Luminescent crystals and manufacturing thereof

1. A method for manufacturing luminescent crystals of 3-500 nm size;

said luminescent crystals being selected from compounds of formula (I)

[M 1 A 1 ] a M 2 b X c   (I), wherein:

A 1 represents one or more organic cations selected from the group consisting of ammonium, formamidinium, guanidinium, imidazolium, pyridinium, pyrrolidinium, protonated thiourea,

M 1 is optional, and if present, represents one or more alkaline metals selected from Cs, Rb, K, Na, Li,

M 2 represents one or more metals selected from the group consisting of Ge, Sn, Pb, Sb, and Bi,

X represents one or more anions selected from the group consisting of chloride, bromide, iodide, cyanide, thiocyanate, isothiocyanate and sulfide,

a represents 1-4,

b represents 1-2,

c represents 3-9;

said method comprising the steps of:

(a) providing a solid material, said solid material (i) having a stoichiometric composition of a moles (A 1 +M 1 ), b moles M 2 and c moles X and (ii) having an average particle size of at least 100 nm and a poly-disperse size distribution;

(b) dispersing said material in the presence of a liquid, whereby said liquid being selected from (i) liquid surfactants, (ii) a combination of surfactant and solvent, (iii) a combination of surfactant, solvent and pre-polymer or polymer and (iv) a combination of surfactant and liquid pre-polymer; and whereby said dispersing is effected by ball milling, by ultrasound, by high shear mixing or by high pressure dispersion.

2. The method according to claim 1 , whereby dispersing of step (b) is effected by ball milling.

3. The method according to claim 1 , whereby dispersing of step (b)

is effected by ball milling with a ball size between 10-1000 μm; and/or

is effected with a specific power input per weight of suspension of at least 10 W/kg; and/or

is effected at a temperature below 120° C.

4. The method according to claim 1 , wherein said luminescent crystals are selected from the group of FAPbX 3 ; wherein FA represents formamidinium.

5. The method according to claim 1 ,

wherein said solvents are selected from the group of aliphatic hydrocarbons (including linear, branched and cyclic hydrocarbons), aromatic hydrocarbons, ethers (including glycol-ethers), esters, alcohols, ketones; and/or

wherein said surfactants are selected from the group of non-ionic, anionic, cationic and zwitter-ionic surfactants; and/or

wherein said pre-polymer is selected from the group of acrylates, carbonates, sulfones, epoxies, vinyls, urethanes, imides, esters, furanes, melamines, styrenes, and silicones, particularly acrylates, urethanes, styrenes, and silicones; and/or

wherein said polymer is selected from the group of acrylate polymers, carbonate polymers, sulfone polymers, epoxy polymers, vinyl polymers, urethane polymers, imide polymers, ester polymers, furane polymers, melamine polymers, styrene polymers and silicone polymers and cyclic olefin copolymers.

6. The method according to claim 1 , wherein in step (a) said solid material:

is obtained by a dry synthetic process; or

is obtained by a wet synthetic process; or

is in situ formed by stoichiometric reaction of two or more precursors that comply with the net stoichiometric composition of formula (I).

7. The method according to claim 6 , wherein:

said dry synthetic process is a dry milling process;

said wet synthetic process is a precipitation process from a solvent or an aqueous phase;

said in situ formation takes place upon ball-milling the starting materials in the presence of surfactant and optionally solvent and/or liquid pre-polymer and/or dissolved solid polymer.

8. The method according to claim 1 , wherein

the weight ratio solid material:liquid material is in the range of 0.0001-0.5, wherein the weight of liquid material is defined as solvent+surfactant+pre-polymer, if present+polymer, if present; and/or

the weight ratio surfactant:solid material is in the range of 100-0.01.

9. The method according to claim 1 further comprising

the step of replacing one or more atom X of synthesized luminescent crystals (I) with another atom X by anion exchange; and/or

the step of combining two or more types of luminescent crystals of formula (I).

10. A composition in the form of a suspension, comprising (i) luminescent crystals of 3-500 nm size, (ii) a surfactant, (iii) optionally a solvent, and (iv) optionally a polymer and/or pre-polymer,

wherein

the luminescent crystals (i) are selected from the group of FAPbX 3 , wherein FA represents formamidinium and X represents one or more anions selected from the group consisting of chloride, bromide, iodide, cyanide, thiocyanate, isothiocyanate and sulfide;

the surfactant (ii) is selected from the group of zwitterionic surfactants; and

the pre-polymer/polymer (iv), if present, is selected from the group of acrylates.

11. A solid polymer composition, comprising:

(i) luminescent crystals of 3-500 nm size selected from the group of FAPbX 3 , wherein FA represents formamidinium and X represents one or more anions selected from the group consisting of chloride, bromide, iodide, cyanide, thiocyanate, isothiocyanate and sulfide, and

(ii) surfactant selected from the group of non-ionic, anionic, cationic and zwitter-ionic surfactants; and

(iv) a hardened/cured polymer, said polymer selected from the group of acrylate polymers, epoxy polymers, urethane polymers, silicone polymers and cyclic olefin copolymers.

12. The solid polymer composition according to claim 11 , wherein:

the weight ratio luminescent crystals:matrix is in the range of 0.00001-0.2, wherein the weight of the matrix is defined by polymer+surfactant; and/or

the weight ratio surfactant:luminescent crystals is in the range of 100-0.01.

13. The solid polymer composition according to claim 11 , wherein

the surfactant (ii) is selected from the group of zwitterionic surfactants; and/or

the polymer (iv) is selected from the group of acrylates.

14. A component, comprising a sheet-like substrate coated with one or more layers, wherein at least one of said layers is a functional luminescent crystal containing layer, wherein said functional luminescent crystal containing layer comprises a solid polymer composition according to claim 11 .

15. A device, selected from the group of electronic devices and optical devices, wherein

said device comprises a substrate and a functional luminescent crystal containing layer; and

said functional luminescent crystal containing layer comprises a solid polymer composition according to claim 11 .

16. An article comprising a decorative coating, wherein

said article comprises a substrate and a coating,

said coating comprises a solid polymer composition according to claim 11 .

17. A method for converting blue light into white light in a QLED or in an LCD, the method comprising using a composition according to claim 11 .

18. The solid polymer composition according to claim 11 , wherein the luminescent crystals (i) are of 3-15 nm size and 75-100% (n/n) of the luminescent crystals (i) are isometric.