All solid state battery and method for producing same
A main object of the present disclosure is to provide an all solid state battery wherein interface resistance between a current collector and an active material layer is low. In the present disclosure, the above object is achieved by providing an all solid state battery comprising: an electrode including a current collector, an electron conductive layer, and an active material layer, in this order, and a solid electrolyte layer formed on the active material layer side of the electrode, and the electron conductive layer is an agglutinate of metal particles or a metal foil, and electron conductivity of the electron conductive layer is 1×10 3 S/cm or more at 25° C.
1. A method for producing the all solid state battery wherein the all solid state battery comprises an electrode and a solid electrolyte layer,
the electrode includes a current collector, an electron conductive layer, and an active material layer, in this order,
the solid electrolyte layer formed on the active material layer side of the electrode,
the electron conductive layer is an agglutinate of metal particles,
electron conductivity of the electron conductive layer is 1×10 3 S/cm or more at 25° C.,
the active material layer comprises an active material and an inorganic solid electrolyte, and
the solid electrolyte layer comprises an inorganic solid electrolyte, and
the method comprising steps of:
a first stack forming step of obtaining a first stack by placing the metal particles on the active material layer,
a second stack forming step of obtaining a second stack including the electron conductive layer by hot pressing the first stack, and
a current collector placing step of obtaining the electrode by placing the current collector on the electron conductive layer of the second stack,
wherein the first stack is formed by coating the active material layer with a slurry including metal particles in the first stacking step, and
the metal particles are plastically deformed in the second stack forming step.
2. The method for producing the all solid state battery according to claim 1 , wherein the first stack is pressed by a hot roll press with a line pressure of 3 ton/cm or more in the second stack forming step.
3. The method for producing the all solid state battery according to claim 1 , wherein the electron conductivity of the electron conductive layer is 2.1×10 4 S/cm or more at 25° C.
4. The method for producing the all solid state battery according to claim 1 , wherein the agglutinate includes a binder.
5. The method for producing the all solid state battery according to claim 1 , wherein material of the metal particles comprises Fe, Ni, or Al, or an alloy including at least one kind of these elements.
6. The method for producing the all solid state battery according to claim 1 , wherein an adhesive layer if formed partially between the current collector and the electron conductive layer.
7. The method for producing the all solid state battery according to claim 1 , wherein the electron conductive layer is the agglutinate of the metal particles including the agglutinate includes a binder, and the proportion of the metal particles, to the total of the metal particles and the binder, is 90 vol % or more.
8. The method for producing the all solid state battery according to claim 1 ,
wherein the electron conductive layer does not include a binder.
9. The method for producing the all solid state battery according to claim 1 ,
wherein a material of the metal particles comprises Fe, Ni, or Al, or an alloy including at least one kind of these elements,
the agglutinate includes a binder, and
the proportion of the metal particles, to the total of the metal particles and the binder, is 90 vol % or more.
10. The method for producing the all solid state battery according to claim 1 ,
wherein the metal particles are Ni particles,
the agglutinate includes a binder, and
the proportion of the Ni particles, to the total of the Ni particles and the binder, is 90 vol % or more and 95 vol % or less.