater than the second thickness, the second temperature is greater than the first temperature, and the second external compressive load is greater than the first external compressive load. The shape memory polymer having the second thickness is configured to convert to the shape-memory polymer having the first thickness when sequentially subjected to the first external compressive load and the second temperature.

Claims (24)

1. A variable capacitor device, comprising:

a dielectric layer comprising a shape-memory polymer;

a first metal plate and a second metal plate, wherein the dielectric layer is sandwiched between the first and the second metal plates;

wherein the shape-memory polymer has a first thickness at a first temperature under a first external compressive load, a second thickness at a second temperature under a second external compressive load, and the shape memory polymer having the second thickness is configured to convert to the shape-memory polymer having the first thickness when sequentially subjected to the first external compressive load and the second temperature, and

wherein the first thickness is greater than the second thickness, the second temperature is greater than the first temperature, and the second external compressive load is greater than the first external compressive load.

2. The variable capacitor device of claim 1 , which has a first capacitance at the first thickness and the first temperature, and a second capacitance at the second thickness and the second temperature, wherein a ratio of the second capacitance to the first capacitance is in the range of 2.5:1 to 1.5:1.

3. The variable capacitor device of claim 1 , wherein the dielectric layer has a thickness in the range of 0.1-2 mm.

4. The variable capacitor device of claim 1 , wherein the shape memory polymer has a glass transition temperature in the range 50-100° C.

5. The variable capacitor device of claim 1 , wherein the shape-memory polymer is at least one selected from the group consisting of polyvinyl alcohol, polyurethane, polyvinylidene difluoride, polylactic acid, polycaprolactone, polyethylene, polyethylene glycol, polyether ether ketone, polyethyl methacrylate, polystyrene, polytetramethylene glycol, polyisoprene, polybutadiene, poly(styrene-butadiene), polynorbornene, poly(norbornene-cyclooctene), poly(tert-butyl acrylate-butyl acrylate), poly(ethyleneterephthalate)-block-poly(ethyleneoxide), polystyrene-block-poly(1,4-butadiene), poly(2-methyl-2-oxazoline)-block-poly(tetrahydrofuran)-block-poly(2-methyl-2-oxazoline), and epoxy.

6. The variable capacitor device of claim 1 , wherein the dielectric layer further comprises at least one dopant selected from the group consisting of hydroxyapatite, polyhedral oligomeric silsesquioxane, titanium oxide nanoparticles, tin oxide nanoparticles, zinc oxide nanoparticles, zinc sulfide nanoparticles, cadmium oxide nanoparticles, graphene sheets, quantum dots, carbon nanotubes, and fullerenes.

7. The variable capacitor device of claim 6 , wherein a volume fraction of said dopant is in the range of 0.005-0.1, with the volume fraction being relative to the total volume of the dielectric layer.

8. The variable capacitor device of claim 6 , wherein a morphology of said dopant is at least one selected from the group consisting of a nanosphere, a nanosheet, a nanotube, a nanofiber, a nanowire, a nanodisk, a nanocube, a nanorod, a nanoring, and a nanostar.

9. The variable capacitor device of claim 6 , wherein said dopant has an average particle size in the range of 1-100 nm.

10. The variable capacitor device of claim 1 , wherein the shape memory polymer is a polyvinyl alcohol polymer which is crosslinked with a crosslinking agent having at least two aldehyde groups or at least two carboxyl groups.

11. The variable capacitor device of claim 10 , wherein the crosslinking agent is glutaraldehyde.

12. The variable capacitor device of claim 1 , wherein each of the first and the second metal plates comprises one metal selected from the group consisting of gold, platinum, silver, copper, aluminum, and titanium.

13. A variable capacitor device, comprising:

a dielectric layer comprising a triple shape-memory polymer;

a first metal plate and a second metal plate, wherein the dielectric layer is sandwiched between the first and the second metal plates;

wherein the triple shape-memory polymer has a first thickness at a first temperature under a first external compressive load, a second thickness at a second temperature under the first external compressive load, a third thickness at a third temperature under a second external compressive load, and the triple shape memory polymer having the third thickness is configured to convert to the triple shape-memory polymer having the second thickness when sequentially subjected to the first external compressive load and the second temperature, and the triple shape memory polymer having the second thickness is configured to convert to the triple shape-memory polymer having the first thickness when sequentially subjected to the first external compressive load and the third temperature, and

wherein the first thickness is greater than the second thickness and the second thickness is greater than the third thickness, the third temperature is greater than the second temperature and the second temperature is greater than the first temperature, and the second external compressive load is greater than the first external compressive load.

14. The variable capacitor device of claim 13 , which has a first capacitance at the first thickness and the first temperature, a second capacitance at the second thickness and the second temperature, and a third capacitance at the third thickness and the third temperature, wherein a ratio of the third capacitance to the second capacitance is in the range of 2.5:1 to 1.5:1, and a ratio of the second capacitance to the first capacitance is in the range of 2.5:1 to 1.5:1.

15. The variable capacitor device of claim 13 , wherein the triple shape-memory polymer is a combination of two shape-memory polymers each is selected from the group consisting of polyvinyl alcohol, polyurethane, polyvinylidene difluoride, polylactic acid, polycaprolactone, polyethylene, polyethylene glycol, polyether ether ketone, polyethyl methacrylate, polystyrene, polytetramethylene glycol, polyisoprene, polybutadiene, poly(styrene-butadiene), polynorbornene, poly(norbornene-cyclooctene), poly(tert-butyl acrylate-butyl acrylate), poly(ethyleneterephthalate)-block-poly(ethyleneoxide), polystyrene-block-poly(1,4-butadiene), poly(2-methyl-2-oxazoline)-block-poly(tetrahydrofuran)-block-poly(2-methyl-2-oxazoline), and epoxy.

16. The variable capacitor device of claim 13 , wherein the triple shape-memory polymer is an interpenetrating polymer network of two crosslinked polymers having a glass transition temperature difference within the range of 50-200° C.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Aug 18, 2016
From: AL-HAZMI, FATEN EBRAHIM S.; YAKUPHANOGLU, FAHRETTIN; AL-GHAMDI, AHMED A.; AL-TURKI, YUSUF
To: KING ABDULAZIZ UNIVERSITY