Negative electrode including a polymeric single-ion conductor coating
A negative electrode includes a metal substrate and a polymeric single-ion conductor coating formed on a surface of the metal substrate. The metal substrate is selected from the group consisting of lithium, sodium, and zinc. The polymeric single-ion conductor coating is formed of i) a metal salt of a sulfonated tetrafluoroethylene-based fluoropolymer copolymer or ii) a polymeric metal salt having an initial polymeric backbone and pendent metal salt groups attached to the initial polymeric backbone.
1. A negative electrode, consisting essentially of:
a metal substrate selected from the group consisting of lithium, sodium, and zinc; and
a polymeric single-ion conductor coating formed on a surface of the metal substrate, the polymeric single-ion conductor coating formed of a polymeric metal salt having a polymeric backbone and pendent metal salt groups attached to the polymeric backbone,
wherein the polymeric backbone is selected from the group consisting of polyolefin, polyvinylidene fluoride, polyethylene oxide, polyimide, and co-polymers thereof, and the pendent metal salt groups are attached directly to one of the polyolefin, polyvinylidene fluoride, polyethylene oxide, and polyimide, and
wherein the polymeric single-ion conductor coating has a comb-like structure where the polymeric backbone extends across the surface and the pendent metal salt groups are attached to the polymeric backbone so as to extend outward and away from the surface at a predetermined position.
2. The negative electrode as defined in claim 1 wherein the polymeric backbone is cross-linked.
3. The negative electrode as defined in claim 1 wherein the polymeric backbone is not cross-linked.
4. The negative electrode as defined in claim 1 wherein the pendent metal salt is one of:
a lithium salt selected from the group consisting of lithium bis(trifluoromethane)sulfonimide, lithium malonatodifluoroborate, lithium sulfonate, lithium triflate, analogs thereof, and combinations thereof; or
a sodium salt selected from the group consisting of sodium trifluoromethanesulfonate, NaClO 4 , NaPF 6 , NaBF 4 , NaTFSI (sodium(I) Bis(trifluoromethanesulfonyl)imide), NaFSI (sodium(I) Bis(fluorosulfonyl)imide), analogs thereof, and combinations thereof; or
a zinc salt selected from the group consisting of zinc trifluoromethanesulfonate, Zn(ClO 4 ) 2 , Zn(PF 6 ) 2 , Zn(BF 4 ) 2 , Zn(TFSI) 2 (zinc(II) Bis(trifluoromethanesulfonyl)imide), Zn(FSI) 2 (zinc(II) Bis(fluorosulfonyl)imide), analogs thereof, and combinations thereof.
5. The negative electrode as defined in claim 1 wherein the metal substrate is selected from the group consisting of lithium foil, sodium foil, and zinc foil.
6. The negative electrode as defined in claim 1 wherein the pendent metal salt groups are substantially evenly distributed along the surface of the metal substrate.
7. The negative electrode as defined in claim 1 wherein the pendent metal salt is one of: lithium malonatodifluoroborate, NaClO 4 , NaPF 6 , NaBF 4 , NaFSI (sodium(I) bis(fluorosulfonyl)imide), zinc trifluoromethanesulfonate, Zn(ClO 4 ) 2 , Zn(PF 6 ) 2 , Zn(BF 4 ) 2 , Zn(FSI) 2 (zinc(II) bis(fluorosulfonyl)imide), and combinations thereof.
8. An electrochemical cell, comprising:
a positive electrode; and
a negative electrode consisting essentially of:
a metal substrate selected from the group consisting of lithium, sodium, and zinc; and
a polymeric single-ion conductor coating formed on a surface of the metal substrate, the polymeric single-ion conductor coating formed of a polymeric metal salt having a polymeric backbone and pendent metal salt groups attached to the polymeric backbone;
wherein the polymeric single-ion conductor coating faces the positive electrode and the polymeric backbone is selected from the group consisting of polyolefin, polyvinylidene fluoride, polyethylene oxide, polyimide, and co-polymers thereof, and the pendent metal salt groups are attached directly to one of the polyolefin, polyvinylidene fluoride, polyethylene oxide, and polyimide, and
wherein the polymeric single-ion conductor coating has a comb-like structure where the polymeric backbone extends across the surface and the pendent metal salt groups are attached to the polymeric backbone so as to extend outward and away from the surface at a predetermined position.
9. The electrochemical cell as defined in claim 8 wherein the pendent metal salt is one of:
a lithium salt selected from the group consisting of lithium bis(trifluoromethane)sulfonimide, lithium malonatodifluoroborate, lithium sulfonate, lithium triflate, analogs thereof, and combinations thereof; or
a sodium salt selected from the group consisting of sodium trifluoromethanesulfonate, NaClO 4 , NaPF 6 , NaBF 4 , NaTFSI (sodium(I) Bis(trifluoromethanesulfonyl)imide), NaFSI (sodium(I) Bis(fluorosulfonyl)imide), analogs thereof, and combinations thereof; or
a zinc salt selected from the group consisting of zinc trifluoromethanesulfonate, Zn(ClO 4 ) 2 , Zn(PF 6 ) 2 , Zn(BF 4 ) 2 , Zn(TFSI) 2 (zinc(II) Bis(trifluoromethanesulfonyl)imide), Zn(FSI) 2 (zinc(II) Bis(fluorosulfonyl)imide), analogs thereof, and combinations thereof.
10. The electrochemical cell as defined in claim 8 wherein the polymeric single-ion conductor coating further includes a solvent to increase metal cation mobility.
11. The electrochemical cell as defined in claim 8 , further comprising a separator positioned between the positive electrode and the polymeric single-ion conductor coating of the negative electrode.
12. The electrochemical cell as defined in claim 8 wherein the pendent metal salt groups are substantially evenly distributed along the surface of the metal substrate.
13. The electrochemical cell as defined in claim 8 wherein the pendent metal salt is one of: lithium malonatodifluoroborate, NaClO 4 , NaPF 6 , NaBF 4 , NaFSI (sodium(I) bis(fluorosulfonyl)imide), zinc trifluoromethanesulfonate, Zn(ClO 4 ) 2 , Zn(PF 6 ) 2 , Zn(BF 4 ) 2 , Zn(FSI) 2 (zinc(II) bis(fluorosulfonyl)imide), and combinations thereof.
14. A method for obtaining a homogeneous distribution of metal ions across a surface of a metal substrate, the method comprising:
selecting the metal substrate from the group consisting of lithium, sodium, and zinc; and
forming a polymeric single-ion conductor coating on the surface of the metal substrate, the polymeric single-ion conductor coating formed of i) a metal salt of a sulfonated tetrafluoroethylene-based fluoropolymer copolymer or ii) a polymeric metal salt having a polymeric backbone and pendent metal salt groups attached to the polymeric backbone, wherein the polymeric backbone is selected from the group consisting of polyolefin, polyvinylidene fluoride, polysulfone, polyethylene oxide, polyacrylate, polysiloxane, poly(vinyl acetate), polyimide, and co-polymers thereof and the pendent metal salt groups are attached directly to one of the polyolefin, polyvinylidene fluoride, polyethylene oxide, polysulfone and polyimide
wherein forming the polymeric single-ion conductor coating on the surface of the metal substrate includes:
forming a coating composition including a solvent and one of the metal salt of sulfonate tetrafluoroethylene-based fluoropolymer copolymer or the polymeric metal salt dissolved or dispersed in the solvent;
coating the coating composition on a sacrificial material;
drying the coating to form a free-standing film;
removing the sacrificial material from the free-standing film; and
vacuum depositing the metal substrate on the free-standing film.
15. The method as defined in claim 14 wherein:
the pendent metal salt is one of:
a lithium salt selected from the group consisting of lithium bis(trifluoromethane)sulfonimide, lithium malonatodifluoroborate, lithium sulfonate, lithium triflate, analogs thereof, and combinations thereof; or
a sodium salt selected from the group consisting of sodium trifluoromethanesulfonate, NaClO 4 , NaPF 6 , NaBF 4 , NaTFSI (sodium(I) Bis(trifluoromethanesulfonyl)imide), NaFSI (sodium(I) Bis(fluorosulfonyl)imide), analogs thereof, and combinations thereof; or
a zinc salt selected from the group consisting of zinc trifluoromethanesulfonate, Zn(ClO 4 ) 2 , Zn(PF 6 ) 2 , Zn(BF 4 ) 2 , Zn(TFSI) 2 (zinc(II) Bis(trifluoromethanesulfonyl)imide), Zn(FSI) 2 (zinc(II) Bis(fluorosulfonyl)imide), analogs thereof, and combinations thereof.
16. The method as defined in claim 15 , further comprising forming the polymeric metal salt by tethering the pendent metal salt groups to the polymeric backbone.
17. The method as defined in claim 14 wherein the metal salt of a sulfonated tetrafluoroethylene-based fluoropolymer copolymer and the pendent metal salt group are substantially evenly distributed along the surface of the metal substrate.
18. The method as defined in claim 14 , wherein the pendent metal salt is one of: lithium malonatodifluoroborate, NaClO 4 , NaPF 6 , NaBF 4 , NaFSI (sodium(I) bis(fluorosulfonyl)imide), zinc trifluoromethanesulfonate, Zn(ClO 4 ) 2 , Zn(PF 6 ) 2 , Zn(BF 4 ) 2 , Zn(FSI) 2 (zinc(II) bis(fluorosulfonyl)imide), and combinations thereof.