Electrolytic medium for electropolishing and method of electropolishing with said medium
Electrolytic medium for electropolishing and electropolishing method using the electrolytic medium. The electrolytic medium includes solid particles retaining therein a water. Covering each of the solid particles that retains the water is an electrically non-conductive immiscible liquid. The non-conductive immiscible liquid is displaceable on the solid particles to allow electrical conductivity between solid particles that contact one another and to allow electrical conductivity between the solid particles and the workpiece upon the solid particles contacting the surface of the workpiece.
1 . An electrolytic medium for electropolishing a workpiece made of a conductive inorganic composite material, the electrolytic medium comprising:
solid particles that each retains a liquid comprising distilled water; and
an electrically non-conductive immiscible liquid covering each of the solid particles in which is retained the distilled water, the electrically non-conductive immiscible liquid being displaceable on the solid particles to allow electrical conductivity between solid particles that contact one another and to allow electrical conductivity between the solid particles and the workpiece upon the solid particles contacting a surface of the workpiece.
2 . The electrolytic medium according to claim 1 , wherein the electrically non-conductive immiscible liquid is in an amount sufficient to at least partially coat the surface of the workpiece.
3 . The electrolytic medium according to claim 1 , wherein the electrically non-conductive immiscible liquid comprises a liquid silicone.
4 . The electrolytic medium according to claim 1 , wherein the electrically non-conductive immiscible liquid viscosity is between 1 and 20 cP at 25° C.
5 . The electrolytic medium according to claim 3 , wherein the electrically non-conductive immiscible liquid viscosity is between 1 and 20 cP at 25° C.
6 . The electrolytic medium according to claim 1 , wherein each of the solid particles comprise an ion exchange resin.
7 . The electrolytic medium according to claim 6 , wherein the ion exchange resin comprises a copolymer of styrene and sulfonated divinylbenzene.
8 . The electrolytic medium according to claim 1 , wherein the solid particles have a diameter distribution between 0.05 and 1 mm.
9 . The electrolytic medium according to claim 1 , wherein the liquid retained in the solid particles has an electrical conductivity below 10 μS/cm.
10 . A method for electropolishing a surface of a workpiece made of a conductive inorganic composite material, the method comprising:
contacting the surface of the workpiece against an electrolytic medium that comprises solid particles that each has retained therein a liquid comprising distilled water, each of the solid particles retaining the liquid being covered by an electrically non-conductive immiscible liquid;
electrically connecting the workpiece to a first pole of an electrical power supply and electrically connecting the electrolytic medium to a second pole of the power supply, the first and second poles having opposite polarity; and
producing relative movement between the surface of the workpiece and the solid particles of the electrolytic medium.
11 . The method according to claim 10 , wherein the first pole is a negative pole and the second pole is a positive pole.
12 . The method according to claim 10 , wherein the electrolytic medium is electrically connected to an electrode that is electrically coupled to the second pole of the power supply such that current flows through the electrode to the electrolytic medium and then from the electrolytic medium through the workpiece.
13 . The method according to claim 10 , wherein the conductive inorganic composite material is selected from the group consisting of: a metal-metal composite material, a ceramic-ceramic composite material, and a metal-ceramic composite material.
14 . The method, according to claim 10 , wherein during electropolishing a positive voltage and a negative voltage are alternatingly applied to the workpiece.
15 . The method according to claim 14 , wherein during a first time interval the positive voltage is applied to the workpiece and during a second time interval the negative voltage is applied to the workpiece.
16 . The method according to claim 14 , wherein during a first time interval no voltage is applied to the workpiece for a duration of 0.1 to 100 microseconds, during a second time interval after the first time interval +5 to +100 volts is applied to the workpiece for a duration of 1 to 100 microseconds, during a third time interval after the second time interval no voltage is applied to the workpiece for a duration of 0.1 to 100 microseconds, and during a fourth time interval after the third time interval −10 to −250 volts is applied to the workpiece for a duration of 1 to 100 microseconds.
17 . The method according to claim 15 , wherein the positive voltage is applied to the workpiece at a constant rate during the first time interval and the negative voltage is applied to the workpiece at a constant rate during the second time interval.
18 . The method according to claim 15 , wherein the positive voltage is applied to the workpiece at a variable rate during the first time interval.
19 . The method according to claim 15 , wherein the negative voltage is applied to the workpiece at a variable rate during the second time interval.
20 . The method according to claim 19 , wherein the positive voltage is applied to the workpiece at a variable rate during the first time interval.