The present disclosure relates to a method for manufacturing a covalently functionalized coated magnetic nanoparticle and to said particles and uses thereof. The preparation method includes forming a shell of a hydrophilic polymer coating layer on top of a magnetic metal core coated with a carbon coating. In the method a particle comprising a magnetic metal core coated with a carbon coating is provided. The surface of the particle is subjected to covalent functionalization by generating amino reactive groups via diazonium chemistry and subsequently an irreversible attachment of an atom transfer radical polymerization (ATRP) initiator is carried out on said surface. A hydrophilic polymer layer is formed) by a surface initiated atom transfer radical polymerization (SI-ATRP) reaction with a monomer comprising N-isopropylacrylamide (NIPAM).
1. A method for manufacturing a covalently functionalized coated magnetic nanoparticle, which includes forming a shell of a hydrophilic polymer coating layer on top of a magnetic metal core coated with a carbon coating, comprising the steps of
(i) providing a particle comprising a magnetic metal core coated with a carbon coating, and
(ii) subjecting the surface of the particle from step (i) to covalent functionalization by generating amino reactive groups on said surface via diazonium chemistry, and
(iii) carrying out an irreversible attachment of an atom transfer radical polymerization (ATRP) initiator on the surface obtained from step (ii), and
(iv) forming a hydrophilic polymer layer on the surface obtained from step (ii) by a surface initiated atom transfer radical polymerization (SI-ATRP) reaction with a monomer comprising N-isopropylacrylamide (NIPAM).
2. The method of claim 1 , wherein the reactions of steps (ii)-(iv) take place in an aqueous solvent.
3. The method of claim 1 , wherein the reaction temperatures at steps (ii)-(iv) are less than 30° C.
4. The method of claim 1 , wherein the functionalization includes use of an amine.
5. The method of claim 4 , wherein the amine is 4-aminophenylamine.
6. The method of claim 1 , wherein the magnetic metal core is selected from cobalt, iron or nickel.
7. The method of claim 1 , wherein the initiator is selected from 2-bromo-2-methylpropionyl bromide, 2-bromobutyrate, ethyl 2-bromopropionate or 2-chloropropionyl chloride.