Gate stack treatment
The present disclosure describes a method for forming gate stack layers with a fluorine concentration up to about 35 at. %. The method includes forming dielectric stack, barrier layer and soaking the dielectric stack and/or barrier layer in a fluorine-based gas. The method further includes depositing one or more work function layers on the high-k dielectric layer, and soaking at least one of the one or more work function layers in the fluorine-based gas. The method also includes optional fluorine drive in annealing process, together with sacrificial blocking layer to avoid fluorine out diffusion and loss into atmosphere.
1. A method, comprising:
forming a fin on a substrate;
forming a gate dielectric stack on the fin, wherein the gate dielectric stack comprises a high-k dielectric layer disposed on an interfacial dielectric layer;
exposing a surface of the high-k dielectric layer to a fluorine-based gas.
2. The method of claim 1 , wherein the fluorine-based gas comprises fluorine gas (F 2 ), nitrogen trifluoride (NF 3 ), fluoroform (CHF 3 ), tetrafluoromethane (CF 4 ), sulfur hexafluoride (SF 6 ), hexafluoroethane (C 2 F 6 ), or combinations thereof.
3. The method of claim 1 , wherein exposing the surface of the high-k dielectric layer to the fluorine-based gas comprises heating the substrate at a temperature between about 70° C. and about 950° C.
4. The method of claim 1 , wherein exposing the surface of the high-k dielectric layer to the fluorine-based gas occurs at an ambient pressure between about 0.5 Torr and about 150 Torr.
5. The method of claim 1 , wherein exposing the surface of the high-k dielectric layer to the fluorine-based gas comprises increasing a fluorine concentration of the high-k dielectric layer to between about 0.01 atomic % and about 35 atomic %.
6. The method of claim 1 , further comprising:
depositing a sacrificial blocking layer on the high-k dielectric layer;
annealing the substrate at a temperature between about 70° C. and about 550° C.;
removing the sacrificial blocking layer; and
depositing a capping layer.
7. The method of claim 6 , wherein the sacrificial blocking layer comprises silicon or titanium nitride with a thickness between about 5 Å and about 30 Å.
8. The method of claim 6 , wherein annealing the substrate comprises annealing the substrate in nitrogen ambient, in forming gas ambient, in ammonia ambient, or in diluted oxygen ambient.
9. A method, comprising:
forming a fin on a substrate;
forming, on the fin, a gate dielectric stack of a transistor, wherein the gate dielectric stack comprises a high-k dielectric layer disposed on an interfacial dielectric layer;
exposing a surface of the high-k dielectric layer to a fluorine-based gas;
depositing a capping layer on the high-k dielectric layer;
depositing a work function layer on the capping layer; and
doping the work function layer with fluorine by soaking the work function layer in the fluorine-based gas.
10. The method of claim 9 , wherein exposing the surface of the high-k dielectric layer to the fluorine-based gas comprises exposing the surface of the high-k dielectric layer to one or more of fluorine (F 2 ), nitrogen trifluoride (NF 3 ), fluoroform (CHF 3 ), tetrafluoromethane (CF 4 ), sulfur hexafluoride (SF 6 ), hexafluoroethane (C 2 F 6 ), and combinations thereof.
11. The method of claim 9 , wherein soaking the work function layer comprises heating the substrate to a temperature between about 70° C. and about 950° C. while exposing the work function layer to one or more of fluorine (F 2 ), nitrogen trifluoride (NF 3 ), fluoroform (CHF 3 ), tetrafluoromethane (CF 4 ), sulfur hexafluoride (SF 6 ), hexafluoroethane (C 2 F 6 ), and combinations thereof.
12. The method of claim 9 , wherein soaking the work function layer comprises increasing a fluorine concentration of the work function layer to between about 0.01 atomic % and about 35 atomic percent.
13. The method of claim 9 , wherein soaking the work function layer comprises modulating a threshold voltage of the transistor.
14. A method, comprising:
forming a fin on a substrate;
forming, on the fin, a gate dielectric stack of a transistor, wherein the gate dielectric stack comprises a high-k dielectric layer disposed on an interfacial dielectric layer;
exposing a surface of the high-k dielectric layer to a fluorine-based gas;
depositing a capping layer on the high-k dielectric layer;
depositing a barrier layer on the capping layer;
soaking the barrier layer in the fluorine-based gas at a temperature between about 70° C. and about 950° C.;
depositing a work function layer on the capping layer; and
doping the work function layer by soaking the work function layer in the fluorine-based gas.
15. The method of claim 14 , wherein soaking the barrier layer comprises increasing a fluorine concentration of the barrier layer to between about 0.01 atomic % and about 35 atomic %.
16. The method of claim 14 , wherein soaking the barrier layer comprises modulating a threshold voltage of the transistor.
17. The method of claim 14 , further comprising,
depositing a sacrificial blocking layer on the barrier layer;
annealing the substrate at a temperature between about 70° C. and about 550° C.; and
removing the sacrificial blocking layer.
18. The method of claim 17 , wherein depositing the sacrificial blocking layer on the barrier layer comprises depositing one or more of a silicon layer and a titanium nitride layer.
19. The method of claim 17 , wherein the sacrificial blocking layer has a thickness between about 5 Å and about 30 Å.
20. The method of claim 17 , wherein annealing the substrate comprises annealing the substrate in one or more of a nitrogen ambient, a forming gas ambient, an ammonia ambient, and an oxygen ambient.