Reinforced polyamide molding compounds having low haze and molded bodies therefrom

1. A polyamide molding compound comprising the following components:

(A) 40 to 95 wt % of a polyamide mixture consisting of the polyamides (A1) and (A2), wherein

(A1) 42 to 68 wt % of at least one semi-crystalline polyamide is selected from the group comprising PA 46, PA 66, PA 66/6, PA 610, PA 612, PA 614, PA 615, PA 616, and mixtures thereof; and

(A2) 32-58 wt % of at least one transparent semi-aromatic polyamide having at least 30 mol % of monomers having aromatic structural units, with respect to the total quantity of diamines and dicarboxylic acids is in the polyamide (A2) that is amorphous or microcrystalline;

(B) 5 to 50 wt % of at least one glass filler having a refractive index in the range from 1.540 to 1.600; and

(C) 0 to 10 wt % of at least one additive;

wherein the weight proportions of the components (A) to (C) add up to 100% by weight of the component (A) and the weight proportions of the components (A1) and (A2) add up to 100% by weight of component (A);

wherein the polyamide molding compound has a transparency of at least 80% and a haze of at most 40%;

wherein the transparency and haze of the polyamide molding compound are measured in accordance with ASTM D1003 on a molded plate of the polyamide molding compound having a dimension of 60 mm×60 mm×2 mm.

2. The polyamide molding compound in accordance with claim 1 , wherein the polyamide mixture (A) comprises 45 to 65 wt % polyamide (A1); and 35 to 55 wt % polyamide (A2); and/or

the proportion of component (A) in the polyamide molding compound is in the range from 49 to 90 wt % with respect to the sum of components (A) to (C); and/or

the proportion of component (B) in the polyamide molding compound is in the range from 10 to 45 wt % with respect to the sum of the components (A) to (C); and/or

the proportion of component (C) in the molding compound is in the range from 0 to 6 wt % with respect to the sum of components (A) to (C).

3. The polyamide molding compound in accordance with claim 1 , wherein the polyamide (A1) is PA 66.

4. The polyamide molding compound in accordance with claim 1 , wherein the at least one transparent polyamide (A2) comprises at least 35 mol % of monomers having aromatic structural units, with respect to the total quantity of diamines and dicarboxylic acids.

5. The polyamide molding compound in accordance with claim 1 , wherein the monomers having aromatic structural units for the transparent polyamide (A2) are selected from the group consisting of terephthalic acid, isophthalic acid, naphthalenedicarboxylic acid (NDA), biphenyldicarboxylic acid, 4,4′-diphenyl ether dicarboxylic acid, 4,4′-diphenylmethanedicarboxylic acid, and 4,4-diphenylsulfonedicarboxylic acid, 1,5-anthracene dicarboxylic acid, p-terphenylene-4,4′-dicarboxylic acid, 2,5-pyridine dicarboxylic acid, xylylenediamine, and mixtures thereof.

6. The polyamide molding compound in accordance with claim 1 , wherein the transparent polyamides (A2) are made up of the following monomers:

(a-A2) 0 to 100 mol % of cycloaliphatic diamines, with respect to the total quantity of diamines;

(b-A2) 0 to 100 mol % of diamines having aromatic structural units, with respect to the total quantity of diamines;

(cA-2) 0 to 100 mol % of open-chain, aliphatic diamines, preferably having 6 to 10 carbon atoms, in particular having 6 carbon atoms, with respect to the total quantity of diamines;

(d-A2) 0 to 70 mol % of open-chain aliphatic dicarboxylic acids, with respect to the total quantity of dicarboxylic acids;

(e-A2) 30 to 100 mol % of aromatic dicarboxylic acids, with respect to the total quantity of dicarboxylic acids;

(f-A2) 0 to 70 mol % of cycloaliphatic dicarboxylic acids, with respect to the total quantity of dicarboxylic acids; and

(g-A2) 0 to 40 wt % of lactams and/or aminocarboxylic acids having 6 to 12 carbon atoms, with respect to the total quantity of the monomers (a-A2) to (g-A2),

where the sum of the diamines (a-A2), (b-A2), and (c-A2) produces 100 mol %;

where the sum of the dicarboxylic acids (d-A2), (e-A2), and (f-A2) produces 100 mol %; and

where the sum of the monomers (b-A2) and (e-A2) amounts to at least 30 mol %, with respect to the sum of the total diamines and of the total dicarboxylic acids in the polyamide (A2).

7. The polyamide molding compound in accordance with claim 6 , wherein

the cycloaliphatic diamine (a-A2) is selected from the group consisting of bis(4-amino-3-methylcyclohexyl)methane, bis-(4-aminocylcohexyl)methane, bis-(4-amino-3-ethylcyclohexyl)methane, bis-(4-amino-3,5,-dimethylcyclohexyl)methane, 2,6-norbornane diamine, 1,3-diaminocyclohexane, 1,4-diaminocyclohexanediamine, isophorone diamine, 1,3-bis-(aminomethyl)cyclohexane, 1,4-bis-(aminomethyl)cyclohexane, 2,2-(4,4′-diaminodicyclohexyl)propane, and mixtures thereof;

the aromatic diamine (b-A2) is selected from xylylenediamines;

and/or

the diamine (c-A2) is selected from the group consisting of 1,4-butanediamine, 1,5-pentanediamine, 2-methyl-1,5,pentanediamine, hexanediamines, 2,2,4-trimethyl-1,6-hexamethylenediamine, 2,4,4-trimethyl-1,6-hexamethylenediamine, nonanediamines, 1,10-decanediamine, 1,11-undecanediamine, 1,12-dodecanediamine, 1,13-tridecanediamine, 1,14-tetradecanediamine, 1,18-octadecanediamine, and mixtures thereof;

and/or

the aliphatic dicarboxylic acid (d-A2) is selected from the group consisting of 1,6-apidic acid, 1,9-nonanedioic acid, 1,10-decanedioic acid, 1,11-undecanedioic acid, 1,12 dedecanedioic acid 1,13-tricanedioic acid, 1,14-tetradecanedioic acid, 1,16-hexxdecanedioic acid, 1,18-octadecanedioic acid, and mixtures thereof;

and/or

the aromatic dicarboxylic acid (e-A2) is selected from the group consisting of terephthalic acid, isophthalic acid, naphthalenedicarboxylic acid (NDA), biphenyldicarboxylic acid, 4,4′-diphenyl ether dicarboxylic acid, 4,4′-diphenylmethanedicarboxylic acid, and 4,4′-diphenylsulfonedicarboxylic acid, anthracene dicarboxylic acid, p-terphenylene-4,4″-dicarboxylic acid, and 2,5-pyridinedicarboxylic acid, and mixtures thereof;

and/or

the cycloaliphatic dicarboxylic acid (f-A2) is selected from the group consisting of 1,3-cyclopentanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, 2,3-norbornanedicarboxylic acid, 2,6-norbornanedicarboxylic acid, and mixtures thereof;

and/or

the lactam and/or the α,ω-aminocarboxylic acids (g-A1) and/or (g-A2) is/are selected from the group consisting of m-aminobenzoic acid, p-aminobenzoic acid, caprolactam (CL), α,ω-aminocaproic acid, α,ω-aminoheptanoic acid, α,ω-aminooctanoic acid, α,ω-aminononanoic acid, α,ω-aminodecanoic acid, α,ω-aminoundecanoic acid (AUA), laurolactam (LL), and α,ω-aminododecanoic acid (ADA).

8. The polyamide molding compound in accordance with claim 1 , wherein the transparency of the polyamide molding compound amounts to at least 83%; and/or

the haze of the polyamide molding compound amounts to a maximum of 35%, or wherein the molded body has an arithmetical mean roughness Ra determined in accordance with DIN EN ISO 4287 (2010-07) by means of a MarSurf XR1 Surface Measuring Station of at most 0.12 μm and/or has a surface roughness R z of at most 1.50 μm.

9. The polyamide molding compound in accordance with claim 1 , wherein the polyamide (A2) is selected from the group consisting of PA 6I/6T, PA 10I/10T, PA DI/DT (D=2-methyl-1,5-pentanediamine), PA MACMI/12, PA MACMI/1012, PA MACMT/12, PA MACMI/MACMT/12, PA MACMI/MACMT, PA MACMI/MACMT/MACM12, PA 6I/6T/MACMI/MACMT, PA 6I/6T/MACMI/MACMT/12, PA 6I/MACMI, PA 6I/6T/PACMI/PACMT, PA 6I/612/MACMI/MACM12, PA 6T/612/MACMT/MACM12, PA 6I/6T/612/MACMI/MACMT/MACM12, PA 6I/6T/MACMI/MACMT/PACMI/PACMT, PA 6I/6T/MACMI/MACMT/PACMI/PACMT/12, PA MACMI/MACMT/MACM36, PA MACMI/MACM36, PA MACMT/MACM36, PA 12/PACMI, PA 12/MACMT, PA 6/PACMT, PA 6/PACMI, PA MXDI, PA MXDI/MXD6, PA MXDI/MXD10, PA MXDI/MXDT, PA MXDI/MACMI, PA MXDI/MXDT/MACMI/MACMT, PA 6I/6T/BACI/BACT, PA MACMI/MACMT/BACI/BACT, PA 6I/6T/MACMI/MACMT/BACI/BACT, and mixtures thereof.

10. The polyamide molding compound in accordance with claim 1 , wherein the at least one glass filler (B) is selected from the group consisting of glass fibers, ground glass fibers, glass particles, glass flakes, glass spheres, hollow glass spheres, and combinations thereof.

11. The polyamide molding compound in accordance with claim 1 , wherein the glass type of the at least one glass filler (B) is selected from the group consisting of E-glass, E-CR-glass, R-glass, AR-glass, and mixtures of glass having substantially the same refractive index.

12. The polyamide molding compound in accordance with claim 1 , wherein the at least one additive (C) is selected from the group consisting of inorganic and organic stabilizers, monomers, impact modifiers, lubricants, colorants, marking means, photochromic agents, demolding means, condensation catalysts, chain regulators, foaming agents, anti-blocking agents, optical brighteners, non-halogen flame retardants, natural sheet silicates, synthetic sheet silicates, nanoscale fillers having a particle size (d90) of a maximum of 100 nm, and mixtures thereof.

13. The polyamide molding compound in accordance with claim 1 , wherein component (A2) has a glass transition temperature determined in accordance with ISO 11357-2 of at least 120° C.

14. A molded body comprising a polyamide molding compound in accordance with claim 1 .

15. The molded body in accordance with claim 14 , which is a multilayer molded body.

16. The polyamide molding compound in accordance with claim 5 , wherein the monomers having aromatic structural units for the transparent polyamide (A2) are selected from the group of terephthalic acid, isophthalic acid, 1,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, and mixtures thereof.

17. The polyamide molding compound in accordance with claim 5 , wherein the monomers having aromatic structural units for the transparent polyamide (A2) are selected from the group of terephthalic acid, isophthalic acid, 1,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, meta-xylylenediamine, and mixtures thereof.