Reusable attaching apparatus and methods of making and using a reusable attaching apparatus

1. A method of attaching a reusable attaching apparatus to a surface, the method comprising:

providing a reusable attaching apparatus comprising: a mounting structure bonded to a reversible adhesive, the reversible adhesive comprising a shape memory polymer having a glass transition temperature (T g ) and comprising a deformable state at temperatures above the T g and a rigid state at temperatures below the T g ;

heating the reversible adhesive to a temperature above the T g , the shape memory polymer reaching the deformable state;

during the heating, contacting the reversible adhesive with a mounting surface and applying pressure thereto, the reversible adhesive deforming and increasing in contact area with the mounting surface; and

cooling the reversible adhesive to a temperature below the T g , the shape memory polymer adopting the rigid state and the reversible adhesive adhering to the mounting surface with an adhesion strength of at least about 1 MPa, thereby attaching the reusable attaching apparatus to the mounting surface,

wherein the shape memory polymer is prepared from a formulation comprising a shape memory polymer precursor and a crosslinking agent, the shape memory polymer precursor comprising a mixture of at least two epoxy monomers each having a different molecular weight, wherein an average molecular weight of the mixture is at least 400 q/mol.

2. The method of claim 1 , wherein the adhesion strength is at least about 1.5 MPa.

3. The method of claim 1 , wherein the pressure applied to the reversible adhesive is in a range from about 0.05 atm to about 10 atm.

4. The method of claim 1 , wherein heating the reversible adhesive comprises heating to a temperature of at least about 120% of the T g .

5. The method of claim 4 , wherein the temperature is at least about 160% of the T g .

6. The method of claim 1 , wherein the heating comprises conductive, radiative, or convective heating using an external heat source.

7. The method of claim 1 , wherein the heating comprises internal heating of the shape memory polymer.

8. The method of claim 7 , wherein the internal heating is carried out with a resistive heating element embedded in or positioned adjacent to the reversible adhesive.

9. The method of claim 8 , wherein the resistive heating element comprises an electrically conductive coil and/or electrically conductive particles.

10. The method of claim 7 , wherein the internal heating is carried out with light-absorbing particles.

11. The method of claim 1 , wherein the cooling comprises passive cooling.

12. The method of claim 1 , wherein the cooling comprises active cooling.

13. The method of claim 1 , further comprising, after the cooling, reheating the reversible adhesive to a temperature above the T g to detach the reusable attaching apparatus from the mounting surface.

14. The method of claim 1 , wherein the mounting surface comprises a natural or synthetic material.

15. The method of claim 1 , wherein the mounting surface is planar, curved, smooth, rough, dry and/or wet.

16. The method of claim 1 , wherein the mounting surface is covered partially or entirely by a liquid, the mounting surface being a wet surface, and

wherein, during the heating, as the reversible adhesive deforms and increases in contact area with the mounting surface, the liquid is forced from the contact area.

17. The method of claim 1 , wherein the shape memory polymer comprises a storage modulus of about 4 MPa or less in the deformable state.

18. The method of claim 1 , wherein the mounting structure includes one or more of the following: hook, bracket, and peg.

19. A method of attaching a reusable attaching apparatus to a surface, the method comprising:

providing a reusable attaching apparatus comprising: a mounting structure bonded to a reversible adhesive, the reversible adhesive comprising a shape memory polymer having a glass transition temperature (T g ) and comprising a deformable state at temperatures above the T g and a rigid state at temperatures below the T g ;

heating the reversible adhesive to a temperature above the T g , the shape memory polymer reaching the deformable state;

during the heating, contacting the reversible adhesive with a mounting surface and applying pressure thereto, the reversible adhesive deforming and increasing in contact area with the mounting surface; and

cooling the reversible adhesive to a temperature below the T g , the shape memory polymer adopting the rigid state and the reversible adhesive adhering to the mounting surface with an adhesion strength of at least about 1 MPa, thereby attaching the reusable attaching apparatus to the mounting surface,

wherein the mounting surface is covered partially or entirely by a liquid, the mounting surface being a wet surface, and

wherein, during the heating, as the reversible adhesive deforms and increases in contact area with the mounting surface, the liquid is forced from the contact area.

20. A method of attaching a reusable attaching apparatus to a surface, the method comprising:

providing a reusable attaching apparatus comprising: a mounting structure bonded to a reversible adhesive, the reversible adhesive comprising a shape memory polymer having a glass transition temperature (T g ) and comprising a deformable state at temperatures above the T g and a rigid state at temperatures below the T g ;

heating the reversible adhesive to a temperature above the T g , the shape memory polymer reaching the deformable state;

during the heating, contacting the reversible adhesive with a mounting surface and applying pressure thereto, the reversible adhesive deforming and increasing in contact area with the mounting surface; and

cooling the reversible adhesive to a temperature below the T g , the shape memory polymer adopting the rigid state and the reversible adhesive adhering to the mounting surface with an adhesion strength of at least about 1 MPa, thereby attaching the reusable attaching apparatus to the mounting surface,

wherein the shape memory polymer is prepared from a formulation comprising a shape memory polymer precursor comprising a mixture of at least two epoxy monomers each having a different molecular weight, and a crosslinking agent, and

wherein a first of the epoxy monomers has a molecular weight of 362 g/mole and a second of the epoxy monomers has a molecular weight of 1075 g/mol.