Nanoparticles and systems and methods for synthesizing nanoparticles through thermal shock
Systems and methods of synthesizing nanoparticles on substrates using rapid, high temperature thermal shock. A method involves depositing micro-sized particles or salt precursors on a substrate, and applying a rapid, high temperature thermal shock to the micro-sized particles or the salt precursors to become nanoparticles on the substrate. A system may include a rotatable member that receives a roll of a substrate sheet having micro-sized particles or salt precursors; a motor that rotates the rotatable member so as to unroll the substrate; and a thermal energy source that applies a short, high temperature thermal shock to the substrate. The nanoparticles may be metallic, ceramic, inorganic, semiconductor, or compound nanoparticles. The substrate may be a carbon-based substrate, a conducting substrate, or a non-conducting substrate. The high temperature thermal shock process may be enabled by electrical Joule heating, microwave heating, thermal radiative heating, plasma heating, or laser heating.
1. A method of forming nanoparticles on a substrate, the method comprising:
depositing salt precursors on a substrate; and
applying a rapid, high temperature thermal shock to the substrate and the salt precursors to cause the salt precursors to become nanoparticles on the substrate,
wherein the high temperature thermal shock is between about 500 K and about 3000 K, and
a duration of the high temperature thermal shock is between about 1 ms and about 5 s.
2. The method of claim 1 , wherein the nanoparticles are metallic, ceramic, inorganic, semiconductor, compounds, or any combination thereof.
3. The method of claim 1 , wherein the salt precursors comprise metal chloride, metal nitrate, metal acetate, or any combination thereof.
4. The method of claim 1 , wherein the nanoparticles have an average diameter of between about 1.0 nm and about 20 nm.
5. The method of claim 1 , wherein the substrate is a carbon-based substrate, a conducting substrate, or a non-conducting substrate.
6. The method of claim 5 , wherein the carbon-based substrate is a reduced graphene oxide substrate or a carbon nanofiber substrate.
7. The method of claim 6 , further comprising:
electrospinning a polymer solution to obtain a nanofiber mat; and
stabilizing and carbonizing the nanofiber mat to obtain the carbon nanofiber substrate.
8. The method of claim 6 , wherein depositing salt precursors on a substrate includes:
dissolving a salt precursor in a solution;
applying the salt precursor solution to carbon nanofibers; and
drying the carbon nanofibers to obtain a precursor-loaded carbon nanofiber substrate.
9. The method of claim 6 , further comprising:
synthesizing graphene oxide;
forming a graphene oxide assembly; and
reducing the graphene oxide assembly to obtain the reduced graphene oxide substrate.
10. The method of claim 5 , wherein the conducting substrate is a metal-based substrate or includes conductive oxides.
11. The method of claim 5 , wherein the non-conducting substrate is a textile or wood.
12. The method of claim 1 , wherein the high temperature thermal shock is provided by direct Joule heating, high temperature radiation heating, microwave heating, plasma heating, or laser heating.
13. The method of claim 1 , further comprising modifying the substrate to change the wetting or interaction between the substrate and the nanoparticles so as to control a size or dispersion of the nanoparticles on the substrate.
14. The method of claim 13 , wherein modifying the substrate includes coating a layer on a surface of the substrate by gas phase, solution phase, or solid phase reactions or processes.
15. The method of claim 13 , wherein modifying the substrate includes treating a surface of the substrate using gas phase, solution phase, or solid phase reactions or processes.
16. A method of forming nanoparticles on a substrate, the method comprising:
depositing salt precursors on a substrate; and
applying a rapid, high temperature thermal shock to the substrate and the salt precursors to cause the salt precursors to become nanoparticles on the substrate,
wherein the high temperature thermal shock is between about 500 K and about 3000 K, and,
a duration of the high temperature thermal shock is based on a desired size of the nanoparticle.