Deposition of boron and carbon containing materials
Methods of depositing boron and carbon containing films are provided. In some embodiments, methods of depositing B,C films with desirable properties, such as conformality and etch rate, are provided. One or more boron and/or carbon containing precursors can be decomposed on a substrate at a temperature of less than about 400° C. In some embodiments methods of depositing silicon nitride films comprising B and C are provided. A silicon nitride film can be deposited by a deposition process including an ALD cycle that forms SiN and a CVD cycle that contributes B and C to the growing film.
1. A method of depositing a B x C film on a three-dimensional structure on a substrate in a reaction space, comprising:
contacting the three-dimensional structure on the substrate with a vapor phase boron precursor in a carrier gas at a process temperature of less than 400° C., such that the boron precursor decomposes on the three-dimensional structure to form the B x C film, wherein x is 0.1 to 25, and wherein the B x C film has an etch rate in a solution comprising hydrofluoric acid of less than 0.2 nm/min.
2. The method of claim 1 , wherein the three-dimensional structure has an aspect ratio of greater than 8:1.
3. The method of claim 1 , wherein the B x C film has a step coverage of greater than 95% on the three-dimensional structure.
4. The method of claim 1 , wherein the B x C film has a reduced etch rate relative to thermal silicon oxide.
5. The method of claim 1 , wherein the B x C film has a wet etch rate ratio relative to the etch rate of thermal silicon oxide of less than 0.3.
6. The method of claim 1 , wherein the etch rate is less than 0.02 nm/min.
7. The method of claim 1 , wherein the carrier gas comprises nitrogen.
8. The method of claim 1 , wherein the carrier gas comprises at least one of helium and neon.
9. The method of claim 1 , wherein a film density of the B x C film is less than 2.5 g/cm 3 .
10. The method of claim 1 , wherein the substrate comprises silicon.
11. The method of claim 1 , wherein the substrate comprises silicon nitride.
12. The method of claim 1 , wherein the B x C film serves as an etch stop layer in a patterning process.
13. The method of claim 12 , wherein the etch stop layer has a film density of 2.0 g/cm 3 to 2.5 g/cm 3 .
14. The method of claim 1 , further comprising exposing the B x C film to a post-deposition plasma treatment process subsequent to depositing the B x C film.
15. The method of claim 14 , wherein the post-deposition plasma treatment process comprises generating a plasma from at least one of a noble gas, nitrogen gas, oxygen gas, and ozone.
16. The method of claim 1 , wherein the process temperature is between 375° C. and 400° C.
17. The method of claim 1 , wherein the process temperature is less than 350° C.
18. The method of claim 1 , wherein the reaction space is part of a batch reactor.
19. The method of claim 18 , further comprising exposing the substrate to a post-deposition plasma treatment process subsequent to forming the etch stop layer.
20. A method of forming an etch stop layer on a three-dimensional feature on a substrate, comprising:
contacting the three-dimensional feature with a vapor phase boron precursor at a process temperature of less than 400° C. such that the boron precursor decomposes on the substrate, wherein the etch stop layer layer comprises B x C, where x is from 0.1 to 25, and wherein a film density of the B x C-film is from 2.0 g/cm 3 to 2.5 g/cm 3 .