Silica-coated alumina activator-supports for metallocene catalyst compositions
Silica-coated alumina activator-supports, and catalyst compositions containing these activator-supports, are disclosed. Methods also are provided for preparing silica-coated alumina activator-supports, for preparing catalyst compositions, and for using the catalyst compositions to polymerize olefins.
1. An activator-support comprising a silica-coated alumina treated with an electron-withdrawing anion, wherein:
the silica-coated alumina has a weight ratio of alumina to silica in a range from about 1:1 to about 2:1 and a surface area in a range from about 200 to about 600 m 2 /g; and
the electron-withdrawing anion comprises fluoride.
2. The activator-support of claim 1 , wherein the weight ratio of alumina to silica is in a range from about 1.2:1 to about 1.8:1.
3. The activator-support of claim 1 , wherein the silica-coated alumina is further characterized by:
a surface area in a range from about 250 to about 500 m 2 /g; and
a pore volume in a range from about 0.5 to about 1.8 mL/g.
4. The activator-support of claim 1 , wherein the activator-support contains from about 2 to about 15 wt. % fluoride.
5. The activator-support of claim 4 , wherein the silica-coated alumina is further characterized by an average particle size in a range from about 5 to about 150 microns.
6. The activator-support of claim 4 , wherein the silica-coated alumina is further characterized by:
a surface area in a range from about 250 to about 500 m 2 /g; and
a pore volume in a range from about 1 to about 1.6 mL/g.
7. The activator-support of claim 6 , wherein the silica-coated alumina is further characterized by an average particle size in a range from about 30 to about 100 microns.
8. The activator-support of claim 1 , wherein the activator-support is further characterized by:
a surface area in a range from about 200 to about 500 m 2 /g; and
a pore volume in a range from about 0.8 to about 1.8 mL/g.
9. The activator-support of claim 1 , wherein:
the weight ratio of alumina to silica is in a range from about 1.2:1 to about 1.8:1; and
the activator-support contains from about 3 to about 12 wt. % fluoride.
10. The activator-support of claim 9 , wherein the silica-coated alumina is further characterized by
a pore volume in a range from about 0.8 to about 1.7 mL/g.
11. The activator-support of claim 9 , wherein the electron-withdrawing anion further comprises sulfate or phosphate.
12. The activator-support of claim 9 , wherein the activator-support is further characterized by:
a surface area in a range from about 200 to about 500 m 2 /g; and
a pore volume in a range from about 1 to about 1.6 mL/g.
13. A process for preparing an activator-support, the process comprising:
contacting a silica-coated alumina with a fluoriding agent to form the activator-support;
wherein the silica-coated alumina has a weight ratio of alumina to silica in a range from about 1:1 to about 2:1 and a surface area in a range from about 200 to about 600 m 2 /g; and
wherein the activator-support contains from about 2 to about 15 wt. % fluoride.
14. The process of claim 13 , further comprising a step of drying and/or a step of calcining after the contacting step.
15. The process of claim 13 , further comprising a step of calcining the silica-coated alumina prior to the contacting step.
16. The process of claim 13 , wherein a slurry of the silica-coated alumina in a solvent is contacted with the fluoriding agent.
17. The process of claim 13 , wherein the silica-coated alumina is impregnated with a solution containing the fluoriding agent and a solvent.
18. The process of claim 17 , wherein the solvent comprises water or an alcohol.
19. The process of claim 13 , wherein the fluoriding agent comprises hydrofluoric acid (HF), ammonium fluoride (NH 4 F), ammonium bifluoride (NH 4 HF 2 ), ammonium tetrafluoroborate (NH 4 BF 4 ), ammonium hexafluorosilicate ((NH 4 ) 2 SiF 6 ), ammonium hexafluorophosphate (NH 4 PF 6 ), hexafluorotitanic acid (H 2 TiF 6 ), ammonium hexafluorotitanic acid ((NH 4 ) 2 TiF 6 ), hexafluorozirconic acid (H 2 ZrF 6 ), AlF 3 , NH 4 AlF 4 , triflic acid, ammonium triflate, or any combination thereof.
20. The process of claim 13 , wherein the silica-coated alumina is calcined while being contacted with the fluoriding agent.
21. The process of claim 13 , wherein a gas stream containing the fluoriding agent fluidizes the silica-coated alumina during calcination.
22. The process of claim 13 , wherein the fluoriding agent comprises perfluorohexane, perfluorobenzene, fluoromethane, trifluoroethanol, HF, F 2 , silicon tetrafluoride (SiF 4 ), a tetrafluoroborate (BF 4 − ) compound, or any combination thereof.
23. The process of claim 13 , wherein:
the silica-coated alumina is characterized by a surface area in a range from about 250 to about 500 m 2 /g and a pore volume in a range from about 0.5 to about 1.8 mL/g;
the weight ratio of alumina to silica is in a range from about 1.2:1 to about 1.8:1; and
the activator-support contains from about 3 to about 12 wt. % fluoride.