Capacitor and method for fabricating the same
Disclosed is a capacitor having a high dielectric constant and low leakage current and a method for fabricating the same, wherein the capacitor may include a first conductive layer, a second conductive layer, a dielectric layer stack between the first conductive layer and the second conductive layer, a dielectric interface layer between the dielectric layer stack and the second conductive layer, and a high work function interface layer between the dielectric interface layer and the second conductive layer.
1. A method for fabricating a capacitor, comprising:
forming a first conductive layer;
forming a dielectric layer stack in which a leakage blocking material is embedded, on the first conductive layer;
forming a dielectric interface layer on the dielectric layer stack;
forming a high work function interface layer on the dielectric interface layer; and
forming a second conductive layer on the high work function interface layer,
wherein the dielectric interface layer comprises a material having a higher electronegativity than the dielectric layer stack.
2. The method of claim 1 , wherein the high work function interface layer comprises a material having a higher work function than the dielectric layer stack.
3. The method of claim 1 , wherein the high work function interface layer is formed of a zirconium nitride-based material.
4. The method of claim 1 , wherein the high work function interface layer comprises zirconium nitride or carbon-doped zirconium nitride.
5. The method of claim 1 , wherein the forming of the high work function interface layer is performed by atomic layer deposition (ALD) of zirconium nitride.
6. The method of claim 1 , wherein the forming of the high work function interface layer is performed by repeating a unit cycle consisting of zirconium source material injection, purge, reaction gas injection and purge.
7. The method of claim 6 , wherein the zirconium source material comprises a carbon-containing zirconium source material.
8. The method of claim 6 , wherein the reaction gas comprises NH 3 .
9. The method of claim 1 , wherein the forming of the dielectric layer stack, the dielectric interface layer and the high work function interface layer is performed by atomic layer deposition (ALD).
10. The method of claim 1 , wherein the dielectric layer stack comprises any one of a Z-AZ—Z(ZrO 2 —Al doped ZrO 2 —ZrO 2 ) stack, a Z-AZ—Z-AZ(ZrO 2 —Al doped ZrO 2 —ZrO 2 —Al doped ZrO 2 ) stack, an H—Z-AZ—Z—H-AZ(HfO 2 —ZrO 2 —Al doped ZrO 2 —ZrO 2 —HfO 2 —Al doped ZrO 2 ) stack, an H-AH—H(HfO 2 —Al doped HfO 2 —HfO 2 ) stack and a Z—H-AH—H—Z(ZrO 2 —HfO 2 —Al doped HfO 2 —HfO 2 —ZrO 2 ) stack.