Method for fabricating semiconductor structure including the substrate structure
View Patent ↗A substrate structure and a method for fabricating a semiconductor structure including the substrate structure are provided. The substrate structure includes a substrate, a bow adjustment layer, and a silicon layer. The bow adjustment layer is on the top surface of the substrate. The silicon layer is on the bow adjustment layer. The substrate structure has a total bow value, and the total vow value is from −20 μm to −40 μm.
1. A method for fabricating a semiconductor structure, comprising:
forming a substrate structure, comprising:
providing a ceramic substrate; and
forming a bow adjustment layer in direct contact with a top surface of the ceramic substrate to adjust a total bow value of the substrate structure to be less than 50 μm, wherein the ceramic substrate has a positive bow value when the bow adjustment layer has a negative bow value, and the ceramic substrate has a negative bow value when the bow adjustment layer has a positive bow value; and
forming a GaN-based semiconductor layer over the substrate structure.
2. The method for fabricating the substrate structure as claimed in claim 1 , wherein forming the bow adjustment layer on the top surface of the ceramic substrate is to adjust the total bow value of the substrate structure to be within a range from −20 μm to −40 μm.
3. The method for fabricating the substrate structure as claimed in claim 1 , wherein the total bow value of the substrate structure is the sum of a bow value of the ceramic substrate and a bow value of the bow adjustment layer.
4. The method for fabricating the substrate structure as claimed in claim 1 , wherein forming the substrate structure further comprises:
forming a silicon layer in direct contact with the bow adjustment layer, wherein the total bow value of the substrate structure is the sum of a bow value of the ceramic substrate, a bow value of the bow adjustment layer, and a bow value of the silicon layer.
5. The method for fabricating the substrate structure as claimed in claim 1 , wherein forming the substrate structure further comprises:
forming a silicon layer on the bow adjustment layer; and
forming a buffer layer on the silicon layer, wherein the total bow value of the substrate structure is the sum of a bow value of the ceramic substrate, a bow value of the bow adjustment layer, a bow value of the silicon layer, and a bow value of the buffer layer.
6. The method for fabricating the substrate structure as claimed in claim 1 , wherein providing the ceramic substrate comprises:
providing a plurality of substrate material powders;
performing a high-temperature process on the substrate material powders to form the ceramic substrate, wherein a temperature of the high-temperature process is from 1500° C. to 1900° C.; and
grinding the top surface of the ceramic substrate, such that a curvature of the top surface of the ceramic substrate is smaller than a curvature of a bottom surface of the ceramic substrate, wherein the bottom surface is opposite to the top surface.
7. The method for fabricating the substrate structure as claimed in claim 6 , wherein providing the ceramic substrate further comprises:
performing a bow measurement on the ceramic substrate before grinding the top surface of the ceramic substrate; and
defining the top surface and the bottom surface of the ceramic substrate based on a reference where the ceramic substrate has a negative bow value.
8. The method for fabricating the substrate structure as claimed in claim 7 , wherein providing the ceramic substrate further comprises:
forming a mark on the bottom surface of the ceramic substrate after defining the top surface and the bottom surface of the ceramic substrate.
9. The method for fabricating the substrate structure as claimed in claim 6 , wherein the substrate material powders comprise aluminum nitride, silicon carbide, aluminum oxide, or a combination thereof.
10. The method for fabricating the substrate structure as claimed in claim 1 , wherein the bow adjustment layer is deposited on the top surface of the ceramic substrate by a deposition process.
11. The method for fabricating the substrate structure as claimed in claim 10 , wherein the deposition process comprises a plasma-enhanced chemical vapor deposition (PECVD) process, a sub-atmospheric chemical vapor deposition (SACVD) process, or a combination thereof.
12. The method for fabricating the substrate structure as claimed in claim 1 , wherein the ceramic substrate is an aluminum nitride substrate.
13. The method for fabricating the substrate structure as claimed in claim 1 , wherein the bow adjustment layer comprises silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, or a combination thereof.