Use of H
The disclosure relates to the use of H 2 SO 4 as an electrolyte in processes for polishing metals, specifically metal parts, for example in jewellery. According to some embodiments the polishing is carried out based on ion transport with electrically conductive free solids in a gaseous environment. According to some embodiments the solids comprise spherical particles with porosity and affinity for retaining the electrolyte so that they have appreciable electric conductivity.
1. A method for polishing a metal part, the method comprising:
electrically coupling the metal part to a first pole of a current generator; and
subjecting the part to friction with non-electrically conductive polymeric bodies charged with a negative electrical charge in a gaseous environment, the non-electrically conductive polymeric bodies retaining an aqueous solution of H 2 SO 4 as an electrolyte, the non-electrically conductive polymeric bodies being electrically coupled to a second pole of the current generator and configured to polish the metal part via ion transport, the second pole having opposite polarity to the first pole.
2. The method according to claim 1 , wherein the first pole is a positive pole and the second pole is a negative pole.
3. The method according to claim 1 , wherein the non-electrically conductive polymeric bodies are porous.
4. The method according to claim 1 , wherein the non-electrically conductive polymeric bodies are macroporous.
5. The method according to claim 1 , wherein the non-electrically conductive polymeric bodies include interconnected pores to retain the electrolyte.
6. The method according to claim 1 , wherein the non-electrically conductive polymeric bodies undergo deformation during the polishing of the metal part.
7. The method according to claim 6 , wherein the electrolyte is released under pressure from the non-electrically conductive polymeric bodies during the deformation.
8. The method of claim 1 , wherein the non-electrically conductive polymeric bodies comprise an ion exchange resin.
9. The method of claim 8 , wherein the ion exchange resin comprises sulfonated styrene-divinylbenzene copolymers.
10. The method according to claim 1 , wherein the non-electrically conductive polymeric bodies comprises a styrene-divinylbenzene copolymer matrix with sulfonic functional groups SO 3− .
11. The method according to claim 10 , wherein the styrene-divinylbenzene copolymer matrix with sulfonic functional groups SO 3− has an ion exchange capacity equal to or greater than 1.7 eq/L.
12. The method according to claim 1 , wherein the non-electrically conductive polymeric bodies are spherical in shape with a diameter of between 0.6 mm and 0.8 mm.
13. The method according to claim 1 , wherein the metal part is made from a material selected from the group consisting of steel, stainless steel and Cr—Co alloys and the electrolyte comprises an 8% to 25% concentration of H 2 SO 4 .
14. The method according to claim 1 , wherein in each of the non-electrically conductive polymeric bodies that retain the electrolyte, the electrolyte comprises 40% to 50% by weight of the non-electrically conductive polymeric body.
15. The method according to claim 13 , wherein in each of the non-electrically conductive polymeric bodies that retain the electrolyte, the electrolyte comprises 40% to 50% by weight of the non-electrically conductive polymeric body.
16. The method according to claim 1 , wherein the metal part is made from a Ni alloy and the electrolyte comprises a 15% to 30% concentration of H 2 SO 4 .
17. The method according to claim 1 , further comprising moving the metal part relative to the solid non-electrically conductive polymeric bodies.