Microcellular foam sheet and processes of making and using
A solid state foaming process for generating a microcellular foam sheet for use in forming a container is provided includes a pre-foaming treatment phase prior to a solid state impregnation and foaming phase. The solid state microcellular foam sheet includes a central foamed section defining a foam layer within the microcellular foam sheet having a first population of cells within which are interspersed a second population of cells.
1. A solid state foaming process for generating a microcellular foam sheet for use in forming a container, the process comprising:
extruding a first layer including a first polymeric material and a blowing agent, wherein the first layer has a first density;
a first expansion comprising at least partially expanding the first layer with the blowing agent to form a pre-foamed sheet comprising a pre-foamed layer having a second density, less than the first density;
impregnating the pre-foamed layer in a solid state with a non-reacting gas that is soluble in the first polymeric material, proceeding until a predetermined concentration of the non-reacting gas in the first polymeric material is in the range of about 3.5 to 6 wt. %; and
a second expansion comprising at least partially expanding the pre-foamed layer with the non-reacting gas to form a microcellular foam layer having a third density, less than the second density.
2. The process of claim 1 wherein the first polymeric material comprises polyethylene terephthalate (PET), polyether ether ketone (PEEK), polyethylene naphthalate (PEN), polybutylene terephthalate (PBT), polymethyl methacrylate (PMMA), polylactide (PLA), polyhydroxy acid (PHA), polypropylene (PP), polyethylene (PE), or thermoplastic urethane (TPU).
3. The process according to claim 1 wherein the blowing agent comprises one of a chemical blowing agent or a physical blowing agent.
4. The process according to claim 3 wherein the chemical blowing agent comprises a combination of sodium bicarbonate and citric acid, a combination of sodium citrate and calcium carbonate, or a combination of calcium distearate, limestone, and calcium oxide.
5. The process according to claim 1 wherein the first expansion occurs during or subsequent to the first polymeric material passing through a die outlet during extrusion.
6. The process according to claim 1 wherein impregnating the pre-foamed layer comprises at least one of:
exposing the pre-foamed layer to the non-reacting gas at a pressure greater than atmospheric pressure for a predetermined period of time within the range of about 2-60 hours; or
exposing the pre-foamed layer to the non-reacting gas at a pressure of about 600 to 900 psi for a predetermined period of time within the range of about 2-60 hours.
7. The process according to claim 1 wherein at least one of:
the second density is less than the first density by about 12% or less; or
the third density is less than the second density by about 35 to 65%.
8. The process according to claim 1 comprising a desorption phase subsequent to the impregnating the pre-foamed layer with the non-reacting gas and prior to the second expansion, wherein the desorption phase occurs one of at atmospheric pressure or less, at a temperature at or below about −6° C., or a combination thereof.
9. The process according to claim 1 further comprising co-extruding, laminating, or extrusion coating a second layer adjacent the first layer to form a multi-layer sheet.
10. The process according to claim 1 wherein the second expansion comprises heating the pre-foamed sheet.
11. The process according to claim 1 wherein a predetermined period of time to reach the predetermined concentration of the non-reacting gas is in the range of about 50% or less of a period of time to achieve the same predetermined concentration of non-reacting gas in a layer that is not pre-foamed.
12. The process according to claim 1 wherein an amount of the blowing agent is in the range of about 0.1 to 5 wt. %.
13. The process according to claim 1 wherein the first polymeric material comprises at least one nucleating agent selected from one of an inorganic nucleating agent, an organic nucleating agent, or combinations thereof.
14. The process according to claim 13 wherein the nucleating agent is selected from the group consisting of talc and polytetrafluoroethylene.
15. The process according to claim 14 wherein the at least one nucleating agent is present in an amount of about 0.5 to 5 wt. %.
16. The process according to claim 1 wherein the microcellular foam layer comprises a central foam section having a first population of cells within which are interspersed a second population of cells having a smaller cell size than the first population of cells.
17. The process according to claim 16 wherein the first population of cells comprises an average diameter of greater than 100 micrometers and the second population of cells comprises an average diameter of less than 10 micrometers.
18. A solid state foaming process for generating a microcellular foam sheet for use in forming a container, the process comprising:
extruding a first layer including a first polymeric material and a blowing agent, wherein the first layer has a first density;
a first expansion comprising at least partially expanding the first layer with the blowing agent to form a pre-foamed sheet comprising a pre-foamed layer having a second density, less than the first density;
impregnating the pre-foamed layer in a solid state with a non-reacting gas that is soluble in the first polymeric material; and
a second expansion comprising at least partially expanding the pre-foamed layer with the non-reacting gas to form a microcellular foam layer having a third density, less than the second density, wherein the microcellular foam layer comprises a central foam section having a first population of cells within which are interspersed a second population of cells having a smaller cell size than the first population of cells.
19. The process according to claim 18 wherein the first population of cells comprises an average diameter of greater than 100 micrometers and the second population of cells comprises an average diameter of less than 10 micrometers.
20. A solid state foaming process for generating a microcellular foam sheet for use in forming a container, the process comprising:
extruding a first layer including a first polymeric material and a blowing agent, wherein the first layer has a first density;
a first expansion comprising at least partially expanding the first layer with the blowing agent to form a pre-foamed sheet comprising a pre-foamed layer having a second density, less than the first density;
impregnating the pre-foamed layer in a solid state with a non-reacting gas that is soluble in the first polymeric material; and
a second expansion comprising at least partially expanding the pre-foamed layer with the non-reacting gas to form a microcellular foam layer having a third density, less than the second density, wherein the second density is less than the first density by about 12% or less and the third density is less than the second density by about 35 to 65%.